A kind of resin composition, polystyrene board and preparation method thereof

A technology of resin composition and polystyrene board, which is applied in the field of thermal insulation materials, can solve the problems of poor flame retardant effect and the combustion performance can only reach B3 or B2 level, and achieve the effect of improving the combustion performance level

Active Publication Date: 2018-06-01
JIANGSU WONIUSHAN THERMAL INSULATION & WATERPROOF TEHNOLOGY
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] 1. Combustion performance depends on raw materials. Hexabromododecane is usually used as a flame retardant. Hexabromododecane can capture free radicals during combustion and stop the chain reaction from continuing. However, it is flame retardant after heating The agent participates in the reaction and is consumed, so the flame retardant effect is not good when burning continuously, and the combustion performance can only reach the B3 or B2 level. In addition, hexabromododecane is made into a flame retardant and will release toxic when used in foam insulation materials. substances, and will quickly produce toxic fumes when exposed to fire

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of resin composition, polystyrene board and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] This embodiment provides a resin composition, including: a thermosetting resin mixture and a curing agent.

[0034] Among them, the mass ratio of polystyrene particles, thermosetting resin mixture and curing agent is shown in Table 1; the subcomponents and contents of thermosetting resin mixture and curing agent themselves are shown in Table 2.

[0035] This embodiment also provides a method for preparing a polystyrene board, and the above-mentioned resin composition is processed according to the following steps:

[0036] The polystyrene particles are pre-dried and cured to obtain polystyrene cured particles, and the thermosetting resin mixture and curing agent are added under stirring to obtain precursor particles;

[0037] Drying the precursor particles twice to obtain dry particles;

[0038] The dried granules are cured and heated to form polystyrene boards.

[0039] specifically,

[0040] After the polystyrene particles are pre-dried and matured, the expansion ra...

Embodiment 2

[0047] This embodiment provides a resin composition, including: a thermosetting resin mixture and a curing agent.

[0048] Among them, the mass ratio of polystyrene particles, thermosetting resin mixture and curing agent is shown in Table 1; the subcomponents and contents of thermosetting resin mixture and curing agent themselves are shown in Table 2.

[0049] This embodiment also provides a method for preparing a polystyrene board, and the above-mentioned resin composition is processed according to the following steps:

[0050] The polystyrene particles are pre-dried and cured to obtain polystyrene cured particles, and the thermosetting resin mixture and curing agent are added under stirring to obtain precursor particles;

[0051] Drying the precursor particles twice to obtain dry particles;

[0052] The dried granules are cured and heated to form polystyrene boards.

[0053] specifically,

[0054] After the polystyrene particles are pre-dried and cured, the expansion rati...

Embodiment 3

[0061] This embodiment provides a resin composition, including: a thermosetting resin mixture and a curing agent.

[0062] Among them, the mass ratio of polystyrene particles, thermosetting resin mixture and curing agent is shown in Table 1; the subcomponents and contents of thermosetting resin mixture and curing agent themselves are shown in Table 2.

[0063] Present embodiment also provides a kind of preparation method of polystyrene board, above-mentioned resin composition is processed according to the following steps:

[0064] The polystyrene particles are pre-dried and cured to obtain polystyrene cured particles, and the thermosetting resin mixture and curing agent are added under stirring to obtain precursor particles;

[0065] Drying the precursor particles twice to obtain dry particles;

[0066] The dried granules are cured and heated to form polystyrene boards.

[0067] specifically,

[0068] After the polystyrene particles are pre-dried and matured, the expansion ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a resin composition, a polystyrene board and a preparation method thereof, which are used to solve the problems in the prior art that the expansion polystyrene board has poor combustion performance, and at the same time, the board is deformed and flows, and the fire is easy to spread. The invention provides a resin composition, a polystyrene board and a preparation method thereof. The combustion performance level of the polystyrene board is improved due to the addition of a thermosetting resin mixture and a curing agent; at the same time, the board is thermosetting, and when it burns, The volume is basically unchanged, does not flow, and self-extinguishes when it is removed from the fire.

Description

technical field [0001] The invention relates to the technical field of thermal insulation materials, in particular to a resin composition, a polystyrene board and a preparation method thereof. Background technique [0002] Expanded polystyrene board is a closed-cell polystyrene foamed plastic board made of expandable polystyrene particles after heating and pre-foaming in a mold. It is widely used in the field of building interior and exterior wall insulation. , is the most widely used thermal insulation material in China. [0003] The main raw materials of ordinary expanded polystyrene boards are polystyrene, styrene, pentane and other organic combustibles, so the combustion performance can only reach B2 level, which cannot meet the requirements of relevant standards. [0004] Expanded polystyrene board generally adopts the following process: particle pre-expansion→drying→forming→cutting→packaging. [0005] The raw material particles of expanded polystyrene board are expan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L61/10C08L61/00C08L61/28C08K13/02C08K3/38C08K5/42C08K3/22C08K3/34C08K3/04C08L25/06
Inventor 刘朋花海东王红潘倩
Owner JIANGSU WONIUSHAN THERMAL INSULATION & WATERPROOF TEHNOLOGY