Root of tooth implant matrix containing silicon, calcium, phosphorus and sodium micro-arc oxidation coating and preparation method thereof

A micro-arc oxidation and implant technology, applied in coatings, implants, dentistry, etc., can solve the problems of muscle tissue necrosis, incomplete coating, easy dissolution of metal ions, etc., and achieve easy process, simple process, avoidance of The effect of muscle tissue necrosis

Inactive Publication Date: 2013-05-08
HARBIN INST OF TECH
View PDF10 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to solve the problems of muscle tissue necrosis and incomplete coating prepared by micro-arc oxidation on the surface of the existing dental root implants and their accessories, and provide silicon, calcium, phosphorus, Sodium micro-arc oxidation coated dental root implant matrix and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Root of tooth implant matrix containing silicon, calcium, phosphorus and sodium micro-arc oxidation coating and preparation method thereof
  • Root of tooth implant matrix containing silicon, calcium, phosphorus and sodium micro-arc oxidation coating and preparation method thereof
  • Root of tooth implant matrix containing silicon, calcium, phosphorus and sodium micro-arc oxidation coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0021] Specific Embodiment 1: The dental root implant matrix containing silicon, calcium, phosphorus, and sodium micro-arc oxidation coating in this embodiment is composed of a dental root implant 1 and a clamp 2, wherein the upper end of the dental root implant 1 is provided with a screw The clamp 2 is inserted into the slot 3. The clamp 2 is composed of a screw 4 and a fitting 5. The screw 4 is screwed to the bottom of the fitting 5. A hole 6 is opened at the side end of the fitting 5. The screw 4 is screwed into the screw insertion slot 3.

[0022] In this embodiment, a micro-arc oxidation bioactive coating can be formed on the surface of the dental root implant by a micro-arc oxidation method, and silicon, calcium, phosphorus, and sodium bioactive elements can be introduced into the coating, so that the dental root implant has apatite-induced ability, can effectively shorten the time of implant-osseointegration, and induce the formation of new bone on the root surface. Mus...

specific Embodiment approach 2

[0024] Embodiment 2: This embodiment differs from Embodiment 1 in that the root implant 1 and the jig 2 are made of pure titanium TA2, TA4 or alloy T2448. Others are the same as in the first embodiment.

specific Embodiment approach 3

[0025] Embodiment 3: This embodiment differs from Embodiment 1 or Embodiment 2 in that: the screw 4 and the screw insertion groove 3 are fixed by a nut 7 . Others are the same as in the first or second embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a root of tooth implant matrix containing silicon, calcium, phosphorus and sodium micro-arc oxidation coating and a preparation method thereof, relating to the field of implant material of a dental department. The invention aims at solving the problems that the existing root of tooth implants and metal ions of accessories thereof are easy to dissolve out to cause muscle tissue necrosis and the coating prepared on the surface of the implant through micro-arc oxidation is incomplete. The preparation method comprises the steps of selecting pure titanium or titanium alloy to be processed into the implant matrix and an oxidation fixture, polishing, washing and drying; and preparing the micro-arc oxidation bio-coating with micro-nano porous appearance on the external surface of the implant matrix by utilizing a micro-arc oxidation technology, taking out, washing and drying so as to obtain the root of tooth implant containing silicon, calcium, phosphorus and sodium micro-arc oxidation coating. According to the tooth implant matrix, biological active elements such as silicon, calcium, phosphorus and sodium are introduced into the coating, so that the root of tooth implant has apatite inducibility, the time for combining the implant and the bone is shortened, the part of the surface of the implant, contacted with the muscle tissue, can be completely oxidized due to the design of the fixture, the efficiency is high, no pollution is generated, and the tooth implant matrix is convenient to produce in large scale.

Description

technical field [0001] The invention relates to a dental root implant substrate and a preparation method thereof, in particular to a dental root implant substrate with a silicon, calcium, phosphorus and sodium micro-arc oxidation coating and a preparation method thereof. Background technique [0002] Dental root implants are widely used in the restoration of patients with dentition defects. However, due to the long time of implant-osseointegration, metal ions are easily dissolved and cause muscle tissue necrosis, resulting in failure cases, which greatly limits its wide application. The micro-arc oxidation method can be used to generate a bioactive coating on the surface of the implant, thereby improving the biological properties of the implant material. While inhibiting the dissolution of metal ions, it can also induce the formation of apatite, so that the implant has biological activity. However, usually in the micro-arc oxidation preparation process, the fixture needs to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61C8/00C25D11/26A61L27/30A61L27/32
Inventor 魏大庆周睿成夙周玉
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com