Basalt fiber-reinforced anti-cracking facing mortar

A technology of basalt fiber and veneer mortar, applied in the field of building materials, can solve the problems of easy cracking, short construction time, fading, etc., and achieve the effects of good acid and alkali resistance, good coating compactness, uniform and lasting color

Inactive Publication Date: 2014-05-07
安徽筑新纤维复合材料科技有限公司
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0014] However, the color decorative mortar currently on the market has problems such as fading and cracking, and has strict construction requirements, especially under some special construction conditions, such as short constr

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Basalt fiber reinforced anti-crack finishing mortar, its raw material ratio is:

[0032] Ordinary Portland white cement: 21 parts

[0033] Quartz sand: 59.25 parts

[0034] Chopped basalt fiber (single filament diameter 13μm, chopped length 6mm): 0.25 parts

[0035] Heavy calcium carbonate (200 mesh): 15 parts

[0036] Vinyl acetate and ethylene copolymer rubber powder: 3 parts

[0037] Natural hectorite: 0.4 parts

[0038] Methyl cellulose ether: 0.1 parts

[0039] Iron oxide red: 1 part.

[0040] Put each raw material component into the mixer according to the above ratio, stir evenly, pack into bags, and obtain the basalt fiber reinforced crack-resistant facing mortar.

[0041] During the construction of the colored mortar prepared in this example, 25% of water was added and stirred evenly, and sprayed or rolled on the outer wall surface. According to the building material industry standard of the People's Republic of China (JC / T1024-2007), the basalt fiber rei...

Embodiment 2

[0043] Basalt fiber reinforced anti-crack finishing mortar, its raw material ratio is:

[0044] Ordinary Portland white cement: 21 parts

[0045] Quartz sand: 61.45 parts

[0046] Chopped basalt fiber (single filament diameter 15μm, chopped length 9mm): 0.1 parts

[0047] Ground calcium carbonate (600 mesh): 11 parts

[0048] Acrylic and ethylene copolymer powder: 4 parts

[0049] 602#Thixotropic lubricant: 0.25 parts

[0050] Hydroxypropyl methylcellulose: 0.2 parts

[0051] Iron oxide red: 2 parts.

[0052] Put each raw material component into the mixer according to the above ratio, stir evenly, pack into bags, and obtain the basalt fiber reinforced crack-resistant facing mortar.

[0053]During the construction of the colored mortar prepared in this example, 25% of water was added and stirred evenly, and sprayed or rolled on the outer wall surface. According to the building material industry standard of the People's Republic of China (JC / T1024-2007), the basalt fiber ...

Embodiment 3

[0055] Basalt fiber reinforced anti-crack finishing mortar, its raw material ratio is:

[0056] Ordinary Portland white cement: 23.35 parts

[0057] Quartz sand: 52 parts

[0058] Chopped basalt fiber (18 μm single filament diameter, 15 mm chopped length): 0.5 parts

[0059] Ground calcium carbonate (300 mesh): 18 parts

[0060] Vinyl acetate and acrylic acid copolymer powder: 2.5 parts

[0061] 987#Thixotropic lubricant: 0.35 parts

[0062] Methyl cellulose ether: 0.3 parts

[0063] Iron oxide yellow: 3 parts.

[0064] Put each raw material component into the mixer according to the above ratio, stir evenly, pack into bags, and obtain the basalt fiber reinforced crack-resistant facing mortar.

[0065] During the construction of the colored mortar prepared in this example, 25% of water was added and stirred evenly, and sprayed or rolled on the outer wall surface. According to the building material industry standard of the People's Republic of China (JC / T1024-2007), the b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile bond strengthaaaaaaaaaa
Water absorptionaaaaaaaaaa
Tensile bond strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a building material, and particularly relates to a basalt fiber-reinforced anti-cracking facing mortar. The basalt fiber-reinforced anti-cracking facing mortar comprises the following components in parts by weight: 19-24 parts of cement, 51-62 parts of silica sand, and 0.1-0.5 part of basalt chopped fiber, wherein the monofilament diameter of the basalt chopped fiber is 9-18mu m, and the chopping length of the basalt chopped fiber is 3-15mm. In the basalt fiber-reinforced anti-cracking facing mortar, the adopted basalt chopped fiber has good acid-base resisting performance, can be effectively mixed into Portland cement in the facing mortar; the reinforced facing mortar has the advantages of good crack resistance, good weather resistance, good ultraviolet ray resistance, uniform color and the like, is durable, can be well combined with various inorganic basement materials, is good in coating compactness, and can be applied to the building fields of interior and exterior wall decoration and the like.

Description

technical field [0001] The invention relates to a building material, in particular to a basalt fiber reinforced crack-resistant facing mortar. Background technique [0002] Finishing mortar refers to a kind of physical mixing of dried and screened aggregate (such as quartz sand), inorganic cementitious material (such as white cement), additives (such as polymer, inorganic pigment) and so on in a certain proportion. Granular or powdery, transported to the construction site in bags or in bulk, and can be used directly after mixing with water. There are many colors of facing mortar, and it is generally used on the surface of the wall for interior and exterior wall decoration. It is suitable for the exterior wall decoration of high-end real estate and villas and the final decoration layer of the entertainment place and restaurant lamp personalized wall exterior insulation system. [0003] Compared with conventional facing materials, facing mortar has the following advantages: ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/04C04B14/46
Inventor 钱立兵李宁徐艳青
Owner 安徽筑新纤维复合材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap