Ceramic tile with embossed textures

A technology of concave-convex texture and ceramic tiles, applied in the field of architectural ceramics, can solve problems such as unnaturalness, dull decorative effect of ceramic tiles, and increased production costs

Active Publication Date: 2013-02-13
FOSHAN DONGPENG CERAMIC +3
View PDF5 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The above methods all use a concave-convex mold to make the surface of the green body form a texture, but because the mold inevitably has artificial traces and does not have a natural random decorative effect, the decorative effect of the p

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0082] A ceramic brick with concave-convex texture, which is processed from a blank and a glaze, and the glaze is prepared from basic components according to the following weight percentages: 15wt% of pre-melt, 8wt% of magnesium oxide, and 12wt% of aluminum oxide , purple wood knot 18wt%, bentonite 47wt%.

[0083] The pre-melt refers to a molten mixture composed of tin oxide, sodium carbonate, raw talc and zinc oxide in a weight ratio of 1:2:2:1.

[0084] The above-mentioned ceramic brick with concave-convex texture is manufactured according to the following steps:

[0085] (1) Preparation of blanks and glazes;

[0086] (2) The blank is pressed and formed by an automatic brick press, and the brick forming pressure is controlled at 5-7Kn / cm 2 between;

[0087] (3) Glaze is sprayed to make the thickness of the glaze layer 1.5mm;

[0088] (4) In the oxidizing atmosphere of the shuttle kiln, firing at a temperature ranging from room temperature to 1200°C for 1.5 hours;

[008...

Embodiment 2

[0091] A ceramic brick with concave-convex texture, which is processed from a blank and a glaze, and the glaze is prepared from basic components according to the following weight percentages: 10wt% of premelt, 12wt% of magnesium oxide, and 8wt% of aluminum oxide , purple wood knot 22wt%, bentonite 48wt%.

[0092] The pre-melt refers to a molten mixture composed of tin oxide, sodium carbonate, raw talc and zinc oxide in a weight ratio of 1:2:2:1.

[0093] The above-mentioned ceramic brick with concave-convex texture is manufactured according to the following steps:

[0094] (1) Preparation of blanks and glazes;

[0095] (2) The blank is pressed and formed by an automatic brick press, and the brick forming pressure is controlled at 5-7Kn / cm 2 between;

[0096] (3) Glazing is carried out by spraying glaze, so that the thickness of the glaze layer is 2mm;

[0097] (4) In the oxidizing atmosphere of the shuttle kiln, fire at a temperature ranging from room temperature to 1200°C...

Embodiment 3

[0100] A ceramic brick with concave-convex texture, which is processed from a blank and a glaze, and the glaze is prepared from basic components according to the following weight percentages: 18wt% of pre-melt, 6wt% of magnesium oxide, and 14wt% of aluminum oxide , purple wood knot 15wt%, bentonite 45wt%, cobalt black 2wt%.

[0101] The pre-melt refers to a molten mixture composed of tin oxide, sodium carbonate, raw talc and zinc oxide in a weight ratio of 1:2:2:2.

[0102] The above-mentioned ceramic brick with concave-convex texture is manufactured according to the following steps:

[0103] (1) Preparation of blanks and glazes;

[0104] (2) The blank is pressed and formed by an automatic brick press, and the brick forming pressure is controlled at 5-7Kn / cm 2 between;

[0105] (3) Glazing is carried out in the way of pouring glaze, so that the thickness of the glaze layer is 1mm;

[0106] (4) In the oxidizing atmosphere of the shuttle kiln, firing at a temperature ranging...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of construction ceramics, and in particular discloses a ceramic tile with embossed textures, which is formed by processing a blank and glaze. The ceramic tile is characterized in that: the glaze is prepared from the following basic components in percentage by weight: 5 to 20 percent of frit, 5 to 15 percent of magnesium oxide, 5 to 15 percent of alumina, 10 to 30 percent of camwood segments, and 20 to 50 percent of bentonite. The invention also discloses a method for manufacturing the ceramic tile with embossed texture, which comprises the following steps of: preparing the blank and glaze; forming a tile blank; applying the glaze; firing; and cooling to a normal temperature. According to the ceramic tile with embossed textures disclosed by the invention, the formation of embossed textures does not require an embossed die, and a natural smooth, continuously changing and non-repeated embossed texture surface decorating effect is represented on the manufactured ceramic tile without artificial trace by virtue of the glaze prescription and process parameter design.

Description

technical field [0001] The invention relates to the technical field of architectural ceramics, in particular to a ceramic brick with concave-convex texture. Background technique [0002] Ceramic tiles are plate-shaped or block-shaped ceramic products produced by clay and other inorganic non-metallic raw materials through molding and sintering processes. They are used to decorate and protect walls and floors of buildings and structures. one of the materials. With the improvement of people's living standards, new requirements are constantly put forward for the decorative effect of ceramic tiles. More and more people hope that ceramic tiles can present concave-convex textures imitating natural leather grains and wood grains. [0003] CN102029644A discloses a production process of wood-grain antique bricks, which includes the following steps: (1) preparing blanks, surface glazes and floral glazes; (2) forming blanks in mold bricks to form green bricks, and the mold bricks are p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B41/86
Inventor 龙海仁
Owner FOSHAN DONGPENG CERAMIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap