Jade-imitated decorative plate made of phosphogypsum base material and preparation method of jade-imitated decorative plate

A phosphogypsum and decorative board technology, applied in the field of phosphogypsum base material imitation jade decorative board and its preparation, can solve the problem that the emission of phosphogypsum is difficult to be solved, and achieves the promotion of solidification performance, enhancement of freeze-thaw resistance, and improvement of performance Effect

Inactive Publication Date: 2015-06-24
GUIZHOU KAILIN GRP CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, phosphogypsum is added as raw material to make pigments; phosphogypsum is added as raw material to make paint; phosphogypsum is added to make insulation blocks, insulation bricks and other technologies; although these apply phosphogypsum to building materials The field has been generalized and mass-produced, but the annual discharge of phosphogypsum is still difficult to solve, so that a large amount of phosphogypsum is still stockpiled. Therefore, the re-application of phosphogypsum needs to continue to expand the field and expand the scope of phosphogypsum. The amount of application, thereby alleviating the defects caused by the stockpiling of phosphogypsum

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Jade-imitated decorative plate made of phosphogypsum base material and preparation method of jade-imitated decorative plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A phosphogypsum base material imitation jade decorative plate, its raw material components are 30kg of phosphogypsum, 0.1kg of quicklime, 5kg of fly ash, 2kg of ceramic fiber, and 20kg of imitation jade paint.

[0032] The imitation jade paint is composed of imitation jade primer, imitation jade top coat and varnish, which are stored separately. Among them, the imitation jade primer accounts for one-third of the imitation jade paint, the varnish is 0.2kg, and the rest is the imitation jade top coat.

[0033] The content of sodium ions in phosphogypsum is 0.1%.

[0034] The content of soluble phosphorus in phosphogypsum is 10%.

[0035] The content of sodium ion in fly ash is 0.1%.

[0036] The sulfur content in fly ash is 2%.

[0037] The length of the ceramic fiber is 0.1 mm.

[0038] The preparation method of the phosphogypsum substrate imitation jade decorative board comprises the following steps:

[0039](1) Raw material processing: put phosphogypsum in the mixi...

Embodiment 2

[0047] A phosphogypsum base material imitation jade decorative plate, its raw material components are 50kg of phosphogypsum, 1kg of quicklime, 9kg of fly ash, 3kg of ceramic fiber, and 30kg of imitation jade paint.

[0048] The imitation jade paint is composed of imitation jade primer, imitation jade top coat and varnish, which are stored separately. Among them, the imitation jade primer accounts for one-third of the imitation jade paint, the varnish is 2.7kg, and the rest is the imitation jade top coat.

[0049] The content of sodium ion in phosphogypsum is 0.01%.

[0050] The content of soluble phosphorus in phosphogypsum is 9%.

[0051] The content of sodium ion in fly ash is 0.09%.

[0052] The sulfur content in fly ash is 1%.

[0053] The length of the ceramic fiber is 0.7mm.

[0054] The preparation method of the phosphogypsum substrate imitation jade decorative board comprises the following steps:

[0055] (1) Raw material processing: put phosphogypsum in the mixing...

Embodiment 3

[0063] A phosphogypsum base material imitation jade decorative plate, its raw material components are 40kg of phosphogypsum, 0.7kg of quicklime, 7kg of fly ash, 2.5kg of ceramic fiber, and 25kg of imitation jade paint.

[0064] The imitation jade paint is composed of imitation jade primer, imitation jade top coat and varnish, which are stored separately. Among them, the imitation jade primer accounts for one-third of the imitation jade paint, 1.25kg of varnish, and the rest is imitation jade top coat.

[0065] The content of sodium ion in phosphogypsum is ≤0.07%.

[0066] The content of soluble phosphorus in phosphogypsum is 8%.

[0067] The content of sodium ion in fly ash is 0.05%.

[0068] The sulfur content in fly ash is 0.1%.

[0069] The length of the ceramic fiber is 0.5mm.

[0070] The preparation method of the phosphogypsum substrate imitation jade decorative board comprises the following steps:

[0071] (1) Raw material processing: put phosphogypsum in the mixing...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of chemical building materials and particularly relates to a jade-imitated decorative plate made of a phosphogypsum base material and a preparation method of the jade-imitated decorative plate. Phosphogypsum, quick lime, coal ash, ceramic fibers and a jade-imitated coating are reasonably proportioned and combined, and raw materials provided in the preparation method are treated, aged, ground and stirred, so that complex biochemical reaction is carried out among all the raw materials; in addition, parameters in all the process steps are controlled so that oriented biochemical reaction is carried out among all the raw materials, soluble impurities in phosphogypsum are reduced, the solidification characteristic of a phosphogypsum product is promoted, and the strength and freezing-thawing resistance of the phosphogypsum base material are improved; the coal ash and the ceramic fibers are added so that the performance of the phosphogypsum base material is improved; in addition, the combination and proportion of the raw materials are controlled, and steps in the preparation method and technical parameters in the steps are combined, so that the radioactivity, heat insulation property, freezing-thawing resistance and breaking strength of the phosphogypsum base material are improved.

Description

technical field [0001] The invention relates to the technical field of chemical building materials, in particular to a phosphogypsum base material imitation jade decorative board and a preparation method thereof. Background technique [0002] Phosphogypsum is a large amount of waste produced in wet-process phosphoric acid, and according to the increase in the output of my country's wet-process phosphoric acid production process and the gradual expansion and growth of the phosphate fertilizer industry, the stockpiling of phosphogypsum has also increased dramatically. Due to its own performance, phosphogypsum is stored and placed in the natural environment. If it is not properly treated, it will bring serious pollution to the environment; at the same time, a large amount of available resources contained in phosphogypsum will also be wasted. into the natural environment, and then bring serious economic burdens to enterprises such as phosphate fertilizer and phosphoric acid. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B41/70
Inventor 杨永彬向前勇杨步雷王伟刘小成胡新菊李泽钢
Owner GUIZHOU KAILIN GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com