A kind of composite multifunctional two-component water-based wood white finish paint and preparation method thereof

A two-component, multi-functional technology, used in biocide-containing paints, antifouling/underwater coatings, coatings, etc., to solve the problems of no stain resistance, mildew resistance, formaldehyde removal, high cost, and not very ideal.

Active Publication Date: 2018-07-06
广东伊思曼新材料科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, there are also many patents or documents disclosing some two-component water-based wood coatings and their production methods, but the coating effects in these patents mostly only meet some basic physical performance indicators of environmental performance and paint film, and other special The additional functions are not very ideal, and the cost is high. In addition, most of these coatings do not have the characteristics of stain resistance and additional composite functions such as anti-mold and formaldehyde removal at the same time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of composite multifunctional two-component water-based wood white finish paint and preparation method thereof
  • A kind of composite multifunctional two-component water-based wood white finish paint and preparation method thereof
  • A kind of composite multifunctional two-component water-based wood white finish paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0080] The composite multifunctional two-component water-based woodware white topcoat provided in this example includes component A, component B and water, and the mass ratio of component A, component B and water is 100:20:20. The formula can be prepared as follows (mass percentage):

[0081] A component:

[0082] Waterborne Hydroxy Acrylic Resin 30%

[0083] Compound modified self-crosslinking acrylic polymer 30%

[0084] Water-based titanium dioxide paste 25%

[0085] Water-based matting agent 3%

[0086] Defoamer 0.5%

[0087] Wetting agent 0.3%

[0088] Thickener 0.5%

[0089] Dispersant 0.5%

[0090] Leveling agent 0.2%

[0091] Mildew and fungicide 3%

[0092] water 7%,

[0093] The sum of the mass percentages of the raw materials in component A is 100%;

[0094] Part B

[0095] Hydrophilic aliphatic polyisocyanate 75%,

[0096] Propylene Glycol Methyl Ether Acetate (PMA) 25%

[0097] The sum of the mass percentages of each raw material is 100%;

[0098] T...

Embodiment 2

[0124] The composite multi-functional two-component water-based wood white finish provided in this example includes component A, component B and water, and the mass ratio of component A, component B and water is 100:22:15. The formula can be prepared as follows (mass percentage):

[0125] A component:

[0126] Waterborne Hydroxy Acrylic Resin 35%

[0127] Compound modified self-crosslinking acrylic polymer 25%

[0128] Water-based titanium dioxide paste 28%

[0129] Aqueous matting agent 2.5%

[0130] Defoamer 0.4%

[0131] Wetting agent 0.4%

[0132] Thickener 0.7%

[0133] Dispersant 0.5%

[0134] Leveling agent 0.3%

[0135] Anti-mold fungicides 2.5%

[0136] Water 4.7%,

[0137] The sum of the mass percentages of the raw materials in component A is 100%;

[0138] Part B

[0139] Hydrophilic aliphatic polyisocyanate 73%,

[0140] Propylene Glycol Methyl Ether Acetate (PMA) 27%

[0141] The sum of the mass percentages of the raw materials in component B is 100%...

Embodiment 3

[0153] The composite multi-functional two-component water-based wood white topcoat provided in this example includes component A, component B and water, and the mass ratio of component A, component B and water is 100:25:10. The formula can be prepared as follows (mass percentage):

[0154] A component:

[0155] Waterborne Hydroxy Acrylic Resin 40%

[0156] Compound modified self-crosslinking acrylic polymer 20%

[0157] Water-based titanium dioxide paste 25%

[0158] Water-based matting agent 2%

[0159] Defoamer 0.3%

[0160] Wetting agent 0.3%

[0161] Thickener 0.5%

[0162] Dispersant 0.5%

[0163] Leveling agent 0.2%

[0164] Anti-mildew fungicide 2%

[0165] Water 9.2%,

[0166] The sum of the mass percentages of the raw materials in component A is 100%;

[0167] B component;

[0168] Hydrophilic aliphatic polyisocyanate 70%,

[0169] Propylene Glycol Methyl Ether Acetate (PMA) 30%

[0170] The sum of the mass percentages of the raw materials in component B i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a composite multi-functional two-component aqueous wood white top coat, which comprises a component A, a component B and water according to a mass part ratio of 100:20-25:10-20, wherein the component A is prepared from the following raw materials by mass: an aqueous hydroxy acrylic acid resin, a compound modified self-cross-linking acrylic acid polymer, an aqueous titanium white slurry, an aqueous matting agent, a defoamer, a wetting agent, a thickening agent, a dispersant, a leveling agent, an anti-mildew bactericidal agent, and the balance of water, and the component B is prepared from the following raw materials by mass: hydrophilic aliphatic polyisocyanate and propylene glycol methyl ether acetic acid ester. The composite multi-functional two-component aqueous wood white top coat of the present invention has advantages of good antibacterial effect, good aldehyde removing effect, good stain resistance, environmental protection, good hardness, high fullness, and moderate cost.

Description

technical field [0001] The invention belongs to the technical field of two-component waterborne woodware coatings, in particular to a composite multifunctional two-component waterborne woodware white topcoat and a preparation method thereof. Background technique [0002] As a decorative material, wood coatings have higher and higher decorative requirements and environmental protection performance. As wood decorative materials, traditional two-component solvent-based PU wood coatings have mature product formulations and processes, and product performance can also be satisfied. The higher demand is mainly manifested in good fullness, high hardness, up to 2H-3H, good high temperature and alcohol resistance, and not easy to tarnish, but because it contains a large amount of volatile organic compounds (VOC), it is harmful to air pollution and The health of construction workers will bring certain harm, and it is more and more obvious that they are restricted by relevant national e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/04C09D5/14C09D5/16C09D7/61
CPCC08K2201/014C08L2205/035C09D5/14C09D5/1662C09D5/1687C09D175/04C08L91/06C08K13/02C08K2003/2241C08K3/36C08K5/101
Inventor 丘子范冯星俊刘光勇
Owner 广东伊思曼新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com