Modified elastomer for MX (M Xylene) nylon and preparation method thereof

A technology of elastomer and nylon, which is applied in the field of modified elastomer of MX nylon and its preparation, can solve the problems affecting product performance and poor compatibility, and achieve the effect of improving product hardness, excellent toughness and reducing cost

Inactive Publication Date: 2013-05-08
东莞市明聚塑胶有限公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] TPE, TPV and polyamide each have their own advantages and disadvantages, and their limited scope of use. If the advantages of combining the two are combined with polyamide and elastomer, the scope of use of the two in industry will be expanded, but the combination of the two materials , especially the difference in polarity and structure between polyamide materials and thermoplastic elastomer TPE, resulting in poor compatibility of the two materials, if the polyamide or TPE is not modified accordingly to improve the compatibility of the two, it will directly affect to product performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified elastomer for MX (M Xylene) nylon and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A modified elastomer of MX nylon, comprising the following components by weight: 15 parts of MXPA, 5 parts of maleic anhydride grafted EPDM, 10 parts of SEBS, 15 parts of ultra-low density polyethylene, 1 part of calcium stearate, white mineral 1 part of oil, wherein the grafting rate of maleic anhydride grafted EPDM is 0.8%.

[0021] A kind of preparation method of the modified elastomer of above-mentioned MX nylon, comprises the following steps:

[0022] First add MXPA and 1 part of white mineral oil into the blender, stir evenly, then add calcium stearate to it, stir evenly, continue to add maleic anhydride grafted EPDM, ultra-low density polyethylene and SEBS to it, After it is stirred evenly, it is introduced into a twin-screw extruder. The processing technology is as follows: the temperature of the first zone is 190-220°C, the temperature of the second zone is 200-230°C, the temperature of the third zone is 210-240°C, the temperature of the fourth zone is 220-250°...

Embodiment 2

[0024] A modified elastomer of MX nylon, comprising the following components by weight: 45 parts of MXPA, 10 parts of maleic anhydride grafted EPDM, 40 parts of SEBS, 45 parts of ultra-low density polyethylene, 8 parts of calcium stearate, white ore 1 part of oil, wherein the grafting rate of maleic anhydride grafted EPDM is 1%.

[0025] A kind of preparation method of the modified elastomer of above-mentioned MX nylon, comprises the following steps:

[0026] First add MXPA and 1 part of white mineral oil into the blender, stir evenly, then add calcium stearate to it, stir evenly, continue to add maleic anhydride grafted EPDM, ultra-low density polyethylene and SEBS to it, After it is stirred evenly, it is introduced into a twin-screw extruder. The processing technology is as follows: the temperature of the first zone is 190-220°C, the temperature of the second zone is 200-230°C, the temperature of the third zone is 210-240°C, the temperature of the fourth zone is 220-250°C, a...

Embodiment 3

[0028] A modified elastomer of MX nylon, comprising the following components in parts by weight: 70 parts of MXPA, 15 parts of maleic anhydride grafted EPDM, 70 parts of SEBS, 75 parts of ultra-low density polyethylene, 15 parts of calcium stearate, white ore 1 part of oil, wherein the grafting rate of maleic anhydride grafted EPDM is 1.5%.

[0029]A kind of preparation method of the modified elastomer of above-mentioned MX nylon, comprises the following steps:

[0030] First add MXPA and 1 part of white mineral oil into the blender, stir evenly, then add calcium stearate to it, stir evenly, continue to add maleic anhydride grafted EPDM, ultra-low density polyethylene and SEBS to it, After it is evenly stirred, it is introduced into a twin-screw extruder. The processing technology is as follows: the temperature of the first zone is 190-220°C, the temperature of the second zone is 200-230°C, the temperature of the third zone is 210-240°C, the temperature of the fourth zone is 2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
degree of graftingaaaaaaaaaa
degree of graftingaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of thermoplastic elastomers and discloses a modified elastomer for MX (M Xylene) nylon and a preparation method thereof. The modified elastomer comprises the following components in parts by weight: 15-70 parts of MXPA, 5-15 parts of nylon toughening compatilizer, 10-70 parts of SEBS, 15-75 parts of ultralow density polyethylene, 1-15 parts of calcium stearate and 1-2 parts of white mineral oil. The modified elastomer has the characteristics of MXPA high-temperature resistance and oil resistance, has the characteristics of low specific gravity and high toughness of SEBS and ultralow density polyethylene, and has high compatibility, proper product hardness and low cost.

Description

technical field [0001] The invention relates to the technical field of thermoplastic elastomers, in particular to a modified elastomer of MX nylon used for wire and cable sheaths and automobile pipelines and a preparation method thereof. Background technique [0002] The existing materials used in wire and cable sheaths and automobile pipelines are mostly styrene thermoplastic elastomer (TPE) and thermoplastic vulcanizate (TPV). TPE is a kind of rubber with high elasticity, high resilience, and plasticity. Processing characteristics, environmental protection, non-toxic and safe, wide range of hardness, excellent colorability, weather resistance, fatigue resistance and temperature resistance, excellent processing performance, no need for vulcanization, can be recycled to reduce costs, wide application fields, can be used for plastics However, TPE has poor heat resistance, and its physical properties decrease greatly as the temperature rises, so the scope of use is limited. T...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/00C08L51/06C08L53/02C08L23/08C08K5/098C08K5/01B29C47/92B29C48/92