Abstract

A steel wire rod or bar steel, the chemical composition of which comprises, in terms of mass%, 0.1-0.6% of C, 0.01-1.5% of Si, 0.05-2.5% of Mn, 0.015-0.3% of Al, and 0.004-0.015% of N, optionally together with definite arbitrary element(s), with the balance consisting of iron and impurities, wherein the impurities contain not more than 0.035% of P and not more than 0.025% of S. In the steel wire rod or bar steel: a surface layer area to a depth equivalent to 15% of the section radius from the surface is a steel tissue that is configured from ferrite having an average particle diameter of 1-15 mum and spherical cementite having an average aspect ratio of 2 or less and an average particle diameter of 0.1-2 mum; an inner area ranging from the point of a depth equivalent to 25% of the section radius from the surface to the core is a steel tissue that is configured from ferrite having an average particle diameter of 15-40 mum and pearlite and/or spherical cementite; after removing surface scale, the surface roughness (Ra) of the surface in the circumferential direction is not more than 4 mum; and the depth of a grain boundary oxidation layer on the surface is not more than 30 mum.

Description

technical field [0001] The present invention relates to steel wire rods or steel bars (including bar in coils; the same applies hereinafter) suitable for cold forging and the like. This application claims the priority based on Japanese Patent Application No. 2012-131316 for which it applied to Japan on June 8, 2012, The content is used here. Background technique [0002] In recent years, in order to increase productivity, it is required to reduce or omit mechanical processing represented by cutting, so the demand for cold forging for medium carbon steel is increasing. However, the deformation resistance of medium carbon steel is higher than that of low carbon steel and low alloy steel, and lacks deformation ability (ductility), so there is a problem that mold cracking and steel material cracking are prone to occur. Therefore, in order to reduce deformation resistance and improve deformability of steel materials for cold forging, spheroidizing annealing for spheroidizing cem...

AI Technical Summary

Problems solved by technology

However, it is limited to steel structures that only specify ferrite and cementite, and there is no regulation on the

Images