Multifunctional mosquito-proof PVC (polyvinyl chloride) material

A PVC material and multi-functional technology, applied in the field of polymer materials, can solve the problem of no mosquito repellent effect and achieve good mosquito repellent effect

Active Publication Date: 2017-01-04
ZHEJIANG WANG YANG POLYMER MATERIALS
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But in many fields, silica gel is not suitable, but there is no PVC material with mosquito repellent effect in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multifunctional mosquito-proof PVC (polyvinyl chloride) material
  • Multifunctional mosquito-proof PVC (polyvinyl chloride) material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] Comprising the following parts by weight:

[0057] 100 parts of PVC crosslinking resin;

[0058] Calcium zinc stabilizer: 3 parts;

[0059] Stearoylbenzoylmethane: 1.5 parts;

[0060] Polyethylene wax: 0.7 parts;

[0061] Ethyl acetoacetate diisopropyl aluminate: 10 parts;

[0062] Mosquito repellent microcapsules: 1 serving;

[0063] 3-(2-aminoethylamine)propylmethyldimethoxysilane: 3 parts;

[0064] Zeolite Silver: 2 parts.

[0065] The mosquito repellent microcapsules comprise the following components in parts by weight:

[0066] 10 parts of deltamethrin and 50 parts of carrier,

[0067]The carrier comprises the following components by weight:

[0068] Hydroxypropyl glycerol distarch: 30 parts;

[0069] Hydroxypropyl-BETA-cyclodextrin: 15 parts;

[0070] BETA-cyclodextrin: 10 parts;

[0071] 2-hydroxyethyl ether: 3 parts;

[0072] Chitosan: 5 parts.

[0073] The preparation method of described mosquito repellent microcapsule is:

[0074] The carrier and...

Embodiment 2

[0076] Comprising the following parts by weight:

[0077] 125 parts of PVC crosslinking resin;

[0078] Calcium zinc stabilizer: 4 parts;

[0079] Stearoylbenzoylmethane: 2 parts;

[0080] Polyethylene wax: 0.4 parts;

[0081] Ethyl acetoacetate diisopropyl aluminate: 5 parts;

[0082] Mosquito repellent microcapsules: 3 servings;

[0083] 3-(2-aminoethylamine)propylmethyldimethoxysilane: 5 parts;

[0084] Zeolite Silver: 2 parts.

[0085] The mosquito repellent microcapsules comprise the following components in parts by weight:

[0086] 10 parts of cyhalothrin and 50 parts of carrier,

[0087] The carrier comprises the following components by weight:

[0088] Hydroxypropyl glycerol distarch: 30 parts;

[0089] Hydroxypropyl-BETA-cyclodextrin: 15 parts;

[0090] BETA-cyclodextrin: 10 parts;

[0091] 2-hydroxyethyl ether: 3 parts;

[0092] Chitosan: 5 parts.

[0093] The preparation method of described mosquito repellent microcapsule is:

[0094] The carrier and t...

Embodiment 3

[0096] Comprising the following parts by weight:

[0097] 150 parts of PVC crosslinking resin;

[0098] Calcium zinc stabilizer: 2 parts;

[0099] Stearoylbenzoylmethane: 1 part;

[0100] Polyethylene wax: 0.1 parts;

[0101] Ethyl acetoacetate diisopropyl aluminate: 15 parts;

[0102] Mosquito repellent microcapsules: 1 serving;

[0103] 3-(2-aminoethylamine)propylmethyldimethoxysilane: 5 parts;

[0104] Zeolite Silver: 2 parts.

[0105] The mosquito repellent microcapsules comprise the following components in parts by weight:

[0106] 10 parts of mosquito repellent and 50 parts of carrier,

[0107] The mosquito repellent is composed of peppermint essential oil, orange peel oil and sandalwood oil in a mass ratio of 1:1:1;

[0108] The carrier comprises the following components by weight:

[0109] Hydroxypropyl glycerol distarch: 30 parts;

[0110] Hydroxypropyl-BETA-cyclodextrin: 15 parts;

[0111] BETA-cyclodextrin: 10 parts;

[0112] 2-hydroxyethyl ether: 3 part...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a multifunctional mosquito-proof PVC (polyvinyl chloride) material, which is prepared from the following materials in parts by weight: 100 to 150 parts of PVC crosslinking resin, 3 to 6 parts of stabilizing agents, 0.1 to 0.7 part of lubricating agents, 0.5 to 1.5 part of chelating agents, 5 to 15 parts of plasticizers, 1 to 5 parts of mosquito repellent micro capsules, 1 to 5 parts of coupling agents, 1 to 5 parts of modification agents and 1 to 5 parts of silver zeolite. The prepared PVC material has better mosquito-proof effects.

Description

technical field [0001] The invention relates to a polymer material, and more specifically relates to a multifunctional anti-mosquito PVC material. Background technique [0002] Polyvinyl chloride, referred to as PVC (Polyvinyl chloride), is a vinyl chloride monomer (vinyl chloridemonomer, referred to as VCM) in peroxides, azo compounds and other initiators; or under the action of light and heat, it can be polymerized according to the mechanism of free radical polymerization. made polymer. Vinyl chloride homopolymers and vinyl chloride copolymers are collectively referred to as vinyl chloride resins. [0003] PVC is a white powder with an amorphous structure, a small degree of branching, a relative density of about 1.4, a glass transition temperature of 77-90°C, and begins to decompose at about 170°C [1], and has poor stability to light and heat. After long-term sunlight exposure, it will decompose to produce hydrogen chloride, and further autocatalyze the decomposition, ca...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L23/06C08K13/06C08K9/12C08K5/00C08K3/34C08K5/544
CPCC08L27/06C08L23/06C08K13/06C08K9/12C08K5/0058C08K3/34C08K5/544
Inventor 汪徳柱汪徳兴
Owner ZHEJIANG WANG YANG POLYMER MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap