A device and energy storage technology, applied in the field of electrochemistry, can solve problems such as unfavorable mass production and complex operation of micron-scale structures, achieve low-cost, high-efficiency series-parallel connection, and meet the needs of output voltage and output current Effect

Active Publication Date: 2018-06-12
SHENZHEN GRADUATE SCHOOL TSINGHUA UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

On the one hand, the operation of the micron-scale structure is complicated; on the other hand, the conductive structure or active material structure is formed one by one, which is not conducive to mass production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of energy storage device and preparation method thereof
  • A kind of energy storage device and preparation method thereof
  • A kind of energy storage device and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0021] Such as figure 1 As shown, the preparation method of the planar energy storage device in this specific embodiment includes the following steps:

[0022] S1. Select an insulating substrate, and form a uniform conductive layer on the insulating substrate by means of magnetron sputtering, chemical plating, vacuum evaporation or coating.

[0023] In this step, the insulating base can be selected from polyethylene terephthalate (PET) film, polyethylene naphthalate (PEN) film, polyvinyl chloride film, polyimide (PI) film, ring Oxygen resin substrate, resin glass fiber board, medium temperature co-fired ceramic chip (MLCC), glass and other materials. The formation of the conductive layer can be accomplished by magnetron sputtering, vacuum evaporation, electroless plating or coating techniques.

[0024] Specifically, the insulating substrate (length 20-1000mm, width 20-500mm, thickness 3-1000μm) is cleaned with alcohol, acetone, etc., and then dried in an oven at 60°C for 2-3...

Embodiment 1

[0038] In this embodiment, the insulating substrate is made of PET film, the material of the conductive layer is made of nickel film, the active material is made of graphene, the packaging film is made of PET film, and the hot melt adhesive is made of PU.

[0039] A flexible polyethylene terephthalate (PET) film with a thickness of 6 μm is used as a substrate, and a nickel film (Ni) with a thickness of 500 nm is plated on the surface of the substrate by magnetron sputtering technology as a current collector.

[0040] Graphene oxide (GO) was prepared by the modified Hummers method as a precursor material, and GO was fully dispersed using an ultrasonic cell pulverizer (power 240W, frequency 25kHz, ultrasonic time 2h), and then the GO dispersion was mixed with absolute ethanol by Blending and stirring at a certain volume ratio for 1-2 hours. Then, use electrostatic spraying technology to fix the PET / Ni film on the working panel, control the temperature at 20-80°C, the high voltag...

Embodiment 2

[0048] In this embodiment, the insulating substrate is made of PI film, the conductive layer material is made of carbon powder material, and the active material is made of MnO 2 , the packaging film is made of ABS film, and the hot melt adhesive is made of silicone resin.

[0049] A 20 μm thick PI film was selected as the substrate, and cleaned with alcohol and acetone before use. After drying, use the coating technology to coat the conductive carbon paste (carbon powder: bisphenol A epoxy resin: curing agent: diluent mass ratio is 41:5:3:1) on the surface of the substrate, and control the coating machine Parameters: film thickness: 30μm, coating speed: 1cm / s, curing temperature: 140°C, so as to obtain a uniform conductive carbon paste current collector.

[0050] Prepare a 0.1-5M potassium permanganate solution, mix it uniformly and use it as a deposition solution, use the above-mentioned conductive layer as an anode, and a platinum electrode as a cathode, apply a DC voltage ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
widthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a power storage device and a preparation method thereof. The preparation method of the energy storage device comprises the following steps: (1) forming a uniform conducting layer on an insulating base; (2) uniformly overlaying an active substance on the conducting layer to form an active substance layer; (3) imaging the active substance layer and the conducting layer, so that the active substance layer and the conducting layer are in set shapes to obtain a plane type electrode structure; (4) coating an electrolyte on the electrode structure; and (5) packaging the electrode structure, so that the active substance layer and the conducting layer in the set shapes are covered with the electrolyte to obtain the energy storage device. The preparation method of the energy storage device disclosed by the invention is low in preparation cost and is convenient for implementation of mass production.

Description

【Technical field】 [0001] The invention relates to the field of electrochemistry, in particular to a pole piece, an energy storage device and a preparation method thereof. 【Background technique】 [0002] At present, energy storage devices, such as lithium-ion batteries and supercapacitors, have been widely used in various consumer electronics products as important energy storage tools. In recent years, with the continuous rise of wearable devices, ultra-thin, flexible, and miniaturized devices have become an important direction for the development of energy storage devices. Obviously, traditional energy storage devices can no longer meet the needs of development due to their large size and limited capacity. Therefore, seeking ultra-thin, miniaturized high-performance energy storage devices is of great significance for upgrading consumer electronics products. [0003] Recently, energy storage devices with planar structures have attracted extensive research and attention. Dif...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/04H01G11/22H01G11/86
CPCH01G11/22H01G11/86H01M4/04H01M4/0402Y02E60/10
Inventor 杨诚谢炳河赖文辉王洋
Owner SHENZHEN GRADUATE SCHOOL TSINGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap