High-performance medical liquid adhesive bandage and preparation method thereof

A Band-Aid, high-performance technology, applied in medical science, bandages, etc., can solve problems such as toxic and harmful chemical reducing agents, and achieve the effects of good biodegradability, non-allergic skin contact, and easy availability of raw materials

Active Publication Date: 2017-07-07
深圳立专技术转移中心有限公司
View PDF11 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the above method effectively produces nano-silver, some toxic and harmful chemical reduction reagents are added in the preparation process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance medical liquid adhesive bandage and preparation method thereof
  • High-performance medical liquid adhesive bandage and preparation method thereof
  • High-performance medical liquid adhesive bandage and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A method for preparing high-performance medical liquid band-aids includes the following specific steps:

[0029] (1) Add 1.0g cellulose acetate, 0.2g castor oil, 0.4g triacetin, 2.0g benzyl alcohol to 10.0g ethyl acetate solution, and mechanically stir to fully dissolve into a film-forming solution;

[0030] (2) Mix 2.0 mL of tannic acid ethanol solution (2.0 mg / mL) with 0.7 mL of silver nitrate aqueous solution (0.1 mg / mL), and react in a constant temperature water bath at 30°C for 8 hours to prepare a silver nanoparticle solution;

[0031] (3) The silver nanoparticle solution prepared in step (2) and 0.02 g of dopamine are added to the film-forming solution prepared in step (1) and mixed uniformly to prepare the high-performance medical liquid band-aid.

Embodiment 2

[0033] A method for preparing high-performance medical liquid band-aids includes the following specific steps:

[0034] (1) Add 1.2 g of cellulose acetate, 0.4 g of castor oil, 0.5 g of triacetin, and 4.0 g of benzyl alcohol to 12.0 g of ethyl acetate solution and fully dissolve it into a film-forming solution with mechanical stirring;

[0035] (2) Mix 1.2 mL of tannic acid ethanol solution (4.0 mg / mL) with 0.3 mL of silver nitrate aqueous solution (0.25 mg / mL), and react in a constant temperature water bath at 35°C for 12 hours to prepare a silver nanoparticle solution;

[0036] (3) The silver nanoparticle solution prepared in step (2) and 0.03 g of dopamine are added to the film-forming solution prepared in step (1) and mixed uniformly to prepare the high-performance medical liquid band-aid.

Embodiment 3

[0038] A method for preparing high-performance medical liquid band-aids includes the following specific steps:

[0039] (1) Add 0.8g cellulose acetate, 0.2g castor oil, 0.4g triacetin, 3.0g benzyl alcohol to 10.0g ethyl acetate solution, and fully dissolve it into a film-forming solution with mechanical stirring;

[0040] (2) Mix 2.0 mL of tannic acid ethanol solution (1.5 mg / mL) with 0.2 mL of silver nitrate aqueous solution (0.3 mg / mL), and react in a constant temperature water bath at 40°C for 24 hours to prepare a silver nanoparticle solution;

[0041] (3) The silver nanoparticle solution prepared in step (2) and 0.01 g of dopamine are added to the film-forming solution prepared in step (1) and mixed uniformly to prepare the high-performance medical liquid band-aid.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
concentrationaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-performance medical liquid adhesive bandage. The liquid adhesive bandage contains the following raw materials (by weight): 80-120 parts of cellulose acetate, 20-50 parts of castor oil, 30-70 parts of glyceryl triacetate, 200-500 parts of benzyl alcohol, 80-1200 parts of ethyl acetate, 1-10 parts of dopamine, 40-400 parts of a silver nitrate aqueous solution and 100-500 parts of an ethanol solution. The adhesive bandage of the invention has a good antibacterial property and also has properties such as high adhesion to skin, waterproofness, air permeability, concealing performance and the like.

Description

Technical field [0001] The invention relates to the technical field of medical materials, in particular to a high-performance liquid band-aid with antibacterial, high adhesion and concealing functions. Background technique [0002] People will inevitably cause various skin injuries in daily life and work, and the methods for treating wounds on the market mainly include powder drugs, ointment drugs, band-aids, medical gauze, etc., but the drugs are waterproof and breathable. Poor, the biocompatibility is not ideal, but medical band-aids and gauze have no antibacterial properties and are prone to secondary infections. At present, many new medical dressings appear on the market. For example, the patent number CN 102772801 A discloses a wound spray for treating abrasions, and the patent number CN 105288722 A provides a kind of nitrocellulose. The waterproof and breathable liquid band-aids of membrane materials, but they only play the simplest protective effect on the wound surface, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A61L26/00
Inventor 袁妍章金凤周珍施楠彬刘仁
Owner 深圳立专技术转移中心有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap