Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A floor paint and polyurethane technology, applied in the field of floor paint, can solve the problems of high substrate humidity and environmental humidity, low paint film compactness, small market share, etc., and achieve complete environmental protection, high brightness, The effect of avoiding harm to human health
Inactive Publication Date: 2016-12-07
张海棠
View PDF2 Cites 5 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
At present, floor paint is divided into solvent-based and solvent-free. Solvent-based floor paint has high requirements for substrate humidity and environmental humidity during construction; solvent-free water-based floor does not have much requirements for substrate and environmental humidity. Because of its non-flammable and
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Example Embodiment
[0010] Example 1
[0011] The polyurethane fireproof floor paint of this embodiment contains the following components by weight: 78 parts of water-based polyurethane resin, 20 parts of melamine formaldehyde resin, 15 parts of polyvinyl acetate emulsion, 16 parts of paraffin emulsion, 3 parts of alkylbenzene sulfonate, 6 parts of vinyl trimethoxysilane, 11 parts of hydroxyethyl cellulose, 3 parts of dinonyl naphthalene sulfonic acid, 1 part of butyl titanate, 4 parts of citric acid, 3 parts of zinc naphthenate, 2 parts of sodium borate, 5 parts of polyurethane curing agent and 10 parts of polyurethane dispersant.
Example Embodiment
[0012] Example 2
[0013] The polyurethane fireproof floor paint of this embodiment comprises the following components by weight: 86 parts of water-based polyurethane resin, 24 parts of melamine formaldehyde resin, 25 parts of polyvinyl acetate emulsion, 18 parts of paraffin emulsion, 7 parts of alkylbenzene sulfonate, 8 parts of vinyl trimethoxysilane, 14 parts of hydroxyethyl cellulose, 7 parts of dinonylnaphthalene sulfonic acid, 4 parts of butyl titanate, 7 parts of citric acid, 7 parts of zinc naphthenate, 4 parts of sodium borate, 12 parts of polyurethane curing agent, 15 parts of polyurethane dispersant, 15 parts of polyvinyl acetate.
Example Embodiment
[0014] Example 3
[0015] The polyurethane fireproof floor paint of this embodiment contains the following components by weight: 78 parts of water-based polyurethane resin, 20 parts of melamine formaldehyde resin, 15 parts of polyvinyl acetate emulsion, 16 parts of paraffin emulsion, 3 parts of alkylbenzene sulfonate, 6 parts of vinyl trimethoxysilane, 11 parts of hydroxyethyl cellulose, 3 parts of dinonyl naphthalene sulfonic acid, 1 part of butyl titanate, 4 parts of citric acid, 3 parts of zinc naphthenate, 2 parts of sodium borate, 5 parts of polyurethane curing agent, 10 parts of polyurethane type dispersant, 9 parts of polyvinyl acetate, 10 parts of liquid rosin resin.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses fireproof polyurethane floor coating. The floor coating comprises the following components in parts by weight: 78 to 86 parts of waterborne polyurethane resin, 20 to 24 parts of melamine formaldehyde resin, 15 to 25 parts of polyvinyl acetate emulsion, 16 to 18 parts of paraffin emulsion, 3 to 7 parts of alkylbenzene sulfonate, 6 to 8 parts of vinyl trimethoxysilane, 11 to 14 parts of hydroxyethyl cellulose, 3 to 7 parts of dinonylnaphthalene sulfonic acid, 1 to 4 parts of butyl titanate, 4 to 7 parts of citric acid, 3 to 7 parts of zinc naphthenate, 2 to 4 parts of sodium borate, 5 to 12 parts of a polyurethane curing agent and 10 to 15 parts of a polyurethane dispersant. The fireproof polyurethane floor coating disclosed by the invention is free of solvents, non-toxic and harmless, and environment-friendly to avoid harm of the organic solvents on health of a human body, and can realize completely environment-friendly construction and application. Furthermore, the fireproof polyurethane floor coating has the characteristics of better water resistance and fire resistance, high tinting strength and yellowing resistance, and further is higher in layer surface brightness, brighter in color and luster and more excellent in physical properties.
Description
technical field [0001] The invention relates to a floor paint, in particular to a polyurethane fireproof floor paint. Background technique [0002] Floor paint was first invented by Germany in 1934. It is mainly made of oil, tree materials, colors, solvents, etc. It is mainly divided into decorative floor paint, heavy-duty anti-corrosion floor paint, and heavy-duty floor paint. Floor paint is made up of many different substances through many production processes such as mixing, dissolving, and dispersing. Floor paint has the characteristics of bright, real, beautiful, wear-resistant, waterproof, and anti-corrosion. Floor paint is made up of many different substances through many production processes such as mixing, dissolving, and dispersing. According to the different functions of each component of floor paint, it can generally be divided into main film-forming substances, secondary film-forming substances and auxiliary film-forming substances. Since the middle and late ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more