A kind of bio-based polyamide and preparation method thereof

A bio-based polyamide and bio-based technology are applied in the fields of bio-based polyamide and its preparation, bio-based polyhexamethylene azelaic acid and its preparation field, and can solve the problems of complicated operation steps and technological processes, unfavorable environmental protection, increased Problems such as the difficulty of post-processing work to achieve the effect of alleviating the increasing depletion of fossil resources

Active Publication Date: 2019-01-15
DONGHUA UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This type of reaction is usually considered to be divided into two steps. On the one hand, the operation steps and process are complicated, and the raw material consumption and equipment requirements are relatively high; using ethanol and other solvents to dissolve monomers such as reactions will consume a large amount of organic solvents. , which is not conducive to environmental protection, but also increases the difficulty of post-processing work; on the other hand, the condensation stage needs to be exhausted under conditions such as high temperature and high pressure, which will cause serious escape of monomers in the reaction system and an imbalance in the ratio of monomers
Therefore, in the reaction process, the hexamethylenediamine monomer needs to be in excess of about 5%, and the excess of the monomer will play a role of end-capping, resulting in a decrease in the molecular weight and performance of the polymer.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of bio-based polyamide and preparation method thereof
  • A kind of bio-based polyamide and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A preparation method of bio-based polyamide, comprising the following steps:

[0037] Preparation of mixed solution of 1,6-hexamethylenediamine and 1,9-azelaic acid: add 1,6-hexamethylenediamine (slightly warmed before use to make it melt from crystal to liquid) into 1,9-azelaic acid, follow The mass ratio of the reaction monomer (that is, the mass sum of 1,9-azelaic acid and 1,6-hexanediamine) to deionized water is 1:0.3. Add deionized water and stir at 400r / min for 2 minutes A mixed solution is then prepared.

[0038] Preparation of polyhexamethylene azelaic acid amide: Add the mixed solution of 1,6-hexanediamine and 1,9-azelaic acid into the polymerization kettle through the feed port of the polymerization kettle, seal the polymerization kettle, 1,9-nonanedioic acid The monomer molar ratio of diacid and 1,6-hexamethylenediamine is 1:1.008; then the atmosphere in the polymerization kettle is replaced with nitrogen atmosphere, and the method of replacing the atmospher...

Embodiment 2

[0041] A preparation method of bio-based polyamide, comprising the following steps:

[0042] Preparation of mixed solution of 1,6-hexamethylenediamine and 1,9-azelaic acid: add 1,6-hexamethylenediamine (slightly warmed before use to make it melt from crystal to liquid) into 1,9-azelaic acid, follow The mass ratio of reaction monomer (that is, the mass sum of 1,9-azelaic acid and 1,6-hexanediamine) to deionized water is 1:0.9, add deionized water, and stir at a speed of 100r / min for 10 minutes A mixed solution is then prepared.

[0043] Preparation of polyhexamethylene azelaic acid amide: Add the mixed solution of 1,6-hexanediamine and 1,9-azelaic acid into the polymerization kettle through the feed port of the polymerization kettle, seal the polymerization kettle, 1,9-nonanedioic acid The monomer molar ratio of diacid and 1,6-hexanediamine is 1:1.01; then the atmosphere in the polymerization kettle is replaced with nitrogen atmosphere, and the method of replacing the atmosphe...

Embodiment 3

[0046] A preparation method of bio-based polyamide, comprising the following steps:

[0047] Preparation of mixed solution of 1,6-hexamethylenediamine and 1,9-azelaic acid: add 1,6-hexamethylenediamine (slightly warmed before use to make it melt from crystal to liquid) into 1,9-azelaic acid, follow The mass ratio of the reaction monomer (that is, the mass sum of 1,9-azelaic acid and 1,6-hexanediamine) to deionized water is 1:0.7. Add deionized water and stir at a speed of 150r / min for 8 minutes A mixed solution is then prepared.

[0048] Preparation of polyhexamethylene azelaic acid amide: Add the mixed solution of 1,6-hexanediamine and 1,9-azelaic acid into the polymerization kettle through the feed port of the polymerization kettle, seal the polymerization kettle, 1,9-nonanedioic acid The monomer molar ratio of diacid and 1,6-hexanediamine is 1:1.005; then the atmosphere in the polymerization tank is replaced with nitrogen atmosphere, and the method of replacing the atmosph...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
temperatureaaaaaaaaaa
Login to View More

Abstract

The invention relates to biological-based polyamide and apreparation method thereof. Biological bases 1,9-azelaic acid and 1,10-decamethylene diamine prepared by adopting renewable biological resources perform direct melting condensation reaction, the biological-based polyamide can be obtained and is specifically biological-based polyazylenediamine.Only water is used as a solvent in the whole synthetic process without any organic solvent or additive, so that the phenomenon that introduced organic solvents and additives change the physical and chemical parameters and properties of the monomersand amine salt in the polymerization process and accordingly the whole polymerizing technological process is influenced can be prevented. The water is used as the solvent, so that the biological-based polyamide is clean and environmentally friendly and conforms to the purpose that biological-based high-molecular materials are green, environmentally friendly and cyclically regeneratable. In addition, the water is used as the solvent, a reaction medium is provided in the polymerization process, and energy transfer, charging and follow-up reaction are promoted.

Description

technical field [0001] The invention relates to the field of bio-based polymer materials, in particular to a bio-based polyamide and a preparation method thereof, in particular to a bio-based polyhexamethylene azelate and a preparation method thereof. Background technique [0002] Since the beginning of the 20th century, the germination of polymer materials has opened a new chapter for human beings to explore and apply materials science. The source of polymer materials has gradually developed from the initial natural polymer materials (such as rubber, animals, plant fibers, etc.) Transitioning to petrochemical resources, while satisfying the materials used by human beings, the issue of sustainable development is undoubtedly an urgent problem that needs to be thought, explored and solved practically. [0003] Polyamide, referred to as PA, is called nylon in the industry, and has been developed for more than 80 years. With its excellent comprehensive properties, polyamide has...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityPatents(China)
IPC IPC(8): C08G69/26C08G69/28
CPCC08G69/26C08G69/28
Inventor陶磊肖茹刘可李圆圆刘畅王华平
OwnerDONGHUA UNIV