A technology of rose essential oil and polyphenylene sulfide, which is applied in the field of modified polyphenylene sulfide materials and its preparation, can solve the problems of high brittleness, poor toughness, and low impact strength, and achieve easy processing and molding, improved performance, and good Effect of processability and mechanical properties

Inactive Publication Date: 2014-08-06
ANHUI YICAINI FIBER MATERIALS TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, polyphenylene sulfide resin also has the disadvantages of high brittle

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0012] Example

[0013] The materials of this example are made from the following raw materials by weight: polyphenylene sulfide 100, ACR impact modifier 9, rose essential oil 2, tartaric acid 3, diatomaceous earth 14, magnesium chloride 3, methacryloyloxypropyl Trimethoxysilane 3, diphenylsilyl diol 6, polyisobutylene 4, sodium ricinole sulfonate 2, polyacrylate 9, dioctyl maleate 8, auxiliary 15. The polyphenylene sulfide used in this example is a high molecular weight cross-linked PPS resin with a weight average molecular weight of 3.0-5×105.

[0014] The auxiliary agent is made from the following raw materials in parts by weight: clay 300, dimethylaminoethyl acrylate 3, nano-titanium dioxide 4, nano-silicon dioxide 1, SnO 2 1. B 2 O 3 5. Sodium Selenite 5, Antioxidant 1035 1, Dimethicone Oil 1, Clove Oil 1, Accelerator TMTD 2, Aluminum Hydroxide 8, Cross-linking Agent TAC 1; The preparation method is to put clay into a calciner Calcined at 740°C for 4 hours, cooled, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of polymer materials, and particularly relates to a modified polyphenyl thioether material containing rose ethereal oil for an automobile plastic part. The material is prepared by the following raw materials in parts by weight: 100 parts of polyphenyl thioether, 7-9 parts of an ACR anti-shock modifying agent, 1-2 parts of rose ethereal oil, 2-3 parts of tartaric acid, 12-14 parts of diatomite, 2-3 parts of magnesium chloride, 2-3 parts of methylacryloyl-oxy-propyl-trimethoxy silane, 4-6 parts of diphenyl silicon glycol, 3-4 parts of polyisobutene, 1-2 parts of castor alcohol sodium sulfonate, 6-9 parts of polyacrylic ester, 6-9 parts of maleic acid dioctyl phthalate, and 12-15 parts of an auxiliary. The modified polyphenyl thioether material combines the advantages of raw materials of the polyphenyl thioether, the polyisobutene, the polyacrylic ester, and the like, modifies properties of conventional polyphenyl thioether materials; the prepared material is solid, easy to process and form, heat ageing resisting, good in chemical stability, smooth in hand feeling, provided with a fragrant smell, and safe and reliable to use, and can be widely used for manufacturing various automobile-used plastic parts.

Description

technical field [0001] The invention belongs to the field of polymer materials, and in particular relates to a modified polyphenylene sulfide material containing rose essential oil for automobile plastic parts and a preparation method thereof. Background technique [0002] PPS resin has high strength, high rigidity, and the rigidity decreases very little under high temperature conditions, and has excellent fatigue resistance and creep resistance; it is widely used in auto parts and has good development potential and competitiveness. However, polyphenylene sulfide resin also has the disadvantages of high brittleness, poor toughness and low impact strength, so it is limited in application. [0003] In order to improve the performance of PPS resin materials and broaden the application range of materials, it is necessary to modify the PPS resin materials so that they can be widely used in various parts of automobiles. SUMMARY OF THE INVENTION [0004] The purpose of the prese...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L71/12C08L23/20C08L33/08C08K13/06C08K9/02C08K3/34C08K5/092C08K3/16C08K5/5425C08K5/5419C08K5/42C08K5/11C08K5/17C08K3/22C08K3/36C08K3/38C08K3/30
Inventor 章云张娃妮柯模松
Owner ANHUI YICAINI FIBER MATERIALS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products