A kind of manufacturing method of aluminum alloy thin wire

A manufacturing method and technology of aluminum alloy wire, applied in the direction of metal/alloy conductor, cable/conductor manufacturing, electrical components, etc., to achieve the effects of reduced power loss, high electrical conductivity, and large elongation at break

Inactive Publication Date: 2017-01-04
TONGYONG TIANJIN ALUMINUM ALLOY PROD CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, whether it is pure aluminum or aluminum alloy, the single wire diameter of the conductor is usually above 1.0mm, and the conductor type composed of it is a second-class conductor according to the standard regulations. The single wire preparation is drawn by a larger wire drawing machine. Complete in one step, there is no precedent for aluminum or aluminum alloy conductors as flexible conductors (category five / category six) in the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of manufacturing method of aluminum alloy thin wire

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Embodiment 1 of the present invention provides a method for manufacturing an aluminum alloy filament with a wire diameter of 0.2 mm, comprising the following steps:

[0040] a) Initial drawing: the aluminum alloy rod is drawn and processed into an aluminum alloy wire, and the drawing speed of the drawing process is 30m / s;

[0041] b) Secondary drawing: the aluminum alloy wire obtained in step a) is drawn into an aluminum alloy wire, and the drawing speed of the drawing process is 15m / s;

[0042] c) Three-time drawing: the aluminum alloy wire obtained in step b) is drawn into aluminum alloy filaments, and the drawing speed of the drawing process is 10m / s;

[0043] d) Heat treatment process: the aluminum alloy filament obtained in step c) is subjected to a process of heating-heating-cooling, wherein,

[0044] During the heating process, the aluminum alloy filament is heated to 340°C, and the required heating time is 2 hours;

[0045] During the heat preservation process...

Embodiment 2

[0054] Embodiment 2 of the present invention provides a method for manufacturing aluminum alloy filaments with a wire diameter of 0.2 mm. The same parts as those in Embodiment 1 will not be described in detail, and the differences are as follows:

[0055] Include the following steps:

[0056] a) Initial drawing: the aluminum alloy rod is drawn into an aluminum alloy wire, and the drawing speed of the drawing process is 20m / s;

[0057] b) Secondary drawing: the aluminum alloy wire obtained in step a) is drawn into an aluminum alloy wire, and the drawing speed of the drawing process is 10m / s;

[0058] c) Three-time drawing: the aluminum alloy wire obtained in step b) is drawn to make aluminum alloy filaments, and the drawing speed of the drawing process is 15m / s;

[0059] d) Heat treatment process: the aluminum alloy filament obtained in step c) is subjected to a process of heating-heating-cooling, wherein,

[0060] In the above heating process, the temperature of the aluminum...

Embodiment 3

[0064] Embodiment 3 of the present invention provides a method for manufacturing aluminum alloy filaments with a wire diameter of 0.2 mm. The same parts as those in Embodiments 1 and 2 above will not be described in detail. The differences are:

[0065] Include the following steps:

[0066] a) Initial drawing: the aluminum alloy rod is drawn into an aluminum alloy wire, and the drawing speed of the drawing process is 25m / s;

[0067] b) Secondary drawing: the aluminum alloy wire obtained in step a) is drawn into an aluminum alloy wire, and the drawing speed of the drawing process is 12m / s;

[0068] c) Three-time drawing: the aluminum alloy wire obtained in step b) is drawn into aluminum alloy filaments, and the drawing speed of the drawing process is 12m / s;

[0069] d) Heat treatment process: the aluminum alloy filament obtained in step c) is subjected to a process of heating-heating-cooling, wherein,

[0070] In the above heating process, the temperature of the aluminum allo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a manufacturing method for aluminum alloy fine wires. The manufacturing method for aluminum alloy fine wires includes the following steps of (a) the first time of drawing, wherein an aluminum alloy rod is drawn into an aluminum alloy line, and the drawing speed is 10-40 m / s; (b) the second time of drawing, the aluminum alloy line obtained from the step (a) is drawn into an aluminum alloy wire, and the drawing speed is 5-30 m / s; (c) the third time of drawing, wherein the aluminum alloy wire obtained from the step (b) is drawn into an aluminum alloy fine wire, and the drawing speed is 5-30 m / s; (d) a heat treatment process, wherein the aluminum alloy fine wire obtained from the step (c) is treated according to the process of heating-heat and preservation-cooling. By means of the manufacturing method for aluminum alloy fine wires, aluminum alloy materials can be drawn into single wires with good mechanical performance and anti-fatigue performance, and the single wires meet the requirements of fifth-class / sixth-class conductors in GB / T3956 and can be used as flexible conductors.

Description

technical field [0001] The invention relates to a method for manufacturing aluminum alloy filaments. Background technique [0002] With the rapid development of my country's economy, my country has also become the world's largest wire and cable manufacturer and consumer. Aluminum is one of the conductor materials for wires and cables. However, due to the poor toughness and fit of pure aluminum conductor materials, it is difficult to draw them to very thin by traditional drawing processes. Even if they are barely drawn successfully, their mechanical properties are difficult to meet. Therefore, in the cable conductor standard GB / T3956-2008 (equivalent to the international standard IEC60228:2004), although aluminum and aluminum alloys are one of the materials that can be used as conductors, they are only used as the first type (solid conductor) and The second type (twisted circular or twisted) conductors, these two types of conductors are only used as conductors for fixed layi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01B1/02H01B13/00
Inventor 陈强
Owner TONGYONG TIANJIN ALUMINUM ALLOY PROD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap