Novel sculpture mortar

A kind of sculpture and mortar technology, applied in the field of new sculpture mortar, can solve the problems of lack of scientific proportioning, insufficient time for sculpture modeling, poor three-dimensional effect, etc.

Active Publication Date: 2014-10-15
SUZHOU TASHI LANDSCAPE ENG TECH CO LTD
View PDF6 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the usual method of making cement-based, plastic stone, rockery, imitation wood, and imitation stone walls is: use ordinary cement sand as the basic material, then use a mixer to mix it into mortar, and directly sculpt it. The main shortcomings are: 1: General Plastic stone and rockery use metal cabinet frames and steel wire mesh as the base surface. After the ordinary mortar is applied to the base surface, it will dehydrate quickly, resulting in reduced strength and many cracks; 2: The solidification time is earlier, and the time for sculpture is not enough Sufficient; 3: The mortar mix ratio is artificially operated randomly, lacking a unified scientific ratio, the quality is unstable, and the service life is short; 4: The thickness of the plaster is 2-3cm, which cannot reach a sufficient thickness, and the three-dimensional effect of the sculpture is not good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] A new type of sculpture mortar, composed of the following components by mass percentage: 41.14% of 32.5R ordinary Portland cement, 55% of 40-80 mesh sand (quartz sand), 1% of 50-70 mesh lightweight aggregate, cellulose Ether 0.02%, dispersible latex powder 0.04%, water reducing agent 0.4%, silicon powder 2%, lignin fiber 0.4%, polypropylene fiber 0%, mix and stir by dry powder mortar mixer, and stir for 20 It can be used in minutes. The mixed sculpture mortar is packaged in a paper packaging bag, 25kg per bag.

[0016] The production and processing order of the constituent materials is: sand - cellulose ether - dispersible latex powder - water reducer - silicon powder - lignin fiber - lightweight aggregate - cement.

[0017] Engineering Example

[0018] Lishui City Adventure Island Water World Phase II imitation stone and imitation wood sculpture project, consumption: 90 tons, production area 1200 square meters, designed with two decorative forms of imitation stone sha...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a novel sculpture mortar. The novel sculpture mortar comprises the following components: 40-50% of 32.5R ordinary Portland cement, 45%-55% of 40-80 mesh sand ( quartz sands), 1-2% of 50-70 mesh light-weight aggregates, 0.01-0.1% of cellulose ether, 0.02-0.2% of dispersible latex powder, 0.2-0.4% of a water-reducing agent, 2-3% of silica powder, 0.3-0.4% of lignin fiber and 0-0.04% of polyropylene fiber. The component composition is to fulfill the following purposes: the operation is simple; no other materials are required for adding and the sculpture mortar can be directly utilized; the novel sculpture mortar facilitates the construction and has excellent workability; the sag resistance of the novel sculpture mortar enables the thickness of the troweling at one time to be more than 5 cm; a more stereoscopic and richer sculptural effect can be created; the construction efficiency is improved; cracks are rarely found on the sculpture and the simulation effect is improved; the structure is compact; the matching is reasonable and the service life can be prolonged; industrialized production is realized, so that the quality is stable and guaranteed.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a novel sculpture mortar. Background technique [0002] At present, the usual method of making cement-based, plastic stone, rockery, imitation wood, and imitation stone walls is: use ordinary cement sand as the basic material, then use a mixer to mix it into mortar, and directly sculpt it. The shortcomings are mainly manifested in: 1: General Plastic stone and rockery use metal cabinet frames and steel wire mesh as the base surface. After the ordinary mortar is applied to the base surface, it will dehydrate quickly, resulting in reduced strength and many cracks; 2: The solidification time is earlier, and the time for sculpture is not enough Sufficient; 3: The mortar mix ratio is artificially operated randomly, lacking a unified scientific ratio, the quality is unstable, and the service life is short; 4: The thickness of the plaster is 2-3cm, which cannot reach a sufficient thick...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/04C04B14/06C04B24/38
Inventor 徐永德
Owner SUZHOU TASHI LANDSCAPE ENG TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products