Polyurethane nubuck resin for high-resilience high-velvet-feeling clothing leather and preparation method of thereof

A high-resilience, clothing leather technology, applied in textiles and papermaking, can solve the problems of insufficient cashmere feeling, poor elasticity, and limited application, and achieve the effect of strong cashmere feeling, high resilience, and fine cells

Active Publication Date: 2016-02-17
ZHEJIANG HUAFON SYNTHETIC RESIN
View PDF6 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in recent years, with the improvement of living standards, the people's demand for consumption has become higher and higher, and the domestic polyurethane nobac resin has gradually exposed the problems of poor elasticity and insufficient velvet feeling, which greatly limits its application in the field of clothing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyurethane nubuck resin for high-resilience high-velvet-feeling clothing leather and preparation method of thereof
  • Polyurethane nubuck resin for high-resilience high-velvet-feeling clothing leather and preparation method of thereof
  • Polyurethane nubuck resin for high-resilience high-velvet-feeling clothing leather and preparation method of thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027]

[0028] Add 900kg of polybutylene adipate-diethylene glycol ester diol, 64kg of 1,4-butanediol, 798.7kg of dimethylformamide and 234kg of 4,4-diphenylmethane diisocyanate into the reaction The prepolymerization reaction was carried out in the kettle, and the reaction temperature was controlled at 70°C. After 3.0 hours of reaction, when the viscosity of the reaction solution reached 60Pa·s / 70°C, 756kg of polycarbonate diol (PCD) and double-terminated hydroxyl polyether were added to modify the reaction solution. 144kg of silicone oil, 64kg of 1,4-butanediol and 6401.3kg of N,N-dimethylformamide, after 40 minutes of reaction, 336kg of 4,4-diphenylmethane diisocyanate was added for chain growth reaction, and the viscosity of the reaction liquid reached 200Pa At s / 25°C, 30kg of methanol was added for capping, and at the same time, 40kg of vehicle and 200kg of polyoxypropylene glycol (PPG) were added to obtain polyurethane nubuck resin for garment leather with high resili...

Embodiment 2

[0030]

[0031] Add 1560kg of polybutylene adipate-diethylene glycol ester diol, 76kg of ethylene glycol, 1425kg of dimethylformamide and 501.5kg of 4,4-diphenylmethane diisocyanate into the reactor for pre-treatment. Polymerization reaction, the reaction temperature is controlled at 80°C, and after 2.0 hours of reaction, when the viscosity of the reaction solution reaches 80Pa·s / 70°C by sampling, add 360kg of polycarbonate diol (PCD), 80kg of double-terminated hydroxyl polyether modified silicone oil, and Diol 114kg and N,N-dimethylformamide 5245kg, after 20 minutes of reaction, add 4,4-diphenylmethane diisocyanate 508.5kg for chain growth reaction, measure the viscosity of the reaction solution when it reaches 280Pa·s / 25℃, add methanol 10kg end-capping, add color vehicle 20kg and polyoxypropylene glycol (PPG) 100kg simultaneously, obtain the polyurethane nubuck resin for clothing leather with high resilience and high cashmere feeling.

Embodiment 3

[0033]

[0034] Add 1200kg of polybutylene adipate-diethylene glycol ester diol, 68kg of ethylene glycol, 1078.1kg of dimethylformamide and 349.2kg of 4,4-diphenylmethane diisocyanate into the reaction kettle For prepolymerization, the reaction temperature is controlled at 70°C. After 3.0 hours of reaction, when the viscosity of the reaction liquid reaches 70Pa·s / 70°C, add 720kg of polycarbonate diol (PCD), 80kg of double-terminated hydroxyl polyether modified silicone oil, 102kg of ethylene glycol and 5706.9kg of N,N-dimethylformamide, reacted for 30 minutes, then added 505.8kg of 4,4-diphenylmethane diisocyanate to carry out the chain extension reaction, when the viscosity of the reaction solution reached 240Pa·s / 25℃ Add methyl alcohol 10kg capping, add color vehicle 30kg and polyoxypropylene glycol (PPG) 150kg simultaneously, obtain the polyurethane nubuck resin for clothing leather with high resilience and high velvet feel.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a polyurethane nubuck resin for high-resilience high-velvet-feeling clothing leather and a preparation method thereof. The polyurethane nubuck resin for the high-resilience high-velvet-feeling clothing leather is prepared from, by weight, 4.0-12% of isocyanate, 16-22% of mixed polyvalent alcohol, 1.0-2.5% of chain extender, 65-80% of N,N-dimethylformamide, 0.1-0.5% of auxiliary, 1.0-2.0% of polypropylene oxide glycol (PPG) and 0.05-0.5% of methyl alcohol. The polyurethane nubuck resin for the high-resilience high-velvet-feeling clothing leather is prepared through the synthesis technology of polybutylene adipate-diethylene glycol ester diol, polycarbonate diol, silicon oil, diisocyanate, other reactants and two midbodies in an independent chain growth mode, and the prepared resin is used for polyurethane nubuck leather. The prepared nubuck leather has the advantages of being high in resilience, uniform in bubble thickness, strong in velvet feeling, good in weather resistance and the like.

Description

technical field [0001] The invention relates to polyurethane nibuck resin and a preparation method thereof. Background technique [0002] Polyurethane synthetic leather has the advantages of excellent mechanical properties, soft texture, and beautiful appearance. It has both an imitation natural leather structure and a natural leather feel. It is the best substitute for genuine leather. Wide range of applications, especially in the field of clothing. Garment leather made of polyurethane resin is very popular in the market due to its soft and delicate hand feeling, good moisture permeability and air permeability, comfortable wearing, folding resistance and wear resistance, and occupies half of the leather clothing. In particular, the garment leather made of polyurethane nubuck resin has a hand feeling unmatched by other products after being sanded. It is delicate, soft and has a strong velvet feel, so it is also deeply loved by consumers. But in recent years, with the impro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/76C08G18/66C08G18/42C08G18/44C08G18/61C08G18/32C08G18/12D06N3/14
CPCC08G18/12C08G18/4241C08G18/664C08G18/7614D06N3/146D06N3/147D06N2209/1635D06N2211/10D06N2211/28C08G18/44C08G18/3206C08G18/61
Inventor 杨信实彭峰于吉鹏郝智平张初银俞杰
Owner ZHEJIANG HUAFON SYNTHETIC RESIN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com