A kind of cemented carbide and local laser coating cemented carbide process

A cemented carbide and laser coating technology, which is applied in metal material coating technology, metal processing equipment, coating, etc., can solve the problem of weak bonding between the alloy layer and the base metal, and achieve the goal of eliminating inclusion elements and avoiding cracks produce, good compatibility effect

Active Publication Date: 2019-06-25
佛山铸昊机械设备有限公司
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Aiming at the problem that the coated alloy layer is not firmly combined with the base metal in the prior art, the present invention provides a cemented carbide and local laser coating cemented carbide process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A cemented carbide, the composition of which is as follows in terms of weight percentage: Cr: 20; W: 10; C: 1.5; Ni: 21; Fe: 1; Si: 0.8; B: 1; Re: 1.5; the balance is Co , the cemented carbide is in powder form and the particle size of the powder is 40-200um. In this embodiment, the particle size of the cemented carbide powder is 200um.

[0030] When the laser cladding cemented carbide process is applied, on the one hand, due to the high energy density of the laser, the temperature of the molten pool during the cladding process is high. After the laser beam is removed, the molten pool condenses rapidly, and alloy elements such as Si and B cannot effectively float up. Part of the brittle elements remain in the cladding layer, resulting in increased crack sensitivity of the cladding layer, and the surface hardness of the alloy layer is not high; on the other hand, the large difference in expansion coefficient between the alloy layer and the substrate leads to The bond is ...

Embodiment 2

[0035] A kind of cemented carbide, each composition is as follows according to weight percentage: Cr: 19; W: 8; C: 0.7; Ni: 13; Fe: 1; B: 1.7; Re: 1.5; The cemented carbide is in powder form and the particle size of the powder is 40-200um. In this embodiment, the particle size of the cemented carbide powder is 40um.

[0036] This embodiment strictly controls the addition of B elements and Si elements. The purpose is to ensure that the cemented carbide has certain self-fluxing, deoxidation, and slag-forming capabilities, and can "wet" the surface of the substrate, and avoid boron in the cladding process. It cannot float up, which increases the crack sensitivity of the cladding layer; at the same time, it reduces the melting point and expands the temperature range of the solid and liquid phases of the alloy, so that the alloy has good fluidity and good wettability to the surface of the substrate during the melting process And showed excellent metallurgical bonding.

[0037] The...

Embodiment 3

[0039] The hob cutter body and the upper and lower covers are usually made of national standard 42CrMo. After forging, normalizing and rough machining, the material is quenched and tempered according to the heat treatment process. The general technical requirements for the upper and lower covers are HB250-280, and the technical requirements for the cutter body are HRC40- 45. This technical requirement is to take into account the processing performance, mechanical properties and use strength of the material. The complex and changeable formation conditions have very high requirements on the cutting tool, and the outside of the hob is severely worn during operation. Therefore, further improving the mechanical properties of the outside of the hob can increase the service life.

[0040] In order to ensure the reasonable maintenance of the tool, the materials of the above-mentioned tool appearance parts are partially laser-coated with cemented carbide after the normal quenching and t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a cemented carbide and a local laser coating process of the cemented carbide, which belongs to the technical field of metal surface hardening treatment. The cemented carbide has the following components in terms of weight percentage: Cr: 20-27; W: 10-14; C: 1.5-2.5; Ni: 21-23; Fe: 1; Si: 0.8-1; 1; Re: 1.5; the balance is Co, and the cemented carbide is in powder form with a particle size of 40-200um. The powder alloy material used in the present invention has good compatibility with the base material, the cladding layer has a relatively small dilution rate and a similar thermal expansion coefficient. After pretreatment and post-heat treatment of the base body and the cladding layer, the temperature gradient is further reduced and the melting rate is reduced. The internal thermal stress of the cladding layer can avoid the occurrence of cracks and alloy layer shedding, thereby solving the problem of weak bonding between the coated alloy layer and the base metal in the prior art, and has the characteristics of high hardness and good wear resistance.

Description

technical field [0001] The invention belongs to the technical field of metal surface hardening treatment, and more specifically relates to a hard alloy and a local laser coating hard alloy process. Background technique [0002] In the field of underground engineering, the application of shield construction method is more and more extensive. The shield construction method is widely used in tunneling in hard rock sections. The shield machine in underground engineering is bulky and heavy, and the underground working space is limited. When working, the cutter head of the shield machine rotates to drive various knives on it to complete the excavation of the soil. The hob body and upper and lower covers of the shield machine are parts that are in direct contact with cuttings and rocks. They are prone to wear and tear during operation and need to be replaced in time. The quality of hob cutter body and upper and lower covers directly affects the rock-breaking ability, tunneling ef...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C30/00C22C19/07B22F1/00C23C24/10
CPCC22C19/07C22C30/00C23C24/103B22F1/052
Inventor 邰淼韩文进
Owner 佛山铸昊机械设备有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com