PC composite based on basalt fiber reinforcement and preparation method thereof

A technology of basalt fiber and composite materials, which is applied in the field of basalt fiber-reinforced PC composite materials and its preparation, can solve the problems of inability to meet the strength requirements of parts, material performance degradation, and easy damage, and achieve excellent performance and tensile strength. The effect of highlighting the intensity and improving the descriptive

Inactive Publication Date: 2017-05-31
DONGGUAN G ONE NUCLEAR MATERIALS CO LTD
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the development of the automobile industry, the requirements for auto parts are getting higher and higher, and the polycarbonate of the existing technology has been increasingly unable to meet the requirements of the automobile industry for the strength of parts
[0004] Therefore, many fiber-reinforced modified resins have appeared at home and abroad, such as increasing the strength of polycarbonate through glass fibers or carbon fibers. However, although carbon fibers have high strength and good thermal stability, they are relatively heavy, easy to rust, and easy to damage. Although glass fiber has high strength and cheap price, it is easy to melt at high temperature, which will lead to the decline of material performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PC composite based on basalt fiber reinforcement and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0025] Based on basalt fiber reinforced PC composite material, including the following components in parts by weight, 30 parts of PC; 30 parts of basalt fiber; 5 parts of kaolin; 12 parts of acrylic fiber; 10 parts of polypropylene; 5 parts of toughening agent; 1.5 parts of lubricant parts; 1.5 parts of coupling agent; 5 parts of compatibilizer.

[0026] The preparation method based on the PC composite material reinforced by basalt fiber comprises the following steps, a. get PC, basalt fiber, kaolin, acrylic fiber, polypropylene, toughening agent, lubricant, coupling agent, compatibilizer of formula quantity, Mix evenly; b. import each component in step a into a screw extruder and extrude to obtain a strip; c. carry out water cooling and air-drying treatment on the strip; d. take the cooled and dried strip in step c and cut grain.

[0027] In step b, the extrusion temperature of the screw extruder is 220° C., and the screw speed is 170 r / m.

specific Embodiment 2

[0029] Based on basalt fiber reinforced PC composite material, including the following components in parts by weight, 35 parts of PC; 20 parts of basalt fiber; 5 parts of kaolin; 12 parts of acrylic fiber; 15 parts of polypropylene; 5 parts of toughening agent; 1.5 parts of lubricant parts; 1.5 parts of coupling agent; 5 parts of compatibilizer.

[0030] The preparation method based on the PC composite material reinforced by basalt fiber comprises the following steps, a. get PC, basalt fiber, kaolin, acrylic fiber, polypropylene, toughening agent, lubricant, coupling agent, compatibilizer of formula quantity, Mix evenly; b. import each component in step a into a screw extruder and extrude to obtain a strip; c. carry out water cooling and air-drying treatment on the strip; d. take the cooled and dried strip in step c and cut grain.

[0031] In step b, the extrusion temperature of the screw extruder is 220° C., and the screw speed is 170 r / m.

specific Embodiment 3

[0033] The PC composite material reinforced based on basalt fiber comprises the following components in parts by weight, 40 parts of PC; 10 parts of basalt fiber; 5 parts of kaolin; 12 parts of acrylic fiber; 20 parts of polypropylene; 5 parts of toughening agent; 1.5 parts of lubricant parts; 1.5 parts of coupling agent; 5 parts of compatibilizer.

[0034] The preparation method based on the PC composite material reinforced by basalt fiber comprises the following steps, a. get PC, basalt fiber, kaolin, acrylic fiber, polypropylene, toughening agent, lubricant, coupling agent, compatibilizer of formula quantity, Mix evenly; b. import each component in the step a into a screw extruder and extrude to obtain a strip; c. carry out water cooling and air-drying to the strip; d. take the cooled and dried strip in step c and cut grain.

[0035] In step b, the extrusion temperature of the screw extruder is 220° C., and the screw speed is 170 r / m.

[0036] Control group:

[0037] PC ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of plastic raw materials and particularly relates to a PC composite based on basalt fiber reinforcement and a preparation method thereof. The PC composite based on basalt fiber reinforcement comprises the following components in parts by weight: 25-45 parts of PC, 10-30 parts of basalt fiber, 4-6 parts of kaolin, 10-15 parts of acrylic fiber, 10-20 parts of polypropylene, 3-8 parts of a toughening agent, 1-2 parts of a lubricant, 1-2 parts of a coupling agent and 2-6 parts of a compatilizer. The PC composite provided by the invention has high bending strength, high tensile strength, good impact strength and stable chemical properties and is convenient to recycle.

Description

technical field [0001] The invention relates to the field of plastic raw materials, in particular to a basalt fiber reinforced PC composite material and a preparation method thereof. Background technique [0002] Polycarbonate (referred to as PC) is a high molecular polymer containing carbonate groups in the molecular chain. According to the structure of the ester group, it can be divided into aliphatic, aromatic, aliphatic-aromatic and other types. Due to its excellent physical and chemical properties, PC engineering plastics are widely used in various industries. Its three major application areas are glass assembly industry, automobile industry, electronics and electrical appliances industry, followed by industrial machinery parts, CDs, packaging, computers and other offices. Equipment, medical and healthcare, film, leisure and protective equipment, etc. [0003] In the automotive industry, polycarbonate has good impact resistance, thermal distortion resistance, good weat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L23/12C08L91/06C08L35/06C08L51/04C08K13/04C08K7/08C08K3/34C08K5/544
CPCC08L69/00C08K2201/014C08K2201/016C08L2205/035C08L2207/53C08L23/12C08L91/06C08L35/06C08L51/04C08K13/04C08K7/08C08K3/346C08K5/544
Inventor 叶海勇叶海军张宏伟
Owner DONGGUAN G ONE NUCLEAR MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap