Physical upgrading method for enrichment of carbonaceous shale type vanadium ore

A carbonaceous shale, enrichment technology, applied in chemical instruments and methods, wet separation, solid separation, etc., can solve the problems of high metallurgical cost and low grade of vanadium ore, and achieve high separation accuracy and equipment production capacity. Large, low production cost effect

Active Publication Date: 2015-03-25
贵州省贵金属矿产资源综合利用工程技术研究中心有限公司
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to solve the problems of low grade of carbonaceous shale-type vanadium ore in the prior art and high metallurgical cost. The minerals are mainly quartz minerals with relatively heavy sp

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0021] Example 1:

[0022] Follow these steps to implement:

[0023] (1) crushing and grinding the vanadium-containing carbonaceous shale ore to a fineness of -2.0mm, and sieving out the part with a fineness of -0.15mm as a concentrate product;

[0024] (2) Put the ore with a fineness of +0.15mm~-2.0mm in a heavy medium cyclone, use ferrosilicon powder as a medium weighting agent, and use a combination of compressed air and mechanical stirring to mix the ferrosilicon powder and the ore , using YTMC250 / 175 heavy medium cyclone, the separation medium density is 1225kg / m 3 , the feeding pressure is 0.07MPa, the second-stage overflow diameter is 40mm, the second-stage underflow diameter is Φ35mm, and the medium-to-ore ratio is 8:1, and the concentrate products and tailings products are sorted.

[0025] (3) the concentrate product obtained in the step (2) is mixed with the concentrate product screened out in the step (1) after the ferrosilicon powder is recovered by magnetic sepa...

Example Embodiment

[0027] Example 2:

[0028] Follow these steps to implement:

[0029] (1) crushing and grinding the vanadium-containing carbonaceous shale ore to a fineness of -1.0mm, and sieving out the part with a fineness of -0.15mm as a concentrate product;

[0030] (2) Put the ore with a fineness of +0.15mm to -1.0mm in a heavy medium cyclone, use ferrosilicon powder as a medium weighting agent, and use a combination of compressed air and mechanical stirring to mix the ferrosilicon powder and the ore. , using YTMC250 / 175 heavy medium cyclone, the separation medium density is 1275kg / m 3, the feeding pressure is 0.08MPa, the second-stage overflow diameter is Φ40mm, the second-stage underflow diameter is Φ30mm, and the medium-to-ore ratio is 6:1, and the concentrate products and tailings products are sorted.

[0031] (3) the concentrate product obtained in the step (2) is mixed with the concentrate product screened out in the step (1) after the ferrosilicon powder is recovered by magnetic ...

Example Embodiment

[0033] Example 3:

[0034] Follow these steps to implement:

[0035] (1) crushing and grinding the vanadium-containing carbonaceous shale ore to a fineness of -3.0mm, and sieving out the part with a fineness of -0.15mm as a concentrate product;

[0036] (2) Put the ore with a fineness of +0.15mm~-3.0mm in the heavy medium cyclone, use the ferrosilicon powder as the medium weighting agent, and mix the ferrosilicon powder with the ore by the combination of compressed air and mechanical stirring. , using YTMC250 / 175 heavy medium cyclone, the separation medium density is 1325kg / m 3 , the feeding pressure is 0.06MPa, the second-stage overflow diameter is Φ50mm, the second-stage underflow diameter is Φ35mm, and the medium-to-ore ratio is 7:1 to separate concentrate products and tailings products.

[0037] (3) the concentrate product obtained in the step (2) is mixed with the concentrate product screened out in the step (1) after the ferrosilicon powder is recovered by magnetic sep...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Finenessaaaaaaaaaa
Finenessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a physical upgrading method for enrichment of carbonaceous shale type vanadium ore. According to the physical upgrading method, dense-medium separation is adopted in combination with hydrometallurgical leaching; in the dense-medium separation step, ferrosilicon powder is used as a medium heavy loader; after a concentrate product and a tailing product are obtained through separation, the ferrosilicon powder is recovered based on the magnetic separation method; a dense medium cyclone YTMC250/175 is adopted, the density of separating media is 1,225 kg/m<3>-1,450 kg/m<3>, ore feeding pressure intensity is 0.01 MPa-0.08 MPa, the second-stage overflow caliber phi is 40 mm-50 mm, the second-stage underflow caliber phi is 25 mm-35 mm, and the ratio of the media to ore is 8:1-2:1. The physical upgrading method can lower the ore grinding cost, and the ferrosilicon powder is adopted to serve as the dense medium heavy loader; the physical upgrading method has the advantages that equipment production capacity is high, separation accuracy is high, medium loss is small, and the production cost is low; by adopting the ferrosilicon powder as the upgrading heavy loader, no influence acts on the environment, and the subsequent vanadium extraction leaching rate through hydrometallurgical leaching is not affected.

Description

technical field [0001] The invention relates to a physical beneficiation method, in particular to a method for enriching carbonaceous shale-type vanadium ore by physical beneficiation. Background technique [0002] Vanadium is an important material for high-tech industries such as special steel, vanadium-titanium alloys, catalysts, and all-vanadium flow energy storage batteries, and is widely used in modern industrial technology. Vanadium ore resources mainly include vanadium-titanium magnetite and vanadium-bearing carbonaceous shale, among which vanadium-bearing carbonaceous shale accounts for 87% of the total reserves of vanadium ore resources in my country, and is an important resource of vanadium. [0003] Because vanadium in carbonaceous shale-type vanadium deposits mainly occurs in mica minerals in the form of isomorphism, the particle size of the vanadium-loaded minerals is too fine, and it is very difficult to beneficiate. Shale-type vanadium ores are used as raw ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B03B7/00B03B9/00
CPCB03B7/00B03B9/00
Inventor 陈文祥龙忠银邓强胡万明余红林陈婧
Owner 贵州省贵金属矿产资源综合利用工程技术研究中心有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap