A kind of control method of high temperature thermoelectric sr3co4o9 thin film resistivity

A thin film resistance and thermoelectric technology, which is applied in the manufacture/processing of thermoelectric devices, vacuum evaporation coating, coating, etc., can solve the problems of high cost and complicated single crystal preparation process, and achieve the effect of continuous control

Active Publication Date: 2018-11-09
KUNMING UNIV OF SCI & TECH
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Currently for material transport anisotropy, such as resistivity anisotropy ρ c / ρ ab And thermoelectric potential anisotropy ΔS=S ab -S c , which is mainly obtained by direct measurement in single crystal materials, but the single crystal preparation process is complicated and expensive; obtaining the transport anisotropy of materials through a simpler method has important research significance for in-depth exploration of the relationship between material structure and performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of control method of high temperature thermoelectric sr3co4o9 thin film resistivity

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Pretreatment of c-axis tilted single crystal substrates: SrTiO with 0° tilt 3 (100) The single crystal substrate is annealed at 1000°C in the air atmosphere for 1 hour, and then treated with acetone, alcohol and deionized water in an ultrasonic cleaner at room temperature for 2 minutes each, and then annealed at 1000°C in the air atmosphere. 1h to obtain a single TiO 2 Termination layer, single crystal substrate with atomically smooth surface.

[0016] Epitaxial thin film growth: using pulsed laser deposition technology with KrF excimer laser with a wavelength of 248nm and a pulse width of 28ns as the light source, with a laser energy of 175mJ, a laser frequency of 3Hz, and a background vacuum of 1×10 -3 Pa, the substrate temperature is 780°C, and the flowing oxygen pressure is 30Pa as the growth process, and the pretreated SrTiO 3 Sr Growth on (001) Single Crystal Substrate 3 co 4 o 9 film, after which at 780°C and 1×10 4 In situ annealing under Pa static oxyge...

Embodiment 2

[0019] Pretreatment of c-axis tilted single crystal substrates: SrTiO with 5° tilt 3 (100) The single crystal substrate is annealed at 1000°C in the air atmosphere for 1 hour, and then treated with acetone, alcohol and deionized water in an ultrasonic cleaner at room temperature for 2 minutes each, and then annealed at 1000°C in the air atmosphere. 1h to obtain a single TiO 2 Termination layer, single crystal substrate with atomically smooth steps.

[0020] Epitaxial thin film growth: using pulsed laser deposition technology with KrF excimer laser with a wavelength of 248nm and a pulse width of 28ns as the light source, with a laser energy of 175mJ, a laser frequency of 3Hz, and a background vacuum of 1×10 -3 Pa, the substrate temperature is 780°C, and the flowing oxygen pressure is 30Pa as the growth process, and the pretreated SrTiO 3 Sr Growth on (001) Single Crystal Substrate 3 co 4 o 9 film, after which at 780°C and 1×10 4 In situ annealing under Pa static oxygen ...

Embodiment 3

[0023] Pretreatment of c-axis tilted single crystal substrates: SrTiO with 10° tilt 3 (100) The single crystal substrate is annealed at 1000°C in the air atmosphere for 1 hour, and then treated with acetone, alcohol and deionized water in an ultrasonic cleaner at room temperature for 2 minutes each, and then annealed at 1000°C in the air atmosphere. 1h to obtain a single TiO 2 Termination layer, single crystal substrate with atomically smooth steps.

[0024] Epitaxial thin film growth: using pulsed laser deposition technology with KrF excimer laser with a wavelength of 248nm and a pulse width of 28ns as the light source, with a laser energy of 175mJ, a laser frequency of 3Hz, and a background vacuum of 1×10 -3 Pa, the substrate temperature is 780°C, and the flowing oxygen pressure is 30Pa as the growth process, and the pretreated SrTiO 3 Sr Growth on (001) Single Crystal Substrate 3 co 4 o 9 film, after which at 780°C and 1×10 4 In situ annealing under Pa static oxygen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
angleaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for regulating and controlling the resistivity of a high-temperature thermoelectric Sr3Co4O9 film, which belongs to the field of functional film materials. The method of the present invention grows Sr3Co4O9 thin films epitaxially along the c-axis on single-crystal substrates inclined at different angles by pulsed laser deposition, and adjusts the resistivity of the epitaxial film along the inclined direction through the c-axis inclination angle of the single-crystal substrate. This method can reflect the electrical transport anisotropy of layered cobalt-based oxide materials.

Description

technical field [0001] The invention provides a high temperature thermoelectric Sr 3 co 4 o 9 The invention relates to a method for regulating and controlling the resistivity of a thin film, belonging to the field of functional thin film materials. Background technique [0002] Split layer structure Sr 3 co 4 o 9 Conducted by CoO 2 layer and insulating Sr 2 CoO 3 The layers are stacked alternately along the c-axis and mismatched along the b-axis, where CoO 2 Low-spin Co in the layer 4+ ( ) provides hole carriers, and strongly localizes thermal and electrical transport to ab In-plane, Sr 2 CoO 3 The layer acts as a phonon scattering center to effectively reduce the thermal conductivity of the material. It is not only an "electronic crystal-phonon glass" material with high electrical conductivity and low thermal conductivity, but also has significant structural and transport anisotropy. , The field of thermoelectric conversion has great application potential. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityPatents(China)
IPC IPC(8): C23C14/28C23C14/08C23C14/58H01L35/34H10N10/01
CPCC23C14/08C23C14/28C23C14/5806H10N10/01
Inventor宋世金虞澜傅佳倪佳邱兴煌陈琪钟毅
OwnerKUNMING UNIV OF SCI & TECH