Scale-like multi-element aluminum zinc silicon alloy powder containing La and Pr, and preparation method thereof

A scaly, zinc-aluminum alloy technology, which is applied in the field of scaly multi-component aluminum-zinc-silicon alloy powder and its preparation, can solve the problem of restricting the industrialization process of chromium-free zinc-aluminum coating technology, affecting the use range and quality of metal powder, drying Complex process and other problems, to achieve the effect of high flaky degree, cost reduction and good dispersibility

Active Publication Date: 2015-06-24
JIANGSU LINLONG NEW MATERIALS CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The drying process of the above-mentioned wet grinding method is complicated, the cycle is long, the efficiency is low, and the metal powder is easy to oxidize. What is more serious is that the dried metal powder will leave a part of the medium, which will affect the use range and quality of the metal powder.
However, the dry grinding process requires long-term stirring and dispersion, which increases energy consumption, and the shape and performance of the ultrafine zinc powder and aluminum powder produced by the dry grinding process are far behind the powders required by the Dacromet process. Thereby limiting the process of industrialization of chromium-free zinc-aluminum coating technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Scale-like multi-element aluminum zinc silicon alloy powder containing La and Pr, and preparation method thereof
  • Scale-like multi-element aluminum zinc silicon alloy powder containing La and Pr, and preparation method thereof
  • Scale-like multi-element aluminum zinc silicon alloy powder containing La and Pr, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Take 10Kg of 300-mesh aluminum-zinc-silicon alloy powder raw material, 0.4Kg of zinc stearate, and 200Kg of steel balls into the ball mill. After vacuuming, nitrogen is introduced, and cooling water is connected to ensure that the temperature during the ball milling process is between 30-40°C. . After ball milling at a speed of 50r / min for 10 hours, the material is discharged, and the ball milled powder is put into a polishing machine for polishing. The polished powder is classified to obtain flake Al-Zn-Si alloy powder.

Embodiment 2

[0045] Get 10Kg of 200-mesh aluminum-zinc-silicon alloy powder raw material, 0.1Kg of polyvinyl alcohol, 0.2Kg of calcium stearate, and 120Kg of steel balls and put them into the ball mill. Between 30-40°C, ball mill at a speed of 100r / min for 14 hours to discharge the material, put the ball-milled powder into a polishing machine for polishing, and classify the polished powder to obtain flake-shaped aluminum-zinc-silicon alloy powder.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
bulk densityaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a scale-like multi-element zinc aluminum alloy powder containing La and Pr, and a preparation method thereof. In the scale-like multi-element zinc aluminum alloy powder, the sheet thickness is 0.1 to 1 micron, the average sheet diameter is 5 to 35 microns, and specifically, the powder comprises the following particles in size: less than or equal to 20% of the powder with the sheet diameter being less than 5 microns, more than or equal to 70% of the powder with the sheet diameter being 5 to 33 microns and less than or equal to 10% of the powder with the sheet diameter being more than 33 microns; the diameter thickness ratio of the average sheet diameter to the sheet thickness of the scale-like multi-element zinc aluminum alloy powder is 35 to 200. The scale-like metal powder and the preparation method thereof provided by the invention are particularly suitable for the fields of production of Dacromet coating liquid, inorganic zinc-enriched paint, heavy anti-corrosion paint and the like.

Description

technical field [0001] The invention relates to a scaly multi-element aluminum-zinc-silicon alloy powder and a preparation method thereof. Background technique [0002] Dacromet technology was first born in the late 1950s. It is a metal coating treatment technology similar to electrogalvanizing. Mike Martin, an American scientist, developed a metal zinc flake and added aluminum flake, chromic acid, Highly dispersed water-soluble paint with deionized water as a solvent, the paint sticks to the metal substrate, and is coated and baked in a fully closed circuit to form a thin coating. Dacromet coating successfully resists the erosion of chloride ions, and the anti-corrosion technology has entered a new level, which has innovated the defect of short anti-corrosion life of the traditional process. The appearance of Dacromet coating is uniform silver gray. The coating contains 80% thin zinc flakes and aluminum flakes, and the rest is chromate. It has excellent properties, such as...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/10C22C18/04C22C30/06B22F9/04
Inventor 冯立新张敏燕魏小昕蒋穹陈竺
Owner JIANGSU LINLONG NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com