Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A kind of ultra-high-strength hot-rolled multi-phase steel plate and production method

A production method and ultra-high-strength technology, applied in the field of hot-rolled steel plate rolling, can solve the problems of low grade, achieve good extension flangeability, good hole expansion performance, and reduce the effect of cracking sensitive points

Active Publication Date: 2020-03-31
ANGANG STEEL CO LTD
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The tensile strength of the steel plate of this invention is partly 780MPa, which is a lower level

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ultra-high-strength hot-rolled multi-phase steel plate and production method
  • A kind of ultra-high-strength hot-rolled multi-phase steel plate and production method
  • A kind of ultra-high-strength hot-rolled multi-phase steel plate and production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0037] Ultra-high-strength hot-rolled multiphase steel plate and its production method, the chemical composition percentages of the hot-rolled multiphase steel plate are: C: 0.05% to 0.15%, Si: 0.1% to 0.8%, Mn: 1.2% to 2.3%, P≤0.012% , S≤0.005%, Cr: 0.20%~0.70%, Mo: 0.10%~0.50%, Nb: 0.02%~0.06%, Ti: 0.05%~0.13%, Als: 0.015%~0.060%, the rest are Fe and unavoidable impurities.

[0038] The production method of ultra-high-strength hot-rolled multi-phase steel plate, through two-stage controlled rolling and three-stage controlled cooling, the tensile strength can reach above 980MPa, and the microstructure is ferrite and bainite with a small amount of martensite and residual Austenitic multiphase steel plate.

[0039] The continuous casting slab of the above composition is heated to 1180-1280°C, and the slab is rolled in multiple passes on the rolling mill. The thickness of the intermediate slab is 35-45mm, preferably 40mm. The temperature is 840-950°C, and the cooling after rol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to an ultrahigh strength hot-rolled complex phase steel plate and a production method thereof. The ultrahigh strength hot-rolled complex phase steel plate comprises the followingchemical components of, by weight percentage, 0.05-0.15% of C, 0.1-0.8% of Si, 1.2-2.3% of Mn, no more than 0.012% of P, no more than 0.005% of S, 0.20-0.70% of Cr, 0.10-0.50% of Mo, 0.02-0.06% of Nb, 0.05-0.13% of Ti, 0.015-0.060% of Als and the balance Fe and inevitable impurities. The ultrahigh strength hot-rolled complex phase steel plate has the advantages that by controlling rolling and cooling, the effects of fine-grain strengthening, phase transformation strengthening and precipitation strengthening are comprehensively utilized, and the purposes that the high-strength performance of materials is maintained, the microhardness difference between two phases is reduced through precipitation strengthening, and the performance of chambering is improved are achieved.

Description

technical field [0001] The invention relates to the field of hot-rolled steel plate rolling, in particular to an ultra-high-strength hot-rolled multi-phase steel plate with a strength of 980 MPa and good hole expansion performance used in the field of automobile manufacturing and a production method. Background technique [0002] At present, the most challenging issues in the automobile manufacturing industry are the improvement of safety and crash performance, the reduction of fuel consumption and the reduction of environmental impact, and the application of cheap and reliable precision equipment. With regard to these aspects, the successful development of high-strength steels has solved some problems. The development and application of ultra-high-strength steel is an effective means to realize the lightweight of automobiles, which is in line with the development trend of energy saving, consumption reduction, environmental protection and safety of the new generation of auto...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/38C22C38/22C22C38/26C22C38/28C22C38/06C21D8/02
CPCC21D8/0226C21D2211/001C21D2211/002C21D2211/005C21D2211/008C22C38/02C22C38/04C22C38/06C22C38/22C22C38/26C22C38/28C22C38/38
Inventor 张宇时晓光韩斌董毅孙成钱陈妍刘仁东乔磊张吉富
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com