Aluminum alloy digital electronic product case and application thereof

A technology of electronic products and aluminum alloys, which is applied in the field of aluminum alloys, can solve the problems of low specific strength, etc., and achieve the effect of suppressing the deterioration of fatigue performance and wide versatility

Active Publication Date: 2014-01-01
苏州利达铸造有限公司
View PDF8 Cites 32 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the specific strength of aluminum alloys is lower than that of magnesium alloys, so how to improve the mechanical strength of commercially available aluminum alloys is an important topic that has attracted great attention at present.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum alloy digital electronic product case and application thereof
  • Aluminum alloy digital electronic product case and application thereof
  • Aluminum alloy digital electronic product case and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-3， and comparative example 1-5

[0017] 1) Raw material preparation: Prepare raw materials according to the alloy composition ratio in Table 1, including pure aluminum with a purity of 99.9%, aluminum-silicon alloy with a silicon content of 12-15%, aluminum-zinc alloy with a zinc content of 10-15%, electrolytic Copper, electrolytic nickel, industrial pure magnesium, industrial pure zirconium, industrial pure titanium and other raw materials.

[0018] 2) Melting: Preheat the above-mentioned raw materials to at least 200°C, then heat the pure aluminum in a melting furnace to 800°C, then add electrolytic copper, electrolytic nickel, commercially pure zirconium and pure titanium, and keep stirring until All the raw materials are melted, then lower the temperature to 720°C and add aluminum-silicon alloy and aluminum-zinc alloy and continue to stir until the raw materials are completely melted, then lower the temperature to 660°C and press industrial pure magnesium to the bottom of the melt for at least 5 minutes, t...

Embodiment 6-7

[0042] Examples 6-7, and Comparative Examples 14-18, the chemical composition of the alloy is the same as that of Example 2, and the optimal selection of the parameters of the electrolyte composition in the two anodic oxidations is mainly investigated. The selection of parameters and performance results are shown in Table 3 , wherein the current density, voltage and oxidation time are the same as in Example 2.

[0043] table 3

[0044]

[0045] In addition to the experiments in Table 3, the conventional CAA method and SAA method were also used to anodize aluminum alloys with the same composition, and the results showed that the fatigue strength could only reach 2×10 4 About the order of magnitude, far less than this application.

[0046] The above results show that the composition of the two-time anodic oxidation has an important influence on the fatigue strength of the alloy. Firstly, the fatigue strength of the two-time anodic oxidation has obvious advantages compared wi...

Embodiment 8-9

[0048] Examples 8-9, and comparative examples 19-22, the chemical composition of the alloy is the same as that of Example 2, and the optimal selection of parameters such as current density, voltage and oxidation time in the two anodic oxidations, the selection of parameters and the performance The results are shown in Table 4, wherein the composition of the electrolyte is the same as in Example 2.

[0049] Table 4

[0050]

[0051] From the results in Table 4, it can be seen that the current density of anodic oxidation should not be too small, otherwise it will make it difficult for the order of the pores of the oxide film to meet the requirements and become the source of fatigue damage, but the current density should not be too large, otherwise it will make the pores Excessive pit depth can also become a source of fatigue damage. The oxidation time should not be too short, otherwise it will not meet the basic requirements of anodic oxidation, and it will not be conducive ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an aluminum alloy digital electronic product case. An aluminum alloy comprises the components in percentage by weight as follows: 4.5-4.8% of Zn, 1.8-2.0% of Cu, 1.6-1.8% of Mg, 2.2-2.5% of Si, 0.05-0.1% of Zr, 0.4-0.6% of Ni, 0.5-1% of Ti and the balance of aluminum and inevitable impurities. To be specific, the aluminum alloy with excellent die casting and anodic oxidation properties for the case is obtained through simple alloy elements and moderate matching firstly, meanwhile, appropriate raw materials and a melting process are adopted, the die casting and mechanical properties of the alloy are guaranteed, an optimal anoxic oxidation treatment process and parameters are selected after die casting, so that the die-casting aluminum alloy with excellent properties for a digital electronic product is obtained, and then the digital electronic product case is obtained finally through shaping and coating.

Description

technical field [0001] The invention relates to the technical field of aluminum alloys, in particular to provide a die-casting aluminum alloy digital electronic product housing, and the invention also mentions the application of the die-casting aluminum alloy digital electronic product housing. Background technique [0002] With the rapid development of the digital electronics industry and the communication industry, the popularity of electronic products such as mobile phones, notebook computers, and digital cameras is increasing day by day, becoming necessary daily necessities for everyone. In order to improve the market competitiveness of various electronic products, manufacturers not only actively improve the performance of digital electronic products, but also try their best to improve the aesthetics and portability of the products, so as to gain more favor from consumers. Therefore, all kinds of digital electronic products are developing towards lightness, thinness, sho...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/10C22F1/053C25D11/12B22D17/32H05K5/04
Inventor 季吉清
Owner 苏州利达铸造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap