Manufacturing method of quartz stone kitchen surface board in integral molding mode

A manufacturing method and technology of quartz stone, applied in the direction of manufacturing tools, ceramic molding machines, etc., can solve the problems affecting the pace of the development of quartz stone countertops, the influence of multiple processing procedures, and the low strength of the bonding surface, achieving low cost and high durability. The effect of low scratching and curing temperature

Inactive Publication Date: 2015-04-22
SANMENXIA BOSHI MINING
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The existing quartz stone kitchen panels have defects such as bonding and glue opening, exposed bonding seams, many processing procedures affecting production cap

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] Quartz stone kitchen panel specifications:

[0046] Production specifications: width 1000mm x length 2200 mm x thickness 15 mm frame height 40 x width 30 mm

[0047] Mold appearance specifications: width 1080mm × length 2280 mm × height 50 mm frame height 50 × width 40 mm

[0048] Dimensions of convex mold: width 940mm × length 2140 mm × height 18 mm;

[0049] After weighing the selected raw materials according to the production ingredient list, they are mixed evenly in the mixer system through the conveyor belt. Additives, fully stir evenly, avoid stirring dead ends. After stirring, the qualified mixture is transported to the distributing machine, which is evenly distributed into the special mold by the distributing machine, and is transported together with the mold to the vacuum high-frequency press system for pressing. After pressing, the quartz stone kitchen panel is initially formed and enters through the conveying line. In the sealed curing furnace, aft...

Embodiment 2

[0051] Quartz stone kitchen panel specifications:

[0052] Production specifications: width 780mm x length 1500 mm x thickness 15 mm frame height 40 x width 30 mm

[0053] Mold appearance specifications: width 860mm × length 1580 mm × height 50 mm frame height 50 × width 40 mm

[0054] Dimensions of convex mold: width 720mm × length 1440 mm × height 18 mm;

[0055] After weighing the selected raw materials according to the production ingredient list, they are mixed evenly in the mixer system through the conveyor belt. Additives, fully stir evenly, avoid stirring dead ends. After stirring, the qualified mixture is conveyed to the distributing machine, which is evenly distributed into the special mold by the distributing machine, and is transported together with the mold to the vacuum high-frequency press system for pressing. After pressing, the quartz stone kitchen panel is initially formed and enters through the conveying line. In the sealed curing furnace, after curi...

Embodiment 3

[0057] Quartz stone kitchen panel specifications:

[0058] Production specifications: width 580mm x length 1200 mm x thickness 15 mm frame height 40 x width 30 mm

[0059] Mold appearance specifications: width 660mm × length 1280 mm × height 50 mm frame height 50 × width 40 mm

[0060] Dimensions of convex mold: width 520mm × length 1140 mm × height 18 mm;

[0061] After weighing the selected raw materials according to the production ingredient list, they are mixed evenly in the mixer system through the conveyor belt. Additives, fully stir evenly, avoid stirring dead ends. After stirring, the qualified mixture is conveyed to the distributing machine, which is evenly distributed into the special mold by the distributing machine, and is transported together with the mold to the vacuum high-frequency press system for pressing. After pressing, the quartz stone kitchen panel is initially formed and enters through the conveying line. In the sealed curing furnace, after curing...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Densityaaaaaaaaaa
Flexural strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a manufacturing method of a quartz stone kitchen surface board in an integral molding mode. According to the method, the quartz stone kitchen surface board is manufactured by utilizing resourceful natural quartz stone raw materials to serve as main raw materials and properly adding auxiliary raw materials. The kitchen surface board has the advantages that materials are arranged in a specially made mould, and the kitchen surface board is integrally molded through a pressing and curing system; accordingly, the costs of cutting, splicing and processing boards by workers are saved, the materials are saved, and the strength and the yield of the boards are improved; the defects of dirt accumulation and bacteria breeding of natural stones are overcome, and the quartz stone kitchen surface board is easy to clean, good in resistance to scratch, dirt, heat, corrosion, ageing and color fading and free of poison and radiation; the production process of vacuum high-frequency pressing and one-time curing and molding is adopted, and compared with similar products, the quartz stone kitchen surface board is higher in strength, free of cracks, attractive in appearance and capable of saving the materials and time, and greatly improves the production efficiency and economic benefits.

Description

Technical field [0001] The present invention involves the field of home improvement kitchen utensils, and is a one -time manufacturing method of quartz stone kitchen panels with silicate products. Background technique [0002] Quartzes are made of large -sized plates through heterogeneous aggregation technology under vacuum conditions under vacuum conditions under vacuum conditions. Its 92%of the quartz crystals are the main structure, making its texture harder and close, with other other other, with other otherDecorative materials cannot compare the characteristics of abrasion, pressure resistance, high temperature resistance, corrosion resistance, and anti -penetration.The colorful combination makes it have the texture of natural stone and the beautiful surface luster.Metracking Mask mask has the superiority that other materials cannot compare. As soon as it is generated, it is sought after by people. The production technology and supporting production equipment industry have g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B28B3/00
CPCB28B3/00
Inventor 匡江南
Owner SANMENXIA BOSHI MINING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap