A kind of tensile strength 780mpa level high reaming steel plate and its manufacturing method
A technology of tensile strength and manufacturing method, which is applied in the field of high-enlarging steel plate with a tensile strength of 780MPa and its manufacturing field, can solve the problems of poor manufacturability, large composition range, fluctuation of mechanical properties of steel plate, etc., and achieves low production cost. , good hole expansion performance, the effect of tissue uniformity
Active Publication Date: 2016-08-24
BAOSTEEL ZHANJIANG IRON & STEEL CO LTD +1
View PDF6 Cites 1 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
This process adopts two-stage cold rolling to produce hot-rolled steel plates with ferrite and bainite dual-phase structure and tensile strength greater than 690MPa. Management will lead to fluctuations in the mechanical properties of steel plate products and poor manufacturability
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0040] The present invention will be further described below in conjunction with the embodiments and accompanying drawings.
[0041] Table 1 is the composition of the steel of the embodiment of the present invention, and Table 2 is the hot rolling process of the steel of the embodiment of the present invention. Table 3 shows the mechanical properties of the steel gauges of the examples of the present invention.
[0042] The sample of the embodiment of the present invention is smelted by converter, RH+LF double refining treatment, continuous casting, slab heating temperature plus 1200-1260°C, final rolling temperature 860-930°C, cooling at a cooling rate greater than 30°C / s, The steel plate is coiled at a temperature of 480-580°C, and the steel coil is air-cooled to room temperature after coiling.
[0043] Comparative Example 1 and Comparative Example 2 are generally commercial materials of the same grade. The high hole reaming steel with a tensile strength of 780MPa in the i...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| tensile strength | aaaaa | aaaaa |
| thickness | aaaaa | aaaaa |
| tensile strength | aaaaa | aaaaa |
Login to View More
Abstract
A high-reaming steel plate with a tensile strength of 780MPa and a manufacturing method thereof, the chemical composition weight percent of which is: C: 0.02-0.1%, Si0.5-1.5%, Mn1.5-2.2%, P≤0.02%, S ≤0.003%, Al0.020~0.060%, N≤0.005%, Nb0.02~0.06%, Ti0.05~0.15%, Ca<0.0050%, Mg0~0.005%, the rest is Fe and unavoidable impurities; and , need to satisfy the following relationship at the same time: ([C]-12 / 48×([Ti]-48 / 14×[N])-12 / 93×[Nb])≥0.005. The invention has a tensile strength of 780MPa grade high-reaming steel plate with a reaming rate λ≥50%, which meets the production requirements of high-strength and light-weight chassis of the automobile industry in my country.
Description
technical field [0001] The invention relates to a high-hole-expanding steel plate, in particular to a high-hole-expanding steel plate with a tensile strength of 780MPa and a manufacturing method thereof. Background technique [0002] Hot-rolled and hot-rolled pickled sheets are widely used in automobile chassis, wheels and body structure parts, and they account for about 28% of the steel used in automobiles. The strength and rigidity of the parts can be improved through the shape design of the flanging and local reaming of the auto parts, and the purpose of thinning and lightening the auto steel plate can be achieved. The hole expansion performance of the steel plate is related to the composition, strength and structure uniformity of the steel plate. The traditional 780MPa steel plate (80 kg grade) is strengthened by low alloy precipitation, and the hole expansion rate of the steel plate is between 30% and 40%. With the development of lightweight automobiles, more and more ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/14C22C33/04C21D8/02
Inventor 郑建平庞厚君
Owner BAOSTEEL ZHANJIANG IRON & STEEL CO LTD