A kind of supercritical fluid injection foaming polylactic acid foam material and preparation method thereof

A technology of supercritical fluid and foam materials, which is applied in the post-treatment and modification of cellulose pulp, can solve the problems of affecting the biological characteristics of PLA materials, difficult large-scale industrial application, and reducing the degradability of materials, so as to improve the crystallization performance and Melt properties, ease of industrial production, and the effect of improving melt strength

Active Publication Date: 2021-06-29
NINGBO INST OF MATERIALS TECH & ENG CHINESE ACADEMY OF SCI
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the addition of these non-bio-based fillers will affect the biological characteristics of PLA materials and reduce the degradability of materials.
[0004] It is worth noting that the current development of PLA foam materials is still traditional chemical foaming agents and physical foaming agents such as alkanes as foaming agents. The resulting foam has large cell size and poor mechanical properties. In addition, most foaming processes use batch Foaming process is difficult to apply in large-scale industrialization

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of supercritical fluid injection foaming polylactic acid foam material and preparation method thereof
  • A kind of supercritical fluid injection foaming polylactic acid foam material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] (1) The dried cellulose pulp is put into a mixed liquor whose volume ratio of toluene, acetic acid, perchloric acid and acetic anhydride is 100:80:0.2:1, wherein the mass fraction of cellulose nanofibers is 5%, at room temperature Stir at low temperature for 1 hour to obtain modified cellulose nanofiber slurry, and then wash with ethanol and deionized water in sequence to obtain an aqueous solution of surface-modified cellulose nanofibers.

[0043] (2) PLA with a weight-average molecular weight of 400,000 is added through the main feeding port of the twin-screw extruder, and then the above-mentioned modified cellulose nanofiber aqueous solution is added by the auxiliary feeding port of the extruder, and the high-shear Shear force melt blending, while removing water vapor through the exhaust port on the extruder barrel, repeated extrusion twice, the temperature of the blending barrel for the first extrusion was 99 ° C, and the screw speed was 100 rpm; the second time Ext...

Embodiment 2

[0047] (1) Putting the dried cellulose pulp into toluene, acetic acid, perchloric acid and acetic anhydride in a volume ratio of 100:80:0.4:3, wherein the mass fraction of cellulose nanofibers is 10%, at room temperature Stir for 2 hours to obtain a modified cellulose nanofiber slurry, and then wash with ethanol and deionized water in sequence to obtain a surface-modified cellulose nanofiber aqueous solution.

[0048] (2) PLA with a weight-average molecular weight of 250,000 is added through the main feeding port of the twin-screw extruder, and then the above-mentioned modified cellulose nanofiber solution is added through the auxiliary feeding port of the extruder, and the high-shear Shear force melt blending, while removing water vapor through the exhaust port on the barrel of the extruder, repeated extrusion twice, the temperature of the blending barrel for the first extrusion was 97 ° C, and the screw speed was 130 rpm; the second time The temperature of the extrusion blen...

Embodiment 3

[0052] (1) Putting the dried cellulose pulp into toluene, acetic acid, perchloric acid and acetic anhydride in a volume ratio of 100:80:0.6:5, wherein the mass fraction of cellulose nanofibers is 20%, at room temperature Stir for 3 hours to obtain a modified cellulose nanofiber slurry, and then wash with ethanol and deionized water in sequence to obtain a surface-modified cellulose nanofiber aqueous solution.

[0053] (2) PLA with a weight-average molecular weight of 150,000 is added through the main feeding port of the twin-screw extruder, and then the above-mentioned modified cellulose nanofiber solution is added through the auxiliary feeding port of the extruder, and the high-shear Shear force melt blending, while removing water vapor through the exhaust port on the extruder barrel, repeated extrusion twice, the temperature of the blending barrel for the first extrusion was 95°C, and the screw speed was 160rpm; the second time Extrusion blending cylinder temperature is 160 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a supercritical fluid injection foamed polylactic acid foam material and a preparation method thereof. The invention uses biological filler cellulose nanofibers to modify and prepare lightweight high-strength polylactic acid foaming materials, and uses cellulose nanofibers as nucleating agents to improve the crystallization performance and melt performance of polylactic acid materials. The prepared cellulose nanofiber modified polylactic acid composite material and supercritical fluid foaming agent were mixed evenly in a microcellular foaming injection molding machine, combined with the opening and closing mold foaming device, microcellular injection foaming was performed to obtain a fully bio-based Polylactic acid foam material. The invention prepares a microporous foamed cellulose nanofiber / polylactic acid composite material with uniform cell size, high cell density and good performance, and the preparation method has high production efficiency, strong operability, stability and reliability, and is easy for industrial production and other outstanding advantages.

Description

technical field [0001] The invention relates to the technical field of polymer material processing, in particular to a supercritical fluid injection foamed polylactic acid foam material and a preparation method thereof. Background technique [0002] Polylactic acid (Polylactide, PLA) is a thermoplastic aliphatic polyester with good mechanical properties, processability, transparency and unique barrier properties. PLA is mainly obtained by ring-opening polymerization of lactide, which is derived from starch and sugars in renewable resources such as wheat, corn, grains, rice straw, etc. PLA is completely biodegradable after being used and discarded, and the final decomposition products are carbon dioxide and water. It will not cause any pollution to the environment. It is a green and environmentally friendly material that has attracted widespread attention. It is expected to replace traditional petroleum-based plastics and be widely used in various fields. In recent years, po...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J9/12C08J5/06C08L67/04C08L1/02D21H11/20
CPCC08J9/122C08J9/0061C08J5/06D21H11/20C08J2203/08C08J2203/06C08J2205/044C08J2367/04C08J2401/02B29B7/48B29B7/92B29B7/94B29B7/603B29B7/845B29B7/726B29B7/7404B29C44/3442B29C44/42B29C44/3446B29K2067/046B29K2201/00C08J2201/03C08J9/0085B32B2307/54B32B2250/40B32B2307/72B32B2266/0264B32B5/18B29B7/20B29B7/90
Inventor 汪龙郑文革任倩张利华吴明辉吴飞罗海斌
Owner NINGBO INST OF MATERIALS TECH & ENG CHINESE ACADEMY OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com