Polishing wheel containing fiber ropes

A polishing wheel and fiber rope technology, applied in the field of polishing wheels, can solve the problems of low polishing efficiency, shortened service life of the polishing wheel, and increased surface temperature of the polishing wheel, and achieves the effect of reducing cost, increasing polishing effect and facilitating grinding

Inactive Publication Date: 2014-02-05
谢泽
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The various polishing wheels currently produced have the following defects: ①Low polishing efficiency, such as hemp wheels (several layers of sisal are sewn together, and only the end face participates in grinding)
There is following shortcoming in the sisal fiber buffing wheel prepared with this kind of method: one, because the sisal fiber length used has only 4-12cm, thereby buffing wheel comes off easily in use sisal fiber, makes the service life of buffing wheel shortening; 2. Due to the limitation of needle punching density, it is impossible to ensure that any part of the polishing wheel can be tightly bonded, which will also affect the use effect of the polishing wheel
The polishing wheel produced by this method is molded and has no porous material, so the whole structure is very dense and has no gaps, which will easily cause the surface temperature of the grinding wheel to rise during the entire grinding process. The workpiece to be ground will also have a large surface temperature rise, which will cause stress concentration and may contaminate the surface of the workpiece to be ground

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polishing wheel containing fiber ropes
  • Polishing wheel containing fiber ropes
  • Polishing wheel containing fiber ropes

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Example 1 (to explore the relationship between the mixing mass ratio of phenolic resin and natural fiber rope and the polishing effect).

[0028] Recipe 1:

[0029]

[0030] Sample making

[0031] 1.1 Process route

[0032] 1.2.1 Glue on the hemp rope: Roll and coat a circle of glue on the processed sisal fiber rope (: 65% modified liquid phenolic resin solution, filler: 35%, glue solid content: 75-77% , the amount of glue is: 0.7-0.8g per gram of sisal fiber rope), and then baked at 70±2°C for 30min.

[0033] 1.2.2 Wrap the glued hemp rope on the mold according to the established route, then put it into the mold cavity, press and shape it, and bake it at 120°C for 4-6 hours (the flat grinding wheel is cured for 4 hours, and the circular grinding wheel is cured for 6 hours) , slowly lowered to room temperature and then out of the oven, unmoulded.

[0034] 1.3 The production pattern of this test is: flat polishing wheel: the outer diameter is 4 inches (101.6-103mm...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Outer diameteraaaaaaaaaa
The inside diameter ofaaaaaaaaaa
Apertureaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polishing wheel containing fiber ropes. A polishing disk of the polishing wheel is composed of the fiber ropes, and the fiber ropes are bound by binder. By regulating the proportion between the fibers and the binder, the polishing effect and grinding efficiency of the polishing wheel can be controlled.

Description

technical field [0001] The invention relates to a polishing wheel containing a fiber rope, which belongs to the field of abrasive tools. Background technique [0002] The various polishing wheels currently produced have the following defects: 1. The polishing efficiency is low, such as hemp wheels (several layers of sisal are sewn together, and only the end faces participate in grinding). Chinese patent CN1238254A discloses a sisal fiber polishing wheel, and discloses that its preparation method is: using a needle loom to make sisal short fibers into felt-like blanks, and then laminating 2-4 layers of sisal felt-like blanks , Sewn into a sisal fiber polishing wheel. There is following shortcoming in the sisal fiber buffing wheel prepared with this kind of method: one, because the sisal fiber length used has only 4-12cm, thereby buffing wheel comes off easily in use sisal fiber, makes the service life of buffing wheel 2. Due to the limitation of needle punching density, it ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B24D13/16B24D13/04
Inventor 谢泽
Owner 谢泽
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products