Metal-welded planar double-vacuum-layer glass with sealing strips and mounting holes

A technology of metal welding and sealing strips, which is applied in the field of flat double-vacuum glass and its production, to reduce production costs, increase airtightness, and improve life expectancy

Inactive Publication Date: 2015-01-21
戴长虹
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The technical problem to be solved by the present invention is to provide a flat double-vacuum glass with metal welded sealing strips and mounting holes and its manufacturing method for the defects of the existing vacuum glass. The manufacturing method of this vacuum glass is simple in pro

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal-welded planar double-vacuum-layer glass with sealing strips and mounting holes

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0044] Example: referring to the attached drawings, the flat double vacuum layer glass is composed of upper glass 1, middle glass 8 and lower glass 2. At least the upper and lower glass of the three glasses are tempered glass or semi-tempered glass, and at least one glass is still low The manufacturing method of radiant glass is as follows: First, cut three pieces of flat glass of the required size according to the shape and size of the flat double vacuum layer glass to be produced, drill a through hole on the three pieces of glass to form the mounting hole 3, and align the three pieces of glass. The glass block is ground, chamfered, cleaned and dried; secondly, seal strips 5 and 6 are printed at the periphery of the upper glass 1, the lower glass 2 and the middle glass 8 and the periphery of the mounting hole 3. The support 7 is printed on the lower surface and the upper surface of the lower glass 2, the middle glass 8 is sent to a high-temperature furnace for high-temperature ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to metal-welded planar double-vacuum-layer glass with sealing strips and mounting holes. The glass comprises upper glass, lower glass and intermediate glass. The glass is characterized in comprising mounting holes. The upper glass, intermediate glass and lower glass are planar glass. At least one sealing strip is provided at each of the peripheries of the lower surfaces of the upper glass and the intermediate glass, and at each of the peripheries of the mounting holes on the lower surfaces of the upper glass and the intermediate glass. At least two sealing strips are provided at each of the peripheries of the upper surface of the intermediate glass and the lower glass, and at each of the peripheries of the mounting holes on the upper surfaces of the intermediate glass and the lower glass. The peripheries of the three pieces of glass are automatically welded together by using a metal solder in a vacuum furnace. The mounting holes are automatically sealed by using the metal solder. The planar double-vacuum-layer glass and the preparation method thereof have simple process. The prepared planar double-vacuum-layer glass and tempered planar double-vacuum-layer glass are beneficial for mounting and application. Air-tightness of the vacuum glass can be effectively ensured. Strength, thermal insulation performance and sound insulation performance of the vacuum glass can be enhanced.

Description

technical field [0001] The invention relates to the technical field of glass deep processing, in particular to a plane double-vacuum-layer glass with metal welding sealing strips and mounting holes and a manufacturing method thereof. [0002] Background technique [0003] Vacuum glass is a new type of energy-saving glass. Vacuum glass can not only solve the "breathing" problem of insulating glass used in large quantities, but also has good heat and sound insulation performance, high wind pressure resistance, small thickness and long service life. advantage. Vacuum glass is generally composed of two to three pieces of glass, a cavity is formed between two adjacent pieces of glass, and an edge sealing structure is arranged around the glass, and the cavity is evacuated to form a vacuum layer. Vacuum glass can be divided into two types according to the way of forming the vacuum layer. One is the vacuum glass without air extraction port. The edge sealing of this vacuum glass is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C27/08
CPCC03C27/08
Inventor 戴长虹
Owner 戴长虹
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap