A kind of recycled polyethylene terephthalate/acrylonitrile-butadiene-styrene copolymer alloy and preparation method thereof

A technology of polyethylene terephthalate and styrene copolymer is applied in the field of preparation of recycled PET/ABS alloy, which can solve the problem of narrow controllable temperature range for alloy processing, low molecular weight of recycled PET, and difficulty in guaranteeing product quality and other problems, to achieve the effect of improving comprehensive performance, excellent processability, and preventing the decline of mechanical properties of the system

Active Publication Date: 2017-03-01
HEFEI GENIUS NEW MATERIALS
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are still the following disadvantages in this technology: the PET used is a new material, and its processing temperature is 260-290°C. At this temperature, ABS has begun to decompose, and the controllable temperature range of alloy processing is very narrow. Not only is the operation difficult, but the product Difficult to guarantee quality
This patent provides an effective way to recycle PET materials, but it has the following disadvantages: it cannot effectively solve the difficulty that the two phases of recycled PET and ABS are incompatible systems, and at the same time, recycled PET itself has low molecular weight, and it is easy to oxidize and fracture chain, leading to the crux of system performance becoming brittle and unstable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of recycled polyethylene terephthalate/acrylonitrile-butadiene-styrene copolymer alloy and preparation method thereof
  • A kind of recycled polyethylene terephthalate/acrylonitrile-butadiene-styrene copolymer alloy and preparation method thereof
  • A kind of recycled polyethylene terephthalate/acrylonitrile-butadiene-styrene copolymer alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Take by weighing 60.0% of dried reclaimed PET flakes by weight ratio, ABS resin is 16.0%, ABS-g-MAH compatibilizer is 2.5%, reinforcing agent is 20%, diisocyanate is 0.5%, antioxidant 1010 is 0.2%, antioxidant 168 is 0.3%, lanthanum acetate is 0.4%, light stabilizer V703 is 0.1%. The above-mentioned components are mixed evenly by a high-speed mixer and then added from the discharge port of the extruder. The temperature of each section of the extruder from the discharge port to the grinding port is between 180-200 °C, and the speed of the main engine is 80r / min. . Alloy materials are granulated by melt blending and extruding. The SEM photo of gained recycled PET / ABS alloy is as follows figure 1 The material test results are shown in Table 1.

Embodiment 2

[0044] Weigh 60.0% of dried recycled PET flakes by weight, ABS resin is 11.0%, reinforcing agent is 25%, ABS-g-GMA compatibilizer is 2.0%, and epoxy molecular weight regulator ADR4370S is 0.7% %, antioxidant 1010 is 0.2%, antioxidant 168 is 0.3%, gallium acetate is 0.5%, antistatic agent 129 is 0.3%. The above-mentioned components are mixed evenly by a high-speed mixer and then added from the discharge port of the extruder. The temperature of each section of the extruder from the discharge port to the grinding port is between 180-200 °C, and the main engine speed is 90r / min. . The SEM photo of gained recycled PET / ABS alloy is as follows figure 2 The material test results are shown in Table 1.

Embodiment 3

[0046] Take by weighing 70.0% of the reclaimed PET flakes that dry well, the ABS resin is 12.0%, the reinforcing agent is 15%, the ABS-g-GMA compatibilizer is 1.0%, the epoxy molecular weight regulator is 1.0%, anti- Oxygen 1010 is 0.2%, antioxidant 168 is 0.3%, and lanthanum acetate is 0.5%. The above-mentioned components are mixed evenly by a high-speed mixer and then added from the discharge port of the extruder. The temperature of each section of the extruder from the discharge port to the grinding port is between 180-200 °C, and the speed of the main engine is 100r / min. . The material test results are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a recycled polyethylene terephthalate / acrylonitrile-butadiene-styrene copolymer alloy and a preparation method thereof. The method comprises the following steps: 60-90% of recycled PET is recovered by weight percentage; ABS resin 2-30%; reinforcing agent 3-30%; compatibilizer 1-5%; antioxidant 0.1-0.5%; rare earth metal salt 0.1-0.5%; molecular weight regulator 0.1-2%; ~ 2%, mixed evenly by a high-speed mixer, then added to the extruder to extrude to obtain a strip. The processing temperature of the extruder from the feeding port to the grinding port is as follows: 180°C, 185°C, 190°C, 195°C , 200°C, 205°C, 210°C, 215°C, the extruder host speed is 80‑120r / min; the above strips are water-cooled and pelletized to obtain modified pellets. Compared with the prior art, the invention has the advantages of being suitable for industrial batch production, having excellent tensile strength, impact strength, high fluidity, high chemical stability and the like.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to the preparation of a recycled PET / ABS alloy with high performance and low cost. Background technique [0002] Polyethylene terephthalate (PET) is a kind of crystalline polyester with good organic solvent resistance, chemical resistance, self-lubricating performance and molding processing performance, etc. It is widely used in long fiber, food packaging bottles , plates, plastic steel strips, etc. With the wide application of PET materials, waste PET materials are gradually increasing. Waste PET materials are non-biodegradable materials. If these waste PET materials cannot be recycled well, it will not only cause waste of resources, but also cause environmental pollution. [0003] ABS plastic is an acrylonitrile-butadiene-styrene copolymer, which has good comprehensive properties, high impact strength, chemical stability and good electrical properties. ABS ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L67/02C08L55/02C08L51/00C08L51/06C08K13/04C08K7/14C08K7/06C08K7/08C08K5/098C08K3/16C08K3/26C08K3/30B29C47/92B29C48/92
CPCB29B9/14B29B7/46B29B7/72B29B7/7461B29B7/90B29B9/06B29B9/12B29C48/875B29C48/92B29C2948/9259B29C2948/92704B29C2948/92885B29C2948/92895
Inventor 杨桂生汪海孙利明
Owner HEFEI GENIUS NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com