A kind of stone powder curing agent and preparation method thereof

A technology of curing agent and stone powder, which is applied in the field of stone powder curing agent and its preparation, can solve the problems of limited application, low unconfined compressive strength of cement soil, etc., achieve good curing performance, reduce construction cost, good compressive performance and The effect of flexural properties

Inactive Publication Date: 2018-10-23
福建港湾新材料有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the unconfined compressive strength of the obtained cement-soil is not high when only cement is used as the curing agent of stone powder, which limits its application in construction.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of stone powder curing agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A kind of stone powder solidifying agent, its raw materials include: 5 parts of gypsum, 15 parts of 425 grade ordinary portland cement, 29 parts of quicklime, 9 parts of limestone, 30 parts of granulated blast furnace slag powder, hydroxyethyl methyl 1.5 parts of base cellulose ether, 6 parts of cast stone powder, 6 parts of ceramic micropowder, 10 parts of furfural slag and 4 parts of medical stone.

[0017] The preparation method of the above-mentioned stone powder curing agent is: after mixing and grinding the raw materials of the curing agent, the curing agent has a specific surface area of ​​450m 2 / kg powder.

Embodiment 2

[0019] A stone powder solidifying agent, the raw materials of which include 6 parts of gypsum, 18 parts of 425 grade ordinary Portland cement, 30 parts of quicklime, 10 parts of limestone, 35 parts of granulated blast furnace slag powder, hydroxyethyl methyl 2 parts of base cellulose ether, 8 parts of cast stone powder, 7 parts of ceramic micropowder, 15 parts of furfural slag and 6 parts of medical stone.

[0020] The preparation method of the above-mentioned stone powder curing agent is: after mixing and grinding the raw materials of the curing agent, the curing agent has a specific surface area of ​​650m 2 / kg powder.

Embodiment 3

[0022] A kind of stone powder solidifying agent, its raw material comprises by weight parts: 4 parts of gypsum, 16 parts of 425 grade ordinary portland cement, 28 parts of quicklime, 8 parts of limestone, 33 parts of granulated blast furnace slag powder, hydroxyethyl methyl 1 part of base cellulose ether, 7 parts of cast stone powder, 8 parts of ceramic micropowder, 12 parts of furfural slag and 5 parts of medical stone.

[0023] The preparation method of the above-mentioned stone powder curing agent is: after mixing and grinding the raw materials of the curing agent, the curing agent has a specific surface area of ​​550m 2 / kg powder.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a mountain flour curing agent. The mountain flour curing agent is prepared from the following raw materials in parts by weight: 4 to 6 parts of gypsum, 15 to 18 parts of cement, 28 to 30 parts of quick lime, 8 to 10 parts of limestone, 30 to 35 parts of mineral powder, 1 to 2 parts of ethoxyl methyl cellulose ether, 6 to 8 parts of cast stone powder, 6 to 8 parts of ceramic micro-powder, 10 to 15 parts of furfural residue and 4 to 6 parts of medical stone. According to the mountain flour curing agent provided by the invention, mountain flour wastes are cured so that resource utilization is realized; problems that a lot of mountain flour is stacked so that a soil body is occupied and the environment is polluted and the like are solved; the mountain flour curing agent has the advantages of energy conservation and environment friendliness, low construction cost and good benefits; the cured mountain flour has good compression resistance and flexural-tensile property. Furthermore, the mountain flour curing agent provided by the invention can replace a traditional cement stirring pile, can be directly mixed with the mountain flour to carry out curing treatment, so that the construction efficiency is greatly improved and the construction cost is reduced.

Description

technical field [0001] The invention belongs to the field of stone powder curing, and in particular relates to a stone powder curing agent and a preparation method thereof. Background technique [0002] With the increasing demand for stone, the waste stone powder produced by stone processing is also increasing day by day, and the accumulation of a large amount of stone powder has caused a huge environmental burden. The traditional method to solve the accumulation of stone powder is to use cement as the curing agent, mix the stone powder with the stone powder, and then use the stirring machine to carry out forced stirring to make the stone powder harden into cement soil with a certain strength. Cement soil can be used as a stone powder foundation in the construction field. On the one hand, it reduces the environmental burden, and on the other hand, it realizes waste utilization. [0003] However, the unconfined compressive strength of the obtained cement soil is not high whe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/10
CPCC04B28/10C04B2111/00767C04B2201/50C04B7/02C04B22/143C04B14/28C04B18/141C04B24/383C04B14/02C04B20/008C04B14/14C04B18/24
Inventor 陈建康倪晨曦陆伟梅丰
Owner 福建港湾新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com