Paint formula with good paintability

A coating and formulation technology, applied in the field of coating formulations with good coating performance, can solve problems such as easy generation of fine bubbles, inability to meet production and living needs, poor coverage performance, etc., and achieve overall film stability, good use prospects, and leveling. good performance

Inactive Publication Date: 2017-04-05
袁传江
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, its powder coating is composed of polyester resin, blocked isophor copper diisocyanate, benzoin and dibutyltin dilaurate. Its disadvantages are poor physical properties, poor covering effect, and easy generation of fine bubbles. Unable to meet electrical spraying and surface protection
That is, the existing powder coatings have poor coverage and cannot meet the needs of production and life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A paint formula with good coating performance, said paint formula comprises 28% of high chlorinated polyethylene resin, 18% of curing agent, 3% of auxiliary agent, 3% of leveling agent, 15% of barium sulfate, and brightening agent by weight percentage 2%, titanium dioxide 6%, masterbatch 2%, power enhancer 3%, thickener 6%, antifungal agent 12% and silicon carbide 2%, the sum of the quantities of each component is equal to 100%.

Embodiment 2

[0018] A coating formulation with good coating performance. The coating formulation comprises 33% of high chlorinated polyethylene resin, 19.5% of curing agent, 3% of auxiliary agent, 3% of leveling agent, 12.5% ​​of barium sulfate, and 2% of brightening agent by weight percentage. %, titanium dioxide 5.5%, color masterbatch 2%, power enhancer 3%, thickener 5.5%, antifungal agent 9% and silicon carbide 2%, the sum of the quantities of each component is equal to 100%.

Embodiment 3

[0020] A coating formulation with good coating performance, said coating formulation comprises 38% of high chlorinated polyethylene resin, 21% of curing agent, 3% of auxiliary agent, 3% of leveling agent, 10% of barium sulfate, and brightening agent by weight percentage 2%, titanium dioxide 5%, masterbatch 2%, energizer 3%, thickener 5%, antifungal agent 6% and silicon carbide 2%, the sum of the quantities of each component is equal to 100%.

[0021] When the coating formula with good composite coating performance of the present invention is prepared, the ingredients of each component are prepared according to the formula, put into a mixer, fully mixed for 30 minutes at a speed of 600 rpm, and then put into a dryer to dry and form Flake, and then through the mill to get the powder coating.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a paint formula with good paintability. The paint formula comprises, by weight, 28-38% of high-chlorinated polyethylene resin, 18-21% of curing agents, 3% of auxiliaries, 3% of flatting agents, 10-15% of barium sulfate, 2% of sensitizers, 5-6% of titanium dioxide, 2% of color master, 3% of electric power increase agents, 5-6% of thickening agents, 6-12% of mildew preventives and 2% of silicon carbide, and the weight sum of the components is equal to 100%. The paint formula has the advantages of good covering performance and low cost.

Description

technical field [0001] The invention relates to the field of powder coatings, in particular to a coating formulation with good coating performance. Background technique [0002] Powder coating is a new type of solvent-free 100% solid powder coating. It has the characteristics of no solvent, no pollution, recyclable, environmental protection, saving energy and resources, reducing labor intensity and high mechanical strength of the coating film. In the prior art, its powder coating is composed of polyester resin, blocked isophor copper diisocyanate, benzoin and dibutyltin dilaurate. Its disadvantages are poor physical properties, poor covering effect, and easy generation of fine bubbles. Unable to meet electrical spraying and surface protection. That is, the existing powder coatings have poor coverage and cannot meet the needs of production and life. Contents of the invention [0003] The technical problem to be solved by the present invention is to overcome the above-men...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D123/28C09D7/12
Inventor 袁传江
Owner 袁传江
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap