Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

sun protection clothing

A technology of sun protection clothing and polyester fiber, which is applied in the field of cloth and can solve the problems of decreased ability to prevent ultraviolet rays and lack of sun protection effect

Active Publication Date: 2018-11-09
浙江鹏越纺织有限公司
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, on the sunscreen clothing currently available in the market, after repeated washing, its ability to prevent ultraviolet rays will be greatly reduced, and the sunscreen effect will not be achieved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • sun protection clothing
  • sun protection clothing
  • sun protection clothing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Nylon fiber: 80 parts;

[0038] Nano titanium dioxide: 20 parts;

[0039] 2,2',4,4'-Tetrahydroxybenzophenone: 2 parts;

[0040] Dibenzoylmethane: 2 parts;

[0041] 4-Nitrophthalamide: 2 parts;

[0042] Sodium alkylbenzene sulfonate: 0.7 parts;

[0043] Bisamide hydroxyethyl quaternary ammonium salt: 1 part;

[0044] Triisopropyl phosphite: 0.5 parts;

[0045] Phosphate-benzenedioctyl: 0.1 parts;

[0046] Ascorbic acid: 0.7 parts;

[0047] Sodium polynaphthalene sulfonate: 10 parts;

[0048] The fabric made of nylon fiber is subjected to anti-ultraviolet finishing, and 2,2',4,4'-tetrahydroxybenzophenone, dibenzoylmethane, and 4-nitrophthalamide are added to the finishing solution , 4-aminobenzophenone, 2-hydroxy-5-methylbenzophenone, mexicanone, two dipping and two rolling, the liquid rolling rate is 30%-45%, and then dried at 90°C , and then carry out the finishing work. In the finishing process, add softener, antioxidant, synergist, and dispersant to the finis...

Embodiment 2

[0050] Nylon fiber: 100 parts;

[0051] Nano titanium dioxide: 10 parts;

[0052] 2,2',4,4'-Tetrahydroxybenzophenone: 1 part;

[0053] Dibenzoylmethane: 3 parts;

[0054] 4-Nitrophthalamide: 4 parts;

[0055] Sodium alkylbenzene sulfonate: 0.5 parts;

[0056] Bisamide hydroxyethyl quaternary ammonium salt: 0.5 parts;

[0057] Triisopropyl phosphite: 1 part;

[0058] Phosphate-benzenedioctyl ester: 0.5 parts;

[0059] Ascorbic acid: 0.5 parts;

[0060] Sodium polynaphthalene sulfonate: 7 parts.

[0061] The fabric made of nylon fiber is subjected to anti-ultraviolet finishing, and 2,2',4,4'-tetrahydroxybenzophenone, dibenzoylmethane, and 4-nitrophthalamide are added to the finishing solution , 4-aminobenzophenone, 2-hydroxy-5-methylbenzophenone, mexicanone, two dipping and two rolling, the liquid rolling rate is 30%-45%, and then dried at 90°C , and then carry out the finishing work. In the finishing process, add softener, antioxidant, synergist, and dispersant to the ...

Embodiment 3

[0063] Nylon fiber: 120 parts;

[0064] Nano titanium dioxide: 30 parts;

[0065] 2,2',4,4'-Tetrahydroxybenzophenone: 0.5 parts;

[0066] Dibenzoylmethane: 1 part;

[0067] 4-Nitrophthalamide: 5 parts;

[0068] Sodium alkylbenzene sulfonate: 1 part;

[0069] Bisamide hydroxyethyl quaternary ammonium salt: 0.1 parts;

[0070] Triisopropyl phosphite: 0.1 part;

[0071] Dioctyl phosphate: 1 part;

[0072] Ascorbic acid: 1 part;

[0073] Sodium polynaphthalene sulfonate: 5 parts;

[0074] The fabric made of nylon fiber is subjected to anti-ultraviolet finishing, and 2,2',4,4'-tetrahydroxybenzophenone, dibenzoylmethane, and 4-nitrophthalamide are added to the finishing solution , 4-aminobenzophenone, 2-hydroxy-5-methylbenzophenone, mexicanone, two dipping and two rolling, the liquid rolling rate is 30%-45%, and then dried at 90°C , and then carry out the finishing work. In the finishing process, add softener, antioxidant, synergist, and dispersant to the finishing solution...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses sun-resistant clothes. The sun-resistant clothes are made of sun-resistant nylon fibers. The sun-resistant nylon fibers are prepared from, by weight, 80-120 parts of polyester fibers, 10-30 parts of nano-titanium dioxide, 0.5-2 parts of 2,2',4,4'-tetrehydroxybenzophenone, 1-3 parts of dibenzoyl methane, 2-5 parts of 4-nitrophthalimide, 0.6-2 parts of softening agent and 0.2-1 part of antioxidant. The produced sun-resistant clothes have a good anti-ultraviolet function and still have the good anti-ultraviolet function after being washed multiple times.

Description

technical field [0001] The present invention relates to a kind of cloth, more specifically relates to a kind of sun protection clothes. Background technique [0002] Sunscreen clothing first became popular in the United States in 2007, and then entered China. At the beginning, it was mostly used in outdoor products, and the application in ordinary clothing was still relatively small, and it was favored by many girls afterwards. [0003] The main function of sun protection clothing is to block the direct radiation of the sun's ultraviolet rays, which is the same as that of parasols. [0004] In the prior art, there are two main aspects of the sun-protecting substances in the sun-proof clothing, one is by enhancing the fabric's ability to absorb ultraviolet rays, and the other is by enhancing the fabric's ability to reflect ultraviolet rays. [0005] However, on the sunscreen clothing currently available in the market, after repeated washing, its ability to prevent ultraviol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M11/46D06M13/152D06M13/123D06M13/256D06M13/292D06M15/39D06M13/335D06M13/11D06M13/46A41D13/00A41D1/02A41D31/00D06M101/34D06M101/32
CPCA41D1/02A41D13/00A41D31/00A41D2400/26A41D2500/50D06M11/46D06M13/11D06M13/123D06M13/152D06M13/256D06M13/292D06M13/335D06M13/461D06M15/39D06M2101/32D06M2101/34D06M2200/25D06M2200/50
Inventor 伍硕硕
Owner 浙江鹏越纺织有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com