An ink composition, inkjet printing technology, applied in the direction of inks, applications, household appliances, etc., can solve problems such as non-biodegradable, non-applied, surfactant or non-surfactant

Inactive Publication Date: 2013-12-04
MARKEM IMAJE HLDG
View PDF25 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the above mentioned surfactants or surfactants are not and

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Biodegradable liquid ink composition for ink jet printing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0181] The following ink compositions of the present invention were prepared by mixing the products mentioned in Table I in the proportions indicated below. The table below also gives the viscosity and conductivity of the inks obtained. Table I

[0182]

[0183] (1)by Perstorp Specialty Produced CAPA6100 with a weight average molecular weight of 30 kDa as determined by size exclusion chromatography (GPC) in THF compared to polystyrene standards;

[0184] (2) Depend on Vyloecol produced by (Japon) with Polymer Manufactured "Mixed D" A weight average molecular weight of 37 kDa determined by size exclusion chromatography (GPC) in THF and compared to polystyrene standards in the column;

[0185] (3) Depend on Dispersants produced;

[0186] (4) by dyes in the produced solution;

[0187] (5) used by made device, particle size (Z-average) was determined by quasi-elastic light scattering in methyl ethyl ketone.

[0188] (6) Viscosity was measured at 20°...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Biodegradable ink composition for ink jet printing, liquid at room temperature, comprising: a) a binder comprising at least 0.5% by weight relative to the total weight of the ink, of at least one biodegradable polymer having a weight average molecular weight less than 70 kDa, preferably less than 60 kDa, more preferably less than 50 kDa, further preferably less than 40 kDa, expressed as polystyrene equivalents; b) an organic vehicle or solvent comprising, preferably composed of, one or more organic solvent compound (s), and optionally water; c) at least 0.1% by weight relative to the total weight of the ink of one or more dye(s) and/or pigment (s); wherein the biodegradable polymer is chosen from among polyhydroxyalkanoates (PHA), polyesteramides (PEA), poly (glycolic acid) s, poly (lactic acid) s (PLA), polycaprolactones (PCL), the copolymers thereof; and aliphatic copolyesters such as succinates, adipates and terephtalates; and wherein the ink composition has a viscosity of 1 to 20 mPa.s, preferably of 2 to 10 mPa.s at 20°C. Process for marking a substrate using said ink composition. Substrate provided with marking obtained by drying and/or absorption of said ink composition.

Description

technical field [0001] The present invention relates to liquid ink compositions for marking all types of supports, substrates and objects, the properties of which are particularly suitable for inkjet marking or Print a wide variety of supports, substrates and objects, whether they are porous or non-porous. The ink composition of the invention is defined as a biodegradable ink composition, and preferably the ink composition of the invention is additionally also a compostable ink composition. Background technique [0002] Biodegradable compositions, components, components, components generally refer to such compositions, components, components, components that can be degraded, decomposed preferably rapidly by living organisms such as microorganisms without polluting the natural environment. [0003] Biodegradation is explained as the progressive simplification of the chemical structure of organic compounds containing inter alia carbon, hydrogen, oxygen, nitrogen atoms, accomp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D11/00
CPCC09D11/36C09D11/102C09D11/30C09D11/00Y10T428/24802Y10T428/1334Y10T428/1352
Inventor 皮埃尔·德圣-罗曼
Owner MARKEM IMAJE HLDG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap