Special cleaner for molten iron ladle furnace liner and using method thereof

A cleaning agent and ladle technology, which is applied in the field of metallurgical auxiliary materials, can solve the problems of no ladle lining cleaning agent, etc., and achieve the effect of preventing air from entering the interior of molten iron, preventing slag accumulation, and reducing the risk of use

Active Publication Date: 2016-07-20
HENAN XIBAO METALLURGICAL MATERIALS GROUP
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of this, the purpose of the present invention is to address the deficiencies of the prior art and provide a special cleaning agent for ladle lining, which solves the problem that there is no special cleaning agent for ladle lining in the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Special cleaner for molten iron ladle furnace liner and using method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A special cleaning agent for ladle furnace lining, comprising the following raw materials in percentage by weight: 38% of premelt, 25% of sodium oxide, 20% of fluorite powder, 10% of calcite powder, and 7% of soda-lime glass.

[0026] The premelt in the special cleaning agent for ladle furnace lining is composed of the following raw materials in weight percentage: 40% of quartz, 29% of limestone, 20% of soda ash, and 11% of clay.

[0027] The chemical composition and mass percentage of the special cleaning agent for ladle furnace lining are SiO 2 25%, Al 2 o 3 2%, CaO30%, MgO3%, Na 2 O25%, F - 15%, its particle size is 18 mesh, its moisture content is 0.4%, its melting point is 780°C, and its viscosity at 1300°C is 0.03Pa·S.

[0028] In the actual production process, after injecting molten iron with a mass of 3 tons into the ladle, 60Kg of the special cleaning agent for ladle furnace lining of this embodiment is sprinkled on the surface of the molten iron. After 3 m...

Embodiment 2

[0030] A special cleaning agent for ladle furnace lining, comprising the following raw materials in percentage by weight: 40% of premelt, 23% of sodium oxide, 18% of fluorite powder, 11% of calcite powder, and 8% of soda-lime glass.

[0031] The premelt in the special cleaning agent for ladle furnace lining is composed of the following raw materials in weight percentage: 45% of quartz, 19% of limestone, 21% of soda ash, and 15% of clay.

[0032] The chemical composition and mass percentage of the special cleaning agent for ladle furnace lining are SiO 2 35%, Fe 2 o 3 2%, CaO25%, MgO1%, Na 2 O18%, F - 19%, its particle size is 80 mesh, its moisture content is 0.5%, its melting point is 800°C, and its viscosity at 1300°C is 0.05Pa·S.

[0033] In the actual production process, after injecting molten iron with a mass of 5 t into the ladle, sprinkle 125Kg of the special cleaning agent for the ladle furnace lining of this embodiment on the surface of the molten iron. After 4 min...

Embodiment 3

[0035] A special cleaning agent for ladle furnace lining, comprising the following raw materials in percentage by weight: 35% of premelt, 27% of sodium oxide, 22% of fluorite powder, 10% of calcite powder, and 6% of soda-lime glass.

[0036] The premelt in the special cleaning agent for ladle furnace lining is composed of the following raw materials in weight percentage: 50% of quartz, 20% of limestone, 20% of soda ash, and 10% of clay.

[0037] The chemical composition and mass percentage of the special cleaning agent for ladle furnace lining are SiO 2 27%, Al 2 o 3 1%, Fe 2 o 3 2%, CaO28%, Na 2 O25%, F - 17%, its particle size is 30 mesh, its moisture content is 0.3%, its melting point is 810°C, and its viscosity at 1300°C is 0.04Pa·S.

[0038] In the actual production process, after injecting molten iron with a mass of 4t into the ladle, 92Kg of the special cleaning agent for ladle furnace lining of this embodiment is sprinkled on the surface of the molten iron. After...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a special cleaner for a molten iron ladle furnace liner and a using method thereof. The cleaner comprises the following raw materials in percentage by weight: 35-40% of pre-melting materials, 23-27% of fluxing agents, 9-11% of calcite powder and 6-8% of soda-lime glass. The special cleaner for the molten iron ladle furnace liner can be used for removing slag of molten iron ladles; meanwhile, the special cleaner is high in melt performance, stable in slag removal effect, low-cost and easily available in preparation raw materials, free of other peculiar smells after put into a working furnace, environmentally-friendly in way and free of influence on the operation environment; the quality of the molten iron is improved; the high-quality raw materials are directly provided for subsequent processes; the subsequent melting processes are eliminated; the processing cost is reduced; the corresponding fees are reduced; the green production standard can be met.

Description

technical field [0001] The invention relates to the field of metallurgical auxiliary materials, in particular to a special cleaning agent for ladle furnace lining and a using method thereof. Background technique [0002] The cleaning agent is mainly used to remove impurities in molten iron in the foundry industry. It can gather insoluble matter on the surface of the molten iron solution to make it easy to remove and ensure the purity of the molten iron solution; it can also be used as a high-quality thermal insulation covering agent and slag blocking material. Excellent insulation layer and excellent slag blocking performance, and can effectively isolate the air to prevent the secondary oxidation of the iron solution. [0003] The molten iron contains a variety of harmful gases and non-metallic inclusions. On the one hand, scrap iron added, returned materials without shot blasting, oxide slag that is easy to form during smelting, and on the other hand, the stirring generated...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B22D1/00
CPCB22D1/00
Inventor 李伟锋李书成杨天奇
Owner HENAN XIBAO METALLURGICAL MATERIALS GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap