Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Adhesive Composition, Adhesive And Adhesive Sheet

A composition and adhesive technology, applied in the field of adhesives, adhesive sheets, and adhesive compositions, can solve the problems of change, corrosion of ITO resistance value, etc., and achieve the effect of excellent warpage resistance

Active Publication Date: 2014-12-31
LINTEC CORP
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, due to the binder containing a large amount of carboxyl group as an acid component, there is a problem that ITO is corroded or the resistance value of ITO is changed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Adhesive Composition, Adhesive And Adhesive Sheet
  • Adhesive Composition, Adhesive And Adhesive Sheet
  • Adhesive Composition, Adhesive And Adhesive Sheet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0117] 1. Preparation of (meth)acrylate polymer

[0118] 76.9 parts by mass of n-butyl acrylate, 10 parts by mass of methyl acrylate, 10 parts by mass of 2-phenylethyl acrylate, 3 parts by mass of 2-hydroxyethyl acrylate and 0.1 parts by mass of acrylic acid were copolymerized to prepare ( Meth)acrylate polymer (A). When the molecular weight of this (meth)acrylate polymer (A) was measured by the method mentioned later, it was 1.5 million weight average molecular weight.

[0119] 2. Preparation of adhesive composition

[0120] 100 parts by mass (solid content conversion value; the same below) of the (meth)acrylate polymer (A) obtained in the above step (1), 0.2 parts by mass of trimethylol as the isocyanate crosslinking agent (B) Propane-modified tolylene diisocyanate (manufactured by Nippon Polyurethane Industry Co., Ltd., trade name "CORONATE L"), 0.3 parts by mass of 3-mercaptopropyltrimethoxysilane as a silane coupling agent (C) having a mercapto group, and A cocondensat...

Embodiment 2～14

[0134] [Examples 2-14, Comparative Examples 1-6]

[0135] In addition to the type and ratio of each monomer constituting the (meth)acrylate polymer (A), the weight average molecular weight of the (meth)acrylate polymer (A), and the compounding amount of the isocyanate crosslinking agent (B) , and the kind and compounding quantity of the silane coupling agent (C) were changed as shown in Table 1, and it carried out similarly to Example 1, and manufactured the polarizing plate with an adhesive bond layer. In addition, in Example 5, when preparing the adhesive composition, an equimolar mixture of 1.8 parts by mass of bis(trifluoromethanesulfonimide) lithium and tetraethylene glycol dimethyl ether was blended as an antistatic agent. product (manufactured by Sanko Chemical Co., Ltd., trade name "SANKONOL TGR").

[0136] Here, the above-mentioned weight average molecular weight (Mw) is a weight average molecular weight in terms of polystyrene measured (GPC measurement) under the fo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
gel fractionaaaaaaaaaa
Login to View More

Abstract

The present invention provides an adhesive composition, an adhesive and an adhesive sheet, which do not influence the adhered objects, such as the transparent conductive film, etc., at the same time, are excellent in durability and light leakage resistance, and are excellent in buckling resistance of a laminator containing an adhesive layer. and In order to solve the above subject, the adhesive composition which contains a (methyl) acrylate polymer (A), an isocyanate class cross-linking agent (B) and a silane coupling agent possessing sulfydryl (C) is provided, and the weight-average molecular weight of the above (methyl) acrylate polymer (A) is 1.4-2.5 millions. A monomeric unit as the polymer contains a monomer possessing the hydroxy, a monomer possessing the aromatic nucleus and a monomer possessing the carboxyl. The (methyl) acrylate polymer (A) as the monomeric unit of the polymer, contains 5-30% by mass of the monomer possessing the aromatic nucleus, and 0.1-0.8 % by mass of the monomer possessing the carboxyl.

Description

technical field [0001] The present invention relates to an adhesive composition, an adhesive (a material for crosslinking the adhesive composition), and an adhesive sheet, and particularly relates to an adhesive combination suitable for optical members such as polarizers materials, adhesives and bonding sheets. Background technique [0002] In recent years, in various electronic devices, a touch panel that also functions as a display device and an input device is frequently used. The types of touch panels mainly include resistive, capacitive, optical and ultrasonic. Resistive touch panels include analog resistive and matrix resistive, and capacitive touch panels include surface and projection types. [0003] The touch panels of mobile electronic devices such as smartphones and tablet terminals that have recently attracted attention often use projected capacitive touch panels. As the projected capacitive touch panel of the mobile electronic device, for example, some studie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J133/08C09J11/06C09J7/02
CPCC09J9/00C09J11/06C09J133/066C09J7/20G02B5/30
Inventor 又野仁荒井隆行所司悟
Owner LINTEC CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com