Cathode material used for solid oxide electrolytic cell and application of cathode material

A solid oxide and cathode material technology, applied in electrodes, electrolytic processes, electrolytic components, etc., can solve the problems of solid oxide electrolytic cells that need to be deepened, Ni agglomeration and volatilization, and low water vapor transmission rate

Active Publication Date: 2015-03-04
TSINGHUA UNIV
View PDF4 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, it was found that the Ni/YSZ cathode material used in the related art would have problems such as low water vapor transmission rate, agglomeration and volatilization of Ni in the high-temperature and high-humidity environment of hi...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cathode material used for solid oxide electrolytic cell and application of cathode material
  • Cathode material used for solid oxide electrolytic cell and application of cathode material
  • Cathode material used for solid oxide electrolytic cell and application of cathode material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0076] 1. Preparation of cathode slurry

[0077] With Sr(NO 3 ) 2 , Fe(NO 3 ) 3 9H 2 O, Mg(NO 3 ) 2 ·6H 2 O, (NH 4 ) 6 Mo 7 o 24 4H 2 O is the raw material, according to Sr 2 Fe 0.9 Mg 0.1 MoO 6-δ The stoichiometric ratio weighs the required raw materials, dissolves citric acid in an appropriate amount of deionized water, and adds accurately weighed Sr(NO 3 ) 2 , Fe(NO 3 ) 3 9H 2 O, Mg(NO 3 ) 2 ·6H 2 O, in order to avoid the formation of ferric molybdate precipitation under weak acid conditions, ammonium molybdate is dissolved in deionized water to form a clear solution and then added to the above mixed solution, wherein the molar ratio of citric acid to the total number of metal ions is guaranteed to be 2:1. Aqueous ammonia was then added to adjust the pH to about 3. Then the solution was placed in a 90°C water bath and heated to evaporate for several hours until a gel was formed. Next, put the gel into a 180°C incubator and continue heating until it ...

Embodiment 2

[0088] 1. Preparation of cathode slurry

[0089] With Sr(NO 3 ) 2 , Fe(NO 3 ) 3 9H 2 O, (NH 4 ) 6 Mo 7 o 24 4H 2 O is the raw material, according to Sr 2 FeMoO 6-δ The stoichiometric ratio weighs the required raw materials, dissolves citric acid in an appropriate amount of deionized water, and adds accurately weighed Sr(NO 3 ) 2 , Fe(NO 3 ) 3 9H 2 O, in order to avoid the formation of ferric molybdate precipitation under weak acid conditions, ammonium molybdate is dissolved in deionized water to form a clear solution and then added to the above mixed solution, wherein the molar ratio of citric acid to the total number of metal ions is guaranteed to be 2:1. Aqueous ammonia was then added to adjust the pH to about 2. Then the solution was placed in a 90°C water bath and heated to evaporate for several hours until a gel was formed. Next, put the gel into a 180°C incubator and continue heating until it burns. After cooling, take out the fluffy combustion product ...

Embodiment 3

[0099] 1. Preparation of cathode slurry

[0100] With Sr(NO 3 ) 2 , Mg(NO 3 ) 2 ·6H 2 O, (NH 4 ) 6 Mo 7 o 24 4H 2 O is the raw material, according to Sr 2 MgO 6-δ The stoichiometric ratio weighs the required raw materials, dissolves citric acid in an appropriate amount of deionized water, and adds accurately weighed Sr(NO 3 ) 2 , Mg(NO 3 ) 2 ·6H 2 O, in order to avoid the formation of ferric molybdate precipitation under weak acid conditions, ammonium molybdate is dissolved in deionized water to form a clear solution and then added to the above mixed solution, wherein the molar ratio of citric acid to the total number of metal ions is guaranteed to be 2:1. Aqueous ammonia was then added to adjust the pH to about 3. Then the solution was placed in a 60°C water bath and heated to evaporate for several hours until a gel was formed. Next, put the gel into a 160°C incubator and continue heating until it burns. After cooling, take out the fluffy combustion product ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a cathode material used for a solid oxide electrolytic cell and application of the cathode material. The chemical constitution of the cathode material is Sr2Fe1-xMxMoO6-Delta, wherein x is larger than or equal to 0 and smaller than or equal to 1; M is one or more selected from Mg, Zn, Ni, Co, Cu and Mn; an SrMoO3 phase is not contained in the cathode material. The cathode material does not comprise the SrMoO3 phase, adopts a single perovskite phase structure, can effectively solve the problem that the electrochemical performance of the Sr2Fe1-xMxMoO6-Delta is undesirable due to existence of the SrMoO3 phase, has favorable electrochemical performance, and can effectively improve hydrogen manufacturing efficiency of the solid oxide electrolytic cell.

Description

technical field [0001] The invention relates to the field of solid oxide electrolytic cells, in particular, to cathode materials for solid oxide electrolytic cells and applications thereof, more specifically, to cathode materials for solid oxide electrolytic cells, and cathodes for solid oxide electrolytic cells - Electrolyte-anode assembly and method for its preparation and solid oxide electrolytic cell. Background technique [0002] Due to the increasingly prominent energy and environmental issues, people have paid more and more attention to the scientific issue of hydrogen production by high-temperature electrolysis of water. In the field of basic research related to solid oxide electrolytic cells, such as electrode materials, electrolyte materials, connector materials and sealing materials, and the overall performance of single cells, there are continuous reports of new achievements. [0003] However, it was found that the Ni / YSZ cathode material used in the related art...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C25B1/04C25B11/04
CPCC25B1/04C25B11/04Y02E60/36
Inventor 马景陶盖文超赵兴宇郝少昌邓长生
Owner TSINGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap