Pressure sensitive adhesive and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A pressure-sensitive adhesive and solvent technology, used in adhesives, adhesive additives, adhesive types, etc., can solve problems such as poor water resistance and low temperature resistance, achieve chemical atmospheric corrosion resistance, and improve high temperature resistance. , Improve the effect of light transmittance
Inactive Publication Date: 2015-10-28
NANTONG KANGERLE MEDICAL MATERIALS CO LTD
View PDF3 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Emulsion-type polyacrylate PSA has the advantages of good environmental protection, low cost and good adhesive performance, but its water resistance and low temperature resistance are not good, and solvent-type polyacrylate PSA can make up for the disadvantages of emulsion-type PSA. insufficient
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0023] The present invention will be further described below in conjunction with embodiment:
[0024] Experimental raw materials:
[0025] 5-8 parts of butyl acrylate;
[0026] 1-2 parts of styrene;
[0027] 1-2 parts of methyl methacrylate;
[0028] 0.1-1 part of α-methacrylic acid;
[0029] Potassium persulfate 0.3-0.5 parts;
[0030] 4-15 parts of 2-butanone;
[0031] Chlorosulfonated polyethylene 1-5 parts;
[0032] Dioctyl phthalate 0.1-0.8 parts;
[0033] Preparation:
[0034] First add the above weight parts of butyl acrylate, styrene, methyl methacrylate, α-methacrylic acid, and 2-butanone into the mixing tank, and slowly heat up to 70°C-80°C while stirring; then add persulfuric acid Potassium, heat up to the reaction temperature and react for 2 hours; when the liquid in the barrel is colorless, transparent and viscous, cool down to room temperature, then add chlorosulfonated polyethylene and dioctyl phthalate to stir, mix for some time and filter out A pressu...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a pressure sensitive adhesive and a preparation method thereof. The pressure sensitive adhesive is composed of the following raw material components including, by weight, 5-8 parts of butyl acrylate, 1-2 parts of styrene, 1-2 parts of methyl methacrylate, 0.1-1 part of alpha-methacrylic acid, 0.3-0.5 part of potassium peroxodisulfate, 4-15 parts of 2-butanone, 1-5 parts of chlorosulphonated polyethylene and 0.1-0.8 part of dioctyl phthalate. The preparation method of the pressure sensitive adhesive comprises the steps that firstly, the butyl acrylate, the styrene, the methyl methacrylate, the alpha-methacrylic acid and the 2-butanone are added in a stirring barrel; secondly, the potassium peroxodisulfate is added, the temperature is increased to the reaction temperature, and reaction is performed for 2 h; thirdly, when liquid in the barrel is colorless, transparent and sticky, the liquid is cooled to the room temperature, then the chlorosulphonated polyethylene and the dioctyl phthalate are added, and after mixing is performed for several time, filtering and discharging are performed. The pressure sensitive adhesive is high in transparency and viscosity, easy to process and convenient to coat, and has the heat resistance and weather resistance; the light transmittance of light rays is improved, and the reliability of the product performance is guaranteed.
Description
technical field [0001] The invention relates to a pressure-sensitive adhesive and a preparation method thereof. Background technique [0002] Pressure-sensitive adhesive (PSA) is an adhesive that can be firmly bonded to the adherend without resorting to solvents, heat or other means, and has been widely used in printing, packaging, medical, manufacturing and Household appliances and many other fields. Acrylic pressure-sensitive adhesives are currently the fastest-growing and most promising type of pressure-sensitive adhesives, which mainly include emulsion type and solvent type. Emulsion-type polyacrylate PSA has the advantages of good environmental protection, low cost and good adhesive performance, but its water resistance and low temperature resistance are not good, and solvent-type polyacrylate PSA can make up for the disadvantages of emulsion-type PSA. insufficient. Contents of the invention [0003] The purpose of the present invention is to provide a product with...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.