Non-magnetic Ti(C, N) base cermet with gradient structure and preparation method thereof

A cermet and magnetic gradient technology, applied in the field of Ti-based cermets, can solve the problems of non-magnetism and achieve the effects of improved bonding strength, low friction coefficient, excellent wear resistance and impact resistance

Active Publication Date: 2014-04-09
HUAZHONG UNIV OF SCI & TECH
View PDF2 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention provides a Ti(C,N)-based cermet with a non-magnetic gradient structure and a preparation method thereof, which solves the contradiction between the...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-magnetic Ti(C, N) base cermet with gradient structure and preparation method thereof
  • Non-magnetic Ti(C, N) base cermet with gradient structure and preparation method thereof
  • Non-magnetic Ti(C, N) base cermet with gradient structure and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] The present invention will be further described below in conjunction with specific examples.

[0024] The first group of embodiments is about the preparation method of Ti(C,N)-based cermet with non-magnetic gradient structure, including the steps of ball milling, molding, vacuum degreasing, vacuum sintering and high-temperature isostatic pressing surface nitriding treatment steps:

[0025] (1) Ball mill mixing step: according to the weight percent of the chemical composition of Ti(C, N) based cermet with non-magnetic gradient structure shown in Table 1, TiC, TiN, Ni, Mo 2 C, WC and Cr 3 C 2 The powder is used as a raw material to be prepared into a mixture, and then ball milling is carried out according to the ball mill mixing process parameters shown in Table 2 to obtain a uniform mixture slurry;

[0026] Table 1 The weight percent of the chemical composition of six non-magnetic gradient Ti(C, N)-based cermets

[0027]

[0028] Table 2 Process parameters for prep...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a non-magnetic Ti(C, N) base cermet with a gradient structure and a preparation method thereof, belonging to Ti(C, N) base cermets and solving the problem of contradictions between strong toughness and no magnetism of existing Ti(C, N) base cermets, so that the Ti(C, N) base cermet simultaneously has strong toughness and no magnetism. The non-magnetic Ti(C, N) base cermet with the gradient structure is prepared by using TiC, TiN, Ni, Mo2C, WC and Cr3C2 powder as the raw materials and carrying out ball-milling and mixing, die forming, vacuum degreasing, vacuum sintering and hot isostatic pressing surface nitriding. The non-magnetic Ti(C, N) base cermet has good wear resistance, red hardness, impact resistance and chemical stability, has low coefficients of friction with the materials such as iron and steel, silicon carbide and the like, has bending strength not less than 1800MPa, core matrix hardness of 86.0-92.5HRA and surface hardening layer Vickers microhardness of 1800-2050kg/mm<2>, is especially suitable for manufacturing non-magnetic cutting tools, non-magnetic dies and non-magnetic wear-resistant parts, has widened application range and has good popularization and application prospects in the industries such as tools and dies, national defences, military projects and the like.

Description

technical field [0001] The invention belongs to Ti(C,N)-based cermets, in particular to a Ti(C,N)-based cermet with a non-magnetic gradient structure and a preparation method thereof. Background technique [0002] With the rapid development of industries such as aerospace, national defense and military industry, communications, machinery, and energy equipment, the performance requirements for magnetic components are constantly improving. Using non-magnetic, wear-resistant molds for molding or tool cutting processing, forming resistance, The cutting resistance is small, which can ensure the consistency of the electromagnetic characteristics of the magnetic components and the processing quality and efficiency. Another example is that if wear-resistant parts such as mechanical seal rings on ships and other equipment are non-magnetic, the lightning protection performance of the equipment can be improved, which is conducive to magnetic stealth. [0003] The non-magnetic material...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C29/02C22C1/05
Inventor 熊惟皓杨青青张曼张国鹏陈肖黄斌姚振华
Owner HUAZHONG UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap