High-strength antistatic polyethylene film as well as preparation method and application thereof

A technology of polyethylene film and low-density polyethylene, which is applied in the field of high-strength antistatic polyethylene film and its preparation, can solve the problems of large film thickness, high cost, and damage to precision electronic components, so as to improve electrical conductivity, anti-static Long-lasting electrostatic properties and improved antistatic properties

Inactive Publication Date: 2017-02-22
东莞市中为包装制品有限公司
View PDF3 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In view of this, the purpose of the present invention is to provide a high-strength antistatic polyethylene film to solve the problems of large thickness and high cost of the film produced in the prior art, as well as the accumulation of static electricity and damage to precision electronic components. At the same time, the present invention The preparation method and application of the high-strength antistatic polyethylene film are also provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength antistatic polyethylene film as well as preparation method and application thereof
  • High-strength antistatic polyethylene film as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] a. 15kg melt index is 0.27g / 10min, density is 0.918g / cm 3 Low-density polyethylene, 65kg melt index is 0.7g / 10min, density is 0.95g / cm 3 Linear low density polyethylene, 15kg melt index is 0.5g / 10min, density is 0.910g / cm 3 The metallocene polyethylene, the mixture of 1kg oleic acid amide and 2kg silicon dioxide and 2kg antistatic agent are put into the mixer, and then stirred at a speed of 1800rpm for 15min to obtain the mixed masterbatch, which is sucked into the hopper with a suction machine Evenly feed the film blowing machine, the temperature setting of the film blowing machine is: the first zone is 130°C, the second zone is 135°C, the third zone and the fourth zone are 140°C, the filter screen is 140°C, after plasticizing, it will pass through 80°C Purpose Stainless steel gauze filters impurities, and then is extruded by a die head at a temperature of 135°C to obtain a high-strength anti-static polyethylene film, which is then blown into a cylindrical shape by a ...

Embodiment 2

[0041] a. 25kg melt index is 0.3g / 10min, density is 0.920g / cm 3 Low-density polyethylene, 60kg melt index is 0.7g / 10min, density is 0.96g / cm 3 Linear low density polyethylene, 10kg melt index is 0.5g / 10min, density is 0.915g / cm 3 The metallocene polyethylene, the mixture of 0.5kg diatomite and 1.5kg silicon dioxide and 3kg antistatic agent are put into the mixer, and then stirred at the speed of 2000rpm for 20min to obtain the mixed masterbatch, which is mixed with a suction machine The suction hopper feeds the blown film machine evenly. The temperature of the blown film machine is set as follows: the first zone is 132°C, the second zone is 137°C, the third zone and the fourth zone are 142°C, and the filter screen is 142°C. Filter impurities through 80-mesh stainless steel gauze, and then extruded by die head, the temperature of die head is 140 ℃, to obtain high-strength anti-static polyethylene film, then blown into a cylindrical shape through a hair dryer, and finally pulle...

Embodiment 3

[0047] a. 35kg melt index is 0.5g / 10min, density is 0.925g / cm 3 Low-density polyethylene, 54kg melt index is 0.7g / 10min, density is 0.97g / cm 3 Linear low density polyethylene, 5kg melt index is 0.75g / 10min, density is 0.940g / cm 3 The metallocene polyethylene, 4kg oleic acid amide and 2kg antistatic agent are put into the mixer, and then stirred at a speed of 2000rpm for 25min to obtain the mixed masterbatch, and the mixed masterbatch is sucked into the hopper by a suction machine and evenly fed into the film blowing machine. The temperature of the film blowing machine is set as follows: the first zone is 135°C, the second zone is 140°C, the third zone and the fourth zone are 145°C, the filter screen is 145°C, after plasticizing, it passes through 80-mesh stainless steel gauze to filter impurities. Then it is extruded by a die with a die temperature of 145°C to obtain a high-strength anti-static polyethylene film, which is then blown into a tube by a hair dryer, and finally wo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
densityaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-strength antistatic polyethylene film. The polyethylene film contains the following components in percentage by weight: 15-35% of low-density polyethylene, 50-70% of linear low-density polyethylene, 5-15% of metallocene polyethylene, 1-4% of an anti-blocking agent, and 1-3% of an antistatic agent. Besides, the invention also discloses a preparation method and application of the high-strength antistatic polyethylene film. The high-strength antistatic polyethylene film provided by the invention is prepared by the steps of taking the low-density polyethylene (LDPE) as a base material, adding the linear low-density polyethylene (LLDPE) and the metallocene polyethylene (MLLPE) and performing blending extrusion, granulation and blow molding, so that the polyethylene film has relatively good tensile strength and antistatic property; and a packaging bag prepared from the high-strength antistatic polyethylene film has the characteristics of good economical efficiency and mechanical property, lasting antistatic property and convenience in use.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a high-strength antistatic polyethylene film and its preparation method and application. Background technique [0002] The packaging of commodities plays an important role in the storage, quality assurance, transportation and beautification of commodities. With the development of the economy, the advancement of science and technology, the ever-changing products, and the fact that people's life tends to be more convenient and leisure, there are higher requirements for product packaging. [0003] With the development of industrialization, office electronic equipment is also developing in a more and more sophisticated direction. The traditional outer packaging in this industry is packed in cartons, but the cartons are poor in moisture resistance, the packaging is prone to mold, and the cartons are prone to friction with the surface of the equipment. It affects...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08L23/06C08K5/20C08K3/36C08K3/34C08K5/17B29C55/28B31B70/16B31B70/64B31B160/10
CPCC08L23/0815B29C55/28C08J5/18C08J2323/08C08J2423/06C08K2201/017C08L2201/04C08L2203/16C08L2205/025C08L2205/03C08L2207/066C08L23/06C08K5/20C08K3/36C08K3/34C08K5/17
Inventor 万杨青
Owner 东莞市中为包装制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap