Preparation method of solar photovoltaic aluminum alloy profile

An aluminum alloy profile and solar photovoltaic technology, which is applied in the field of aluminum alloy material processing, can solve problems such as insufficient mechanical properties, poor processing performance, and low corrosion resistance, so as to improve mechanical properties and processing performance, improve corrosion resistance, and improve The effect of as-cast structure

Active Publication Date: 2014-07-16
淮北津奥铝业有限公司
View PDF3 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the characteristics of the 6063 aluminum alloy itself and the unreasonable heat treatment process, the mechanical properties of the material are insufficient, the corrosion resistance is low, and the processing performance is poor, which greatly limits the wider application of the material.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] A method for preparing an aluminum alloy profile for solar photovoltaics, comprising the following steps:

[0015] (1) Put aluminum ingots, magnesium ingots, and scrap aluminum into the smelting furnace for smelting. The melting temperature is 730°C. When it is more than 80% melted, put in Al-Mn, Al-Cr and other intermediate alloys. After they are all melted, Adjust the temperature to 740°C, add 0.3% hexachloroethane and 0.1% sodium fluorosilicate to the melt weight and refine for 15 minutes. After refining, electromagnetically stir for 10 minutes and let stand for 25 minutes. B-La master alloy, heat preservation for 6 minutes, slag removal, sampling analysis, strict control of the weight percentage of each element composition of the aluminum alloy solution meets the following requirements: Si 0.2-0.5, Fe 0.05-0.1, Cu 0.1-0.15, Mn 0.1-0.2 , Mg 0.5-0.8, Cr 0.2-0.3, Ti 0.05-0.1, Zn 0.04-0.08, Nb 0.03-0.06, Ta 0.024-0.045, Po 0.02-0.04, B 0.004-0.008, La 0.03-0.0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a solar photovoltaic aluminum alloy profile. The aluminum alloy profile is composed of the following elements, by weight, 0.2-0.5% of Si, 0.05-0.1% of Fe, 0.1-0.15% of Cu, 0.1-0.2% of Mn, 0.5-0.8% of Mg, 0.2-0.3% of Cr, 0.05-0.1% of Ti, 0.04-0.08% of Zn, 0.03-0.06% of Nb, 0.024-0.045% of Ta, 0.02-0.04% of Po, 0.004-0.008% of B, 0.03-0.05% of La, 0.02-0.03% of Eu, 0.01-0.02% of Tb and the balance Al. The aluminum alloy profile provided by the invention has excellent mechanical property, processability and corrosion resistance, and is durable in use.

Description

technical field [0001] The invention relates to a method for preparing an aluminum alloy profile for solar photovoltaic, and belongs to the technical field of aluminum alloy material processing. Background technique [0002] Solar energy is a new type of inexhaustible pollution-free green energy. It is one of the seven emerging industries that my country has determined to focus on. Made of durable 6063 aluminum alloy material by extrusion, it is a new market for the application of 6063 aluminum alloy material and has been promoted and applied globally. However, due to the characteristics of the 6063 aluminum alloy itself and the unreasonable heat treatment process, the mechanical properties of the material are insufficient, the corrosion resistance is low, and the processing performance is poor, which greatly limits the wider application of the material. Contents of the invention [0003] The purpose of the present invention is to provide a method for preparing an aluminum...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/08C22C1/06C22F1/047
Inventor 刘长颂
Owner 淮北津奥铝业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap