A Synthetic Process of Composite Superhard Material

A synthesis process, a technology for superhard materials, applied in the process of applying ultra-high pressure, the method of chemically changing substances by using atmospheric pressure, chemical instruments and methods, etc. and other problems, the thermal stability parameters are not much different, the amount of metal dialysis is reduced, and the thermal stability is good.

Active Publication Date: 2019-01-29
湖南泰鼎新材料有限责任公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This currently used synthesis process has some defects. The most important one is that the metal atoms in the cemented carbide dialysis into the superhard material under the action of high temperature and high pressure; and although the product models in each process are exactly the same, However, the amount of dialysis to the superhard material is inconsistent, which also leads to the metal content in the superhard material ranging from 9 to 20%, and the inconsistent metal content in the superhard material will cause individual product quality in the entire batch of products uneven, unstable
[0003] In addition, through inspection and practical application, the thermal stability of the composite superhard material products prepared by the existing technology is low, and the wear ratio is reduced
Not only that, but the yield rate of the resulting products is low, generally lower than 85%

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A Synthetic Process of Composite Superhard Material
  • A Synthetic Process of Composite Superhard Material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Put the assembled cemented carbide and diamond in the pyrophyllite body, put it in the six top hammers of the six-sided hydraulic press, first pressurize to 10MPa, and heat the heating hammer to 700-800°C with power supply, heating time For 30 seconds, pressurize to 90MPa, heat up to 1400°C-1700°C, after reaching the rated time (5-15 minutes) specified by the synthesis process, stop heating, reduce the pressure to zero, and take out the synthesized product.

[0032] The metal content in superhard materials in traditional craft products is 9% to 20%;

[0033] In the products obtained by the above process, the metal content in the superhard material is 1.05%-5.06%.

[0034] And the heat stability of the obtained product is improved to some extent, and the difference of the heat stability parameter before and after the welding of the product is 6%.

Embodiment 2

[0036] Put the assembled cemented carbide and diamond in the pyrophyllite body, and place it in the six top hammers of the six-sided hydraulic press. When the pressure is first increased to 10MPa, the heating hammer is heated to 700-800°C and heated. The time is 30 seconds, the pressure is increased to 90MPa, and the temperature is raised to 1400 ° C ~ 1700 ° C. After reaching the rated time (5 ~ 15 minutes) specified by the synthesis process, further pressure is applied on the hammer surface of the two heating hammers to make it stronger than the four non- The pressure on the hammer surface of the heating hammer is 11% higher. After reaching the rated time (3 to 5 minutes) set by the synthesis process, stop heating, reduce the pressure to zero, and take out the synthesized product.

[0037] The metal content of superhard materials in traditional craft products is 9% to 20%;

[0038] The metal content of the superhard material in the product obtained by the above process is on...

Embodiment 3

[0041] Put the assembled cemented carbide and diamond in the pyrophyllite body, and put it in the six top hammers of the six-sided hydraulic press. When the pressure is first increased to 10MPa, the temperature is raised to 700 ° C ~ 800 ° C, and the heating time is 30 seconds. Press to 90MPa, heat up to 1400℃~1700℃, and after reaching the rated time specified by the synthesis process, apply further pressure on the hammer surfaces of the two heating hammers, making it 19% higher than the pressure on the hammer surfaces of the four non-heating hammers. After reaching the rated time set by the synthesis process, stop heating, reduce the pressure to zero, and take out the synthesized product.

[0042] The metal content of the composite working layer in traditional craft products is 9% to 20%;

[0043] The metal content in the superhard material in the product obtained by the above process is only 2.01%.

[0044] The difference between the thermal stability parameters of the prod...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a synthetic process of a compound superhard material. The synthetic process comprises the following steps: (1) putting an assembled hard alloy and a superhard material into a pyrophyllite body, putting the pyrophyllite body into a cubic press, pressurizing the pyrophyllite body to 8MPa-10MPa, and heating to 700-800 DEG C; and (2) further pressurizing the pyrophyllite body to 90MPa-100MPa, and heating to 1400-1700 DEG C. By virtue of the synthetic process, the dialysis of hard alloy elements in the compounding process of the superhard material can be reduced, the metal content in the superhard material can be reduced, the yield of the superhard material can be increased, the thermal stability of the superhard material can be improved, and the abrasive ratio can be increased.

Description

technical field [0001] The invention belongs to the field of composite superhard material manufacture, and in particular relates to a synthesis process of composite superhard material. Background technique [0002] In my country's composite superhard material manufacturing industry, cemented carbide and superhard materials (diamond or cubic boron nitride, etc.) are usually used to synthesize a new composite superhard material product through high temperature and high pressure on a six-sided hydraulic press. At present, the production process of all composite superhard material products is basically the same, that is, the assembled composite superhard material pyrophyllite is synthesized into a cube, placed in the six top hammers of the six-sided hydraulic press, and the pressure of the press system is reduced. After rising to 50-90MPa, turn on the power and directly heat up the composite superhard material pyrophyllite cube; when the synthetic pressure reaches the rated pres...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J3/06
CPCB01J3/062B01J2203/062B01J2203/0645
Inventor 蒋向上蒋孟瑶
Owner 湖南泰鼎新材料有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com