Preparation method of amino inhibited polyamide hot melt adhesive

A polyamide hot-melt adhesive and amine-based technology, applied in the direction of adhesives, etc., to achieve the effect of high peel strength

Inactive Publication Date: 2014-01-22
SHANGHAI TIANYANG HOT MELT ADHESIVE CO LTD +2
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The chain terminators currently used to prepare polyamide hot-melt adhesives are mainly various monobasic acids, such as stearic acid, 5-hexenoic acid in CN1646604A, and caprolactam in monobasic acid 5-hexenoic acid, 270 Under ℃, react for several hours to obtain product measurement relative viscosity, the peel strength about this kind of polyamide hot-melt adhesive in CN1469891A is lower than 25N / m

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of amino inhibited polyamide hot melt adhesive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Add 0.85 mol of sebacic acid, 0.87 mol of decane diamine, 0.45 mol of nylon 66 salt, 3.5 mol of caprolactam, 0.039 mol of hexadecylamine, and 1.72 g of phosphoric acid into the numerically controlled autoclave, constant pressure 1.65Mpa, constant pressure temperature 215℃ , After constant pressure reaction for 0.75h, release the pressure, the time to release to normal pressure is 1.1h, then pass N 2 Atmospheric pressure reaction for 0.75h and discharge to obtain product P1.

[0017]

Embodiment 2

[0019] Add 0.85 mol of sebacic acid, 0.952 mol of decane diamine, 0.65 mol of nylon 66 salt, 4.3 mol of undecalactam, 0.098 mol of dodecylamine, 3.44 g of tungstomolybdic acid, and constant pressure of 1.7Mpa into the numerically controlled autoclave. Constant pressure temperature 220℃, constant pressure reaction for 0.9h, then release pressure, release to normal pressure for 1.2h, then pass N 2 Atmospheric reaction for 0.8h and discharge to obtain product P2.

[0020]

Embodiment 3

[0022] Add 0.85 mol of sebacic acid, 0.89 mol of decanediamine, 0.5 mol of nylon 66 salt, 3.7 mol of caprolactam, 0.05 mol of octadecylamine, 1.94 g of hydrochloric acid, constant pressure 1.6Mpa, constant pressure temperature 200°C into the numerically controlled autoclave , After the constant pressure reaction for 0.5h, release the pressure, the time to release to normal pressure is 1.0h, then pass N 2 Atmospheric reaction for 0.5h and discharge to obtain product P3.

[0023]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
peel strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of an amino inhibited polyamide hot melt adhesive. The method is characterized by taking a monoamine as a chain terminator, and preparing copolyamide hot melt adhesive from a diacid, a diamine, a nylon salt and lactam. The obtained product has the characteristics of low viscosity, easy coating, and high bonding strength.

Description

technical field [0001] The invention relates to a preparation method of a copolyamide hot-melt adhesive with monoamine as a chain terminator. The polyamide adhesive has the characteristics of low viscosity, easy coating and high bonding strength. Background technique [0002] The chain terminators currently used to prepare polyamide hot-melt adhesives are mainly various monobasic acids, such as stearic acid, 5-hexenoic acid in CN1646604A, and caprolactam in monobasic acid 5-hexenoic acid, 270 Reaction at ℃ for several hours to obtain the measured relative viscosity of the product, the peel strength of this polyamide hot-melt adhesive in CN1469891A is lower than 25N / m. [0003] Monoamines can also be used as chain terminators to prepare polyamide hot-melt adhesives. The present invention has done relevant research on this characteristic. The present invention uses one of dodecylamine, hexadecylamine, and octadecylamine as a polymerization inhibitor , synthesized copolyamide ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J177/00C08G69/36
Inventor 薛为岚周义行李哲龙朱万育曾作祥吴芳群沈艳
Owner SHANGHAI TIANYANG HOT MELT ADHESIVE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap