Metal anticorrosive material, and preparation method thereof
A metal anti-corrosion and raw material technology, applied in anti-corrosion coatings, epoxy resin coatings, coatings, etc., to achieve the effect of good surface toughness, good thixotropy and strong adhesion
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0033] Example 1
[0034] A metal anticorrosive material, comprising the following raw materials in parts by weight: 75 parts of epoxy resin, 25 parts of mixed solvent, 1.75 parts of toughening agent, 0.35 parts of defoamer, 10 parts of phenalkamine epoxy curing agent, and 2.2 parts of anti-aging agent , 0.8 part of antioxidant, 0.45 part of lubricant, 0.9 part of thixotropic agent, 2 parts of pigment and 20 parts of filler;
[0035] The mixed solvent is ethanol, methyl ethyl ketone and DBE in a weight ratio of 1:2:7.
[0036] The toughening agent is nano-silica or liquid polysulfide rubber. The elongation of the epoxy resin is low after curing, and the brittleness is large. When the bonding part is subjected to external force, it is easy to crack and develop rapidly, causing the anti-corrosion coating to crack; nano-dioxide Silicon has strong rigidity. When the cracks expand, they will deflect when encountering nano-silica particles, thereby absorbing energy and achieving the purpo...
Example Embodiment
[0050] Example 2
[0051] A metal anticorrosive material, comprising the following raw materials in parts by weight: 70 parts of epoxy resin, 20 parts of mixed solvent, 0.5 part of toughening agent, 0.2 part of defoaming agent, 4 parts of phenalkamine epoxy curing agent, 1.2 parts of anti-aging agent , 0.1 part of antioxidant, 0.1 part of lubricant, 0.5 part of thixotropic agent, 1 part of pigment and 15 parts of filler;
[0052] The mixed solvent is ethanol, methyl ethyl ketone and DBE in a weight ratio of 1:1.8:6.5.
[0053] The toughening agent is nano-silica or liquid polysulfide rubber. The elongation of the epoxy resin is low after curing, and the brittleness is large. When the bonding part is subjected to external force, it is easy to crack and develop rapidly, causing the anti-corrosion coating to crack; nano-dioxide Silicon has strong rigidity. When the cracks expand, they will deflect when encountering nano-silica particles, thereby absorbing energy and achieving the purpo...
Example Embodiment
[0067] Example 3
[0068] A metal anticorrosive material, comprising the following raw materials in parts by weight: 80 parts of epoxy resin, 30 parts of mixed solvent, 3 parts of toughening agent, 0.5 part of defoaming agent, 16 parts of phenalkamine epoxy curing agent, and 3.2 parts of anti-aging agent , Antioxidant 1.5 parts, lubricant 0.8 parts, thixotropic agent 1.3 parts, pigment 3 parts and filler 25 parts;
[0069] The mixed solvent is ethanol, methyl ethyl ketone and DBE in a weight ratio of 1:2.2:7.5.
[0070] The toughening agent is nano-silica or liquid polysulfide rubber. The elongation of the epoxy resin is low after curing, and the brittleness is large. When the bonding part is subjected to external force, it is easy to crack and develop rapidly, causing the anti-corrosion coating to crack; nano-dioxide Silicon has strong rigidity. When the cracks expand, they will deflect when encountering nano-silica particles, thereby absorbing energy and achieving the purpose of t...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap