Composite multi-functional two-component aqueous wood white top coat and preparation method thereof

A two-component, multi-functional technology that is used in biocide-containing paints, antifouling/underwater coatings, coatings, etc. In addition to formaldehyde, stain resistance and other issues

Active Publication Date: 2016-12-21
广东伊思曼新材料科技有限公司
View PDF3 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, there are also many patents or documents disclosing some two-component water-based wood coatings and their production methods, but the coating effects in these patents mostly only meet some basic physical performance indicators of environmental performance and paint film, and other special The additional functions are not very ideal, and the cost is high. In addition, most of these coatings do not have the characteristics of stain resistance and additional composite functions such as anti-mold and formaldehyde removal at the same time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite multi-functional two-component aqueous wood white top coat and preparation method thereof
  • Composite multi-functional two-component aqueous wood white top coat and preparation method thereof
  • Composite multi-functional two-component aqueous wood white top coat and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0080] The composite multi-functional two-component water-based wood white finish provided by this embodiment includes component A, component B and water, and the mass ratio of component A, component B and water is 100:20:20, specifically Formula can be formulated as follows (mass percentage composition):

[0081] A component:

[0082] Waterborne Hydroxy Acrylic Resin 30%

[0083] Composite modified self-crosslinking acrylic polymer 30%

[0084] Water-based titanium dioxide paste 25%

[0085] Water-based matting agent 3%

[0086] Defoamer 0.5%

[0087] Wetting agent 0.3%

[0088] Thickener 0.5%

[0089] Dispersant 0.5%

[0090] Leveling agent 0.2%

[0091] Anti-mildew fungicide 3%

[0092] water 7%,

[0093] The sum of the mass percentages of each raw material in Group A is 100%;

[0094] Component B

[0095] Hydrophilic aliphatic polyisocyanate 75%,

[0096] Propylene glycol methyl ether acetate (PMA) 25%

[0097] The sum of the mass percentages of each raw mate...

Embodiment 2

[0124] The composite multi-functional two-component water-based wood white finish provided by this embodiment includes component A, component B and water, and the mass ratio of component A, component B and water is 100:22:15, specifically Formula can be formulated as follows (mass percentage composition):

[0125] A component:

[0126] Waterborne Hydroxy Acrylic Resin 35%

[0127] Composite modified self-crosslinking acrylic polymer 25%

[0128] Water-based titanium dioxide 28%

[0129] Water-based matting agent 2.5%

[0130] Defoamer 0.4%

[0131] Wetting agent 0.4%

[0132] Thickener 0.7%

[0133] Dispersant 0.5%

[0134] Leveling agent 0.3%

[0135] Anti-mildew fungicide 2.5%

[0136] Water 4.7%,

[0137] The sum of the mass percentages of each raw material in Group A is 100%;

[0138] Component B

[0139] Hydrophilic aliphatic polyisocyanate 73%,

[0140] Propylene glycol methyl ether acetate (PMA) 27%

[0141] The sum of the mass percentages of each raw mate...

Embodiment 3

[0153] The composite multi-functional two-component water-based wood white finish provided in this embodiment includes component A, component B and water, and the mass ratio of component A, component B and water is 100:25:10, specifically Formula can be formulated as follows (mass percentage composition):

[0154] A component:

[0155] Waterborne Hydroxy Acrylic Resin 40%

[0156] Composite modified self-crosslinking acrylic polymer 20%

[0157] Water-based titanium dioxide paste 25%

[0158] Water-based matting agent 2%

[0159] Defoamer 0.3%

[0160] Wetting agent 0.3%

[0161] Thickener 0.5%

[0162] Dispersant 0.5%

[0163] Leveling agent 0.2%

[0164] Anti-mildew fungicide 2%

[0165] Water 9.2%,

[0166] The sum of the mass percentages of each raw material in Group A is 100%;

[0167] B component;

[0168] Hydrophilic aliphatic polyisocyanate 70%,

[0169] Propylene glycol methyl ether acetate (PMA) 30%

[0170] The sum of the mass percentages of each raw mat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a composite multi-functional two-component aqueous wood white top coat, which comprises a component A, a component B and water according to a mass part ratio of 100:20-25:10-20, wherein the component A is prepared from the following raw materials by mass: an aqueous hydroxy acrylic acid resin, a compound modified self-cross-linking acrylic acid polymer, an aqueous titanium white slurry, an aqueous matting agent, a defoamer, a wetting agent, a thickening agent, a dispersant, a leveling agent, an anti-mildew bactericidal agent, and the balance of water, and the component B is prepared from the following raw materials by mass: hydrophilic aliphatic polyisocyanate and propylene glycol methyl ether acetic acid ester. The composite multi-functional two-component aqueous wood white top coat of the present invention has advantages of good antibacterial effect, good aldehyde removing effect, good stain resistance, environmental protection, good hardness, high fullness, and moderate cost.

Description

technical field [0001] The invention belongs to the technical field of two-component water-based woodware coatings, and in particular relates to a composite multifunctional two-component water-based woodware white finish and a preparation method thereof. Background technique [0002] As a decorative material, wood coatings have higher and higher decorative requirements and environmental protection performance. As wood decoration materials, the traditional two-component solvent-based PU wood coatings have mature product formulas and processes, and the product performance can also meet The higher demand is mainly manifested in good fullness, high hardness, which can reach 2H-3H, high temperature resistance and alcohol resistance, and is not easy to tarnish, but because it contains a large amount of volatile organic compounds (VOC), it is harmful to air pollution and The health of construction workers will bring certain hazards, which are increasingly restricted by the relevant...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D5/14C09D5/16C09D7/12
CPCC08K2201/014C08L2205/035C09D5/14C09D5/1662C09D5/1687C09D175/04C08L91/06C08K13/02C08K2003/2241C08K3/36C08K5/101
Inventor 丘子范冯星俊刘光勇
Owner 广东伊思曼新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap