Agriculture straw regeneration fire-proof heat preservation plate material and preparation method thereof

A technology of fire prevention and heat preservation and straw, which is applied in the direction of flat products, manufacturing tools, wood processing appliances, etc., can solve the problems of environmental damage, waste of resources, etc., and achieve the effects of avoiding short life, good air purification, and large specific surface area

Inactive Publication Date: 2017-09-22
合肥市风达农业有限责任公司
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Crop straw is an important material resource. Improper disposal will not only cause waste of resources, but also cause damage to the environment. Utilization will definitely have a profound impact on the development of sustainable rural economy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A kind of agricultural straw regenerated fireproof and thermal insulation board in this embodiment includes the following raw materials in parts by weight:

[0036] 60 parts of agricultural straw, 10 parts of binder, 3 parts of metal oxide, 3 parts of waterproofing agent, 3 parts of flame retardant, 15 parts of modified kaolin, 12 parts of white cement, and 20 parts of water.

[0037] The agricultural straw in this embodiment is a mixture of wheat straw, rice straw, corn straw, sorghum straw, reed straw, and cotton straw in a weight ratio of 3:1:2:3:4:1.

[0038]The binder in this embodiment is a mixture of shellac, gum arabic, white latex and epoxy glue in a weight ratio of 2:2:1:3.

[0039] The metal oxide in this embodiment is a mixture of magnesium oxide, zinc oxide, aluminum oxide, calcium oxide and barium oxide in a weight ratio of 2:1:1:2:1.

[0040] The waterproofing agent in this embodiment is a mixture of paraffin wax and rosin in a weight ratio of 2:1.

[0...

Embodiment 2

[0050] A kind of agricultural straw regenerated fireproof and thermal insulation board in this embodiment includes the following raw materials in parts by weight:

[0051] 80 parts of agricultural straw, 15 parts of binder, 6 parts of metal oxide, 7 parts of waterproofing agent, 5 parts of flame retardant, 20 parts of modified kaolin, 18 parts of white cement, and 26 parts of water.

[0052] The agricultural straw in this embodiment is a mixture of wheat straw, rice straw, corn straw, sorghum straw, reed straw, and cotton straw in a weight ratio of 3:1:2:3:4:1.

[0053] The binder in this embodiment is a mixture of shellac, gum arabic, white latex and epoxy glue in a weight ratio of 2:2:1:3.

[0054] The metal oxide in this embodiment is a mixture of magnesium oxide, zinc oxide, aluminum oxide, calcium oxide and barium oxide in a weight ratio of 2:1:1:2:1.

[0055] The waterproofing agent in this embodiment is a mixture of paraffin wax and rosin in a weight ratio of 2:1.

[...

Embodiment 3

[0065] A kind of agricultural straw regenerated fireproof and thermal insulation board in this embodiment includes the following raw materials in parts by weight:

[0066] 70 parts of agricultural straw, 13 parts of binder, 4.5 parts of metal oxide, 5 parts of waterproofing agent, 4 parts of flame retardant, 17 parts of modified kaolin, 16 parts of white cement, and 23 parts of water.

[0067] The agricultural straw in this embodiment is a mixture of wheat straw, rice straw, corn straw, sorghum straw, reed straw, and cotton straw in a weight ratio of 3:1:2:3:4:1.

[0068] The binder in this embodiment is a mixture of shellac, gum arabic, white latex and epoxy glue in a weight ratio of 2:2:1:3.

[0069] The metal oxide in this embodiment is a mixture of magnesium oxide, zinc oxide, aluminum oxide, calcium oxide and barium oxide in a weight ratio of 2:1:1:2:1.

[0070] The waterproofing agent in this embodiment is a mixture of paraffin wax and rosin in a weight ratio of 2:1.

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an agriculture straw regeneration fire-proof heat preservation plate material. The agriculture straw regeneration fire-proof heatpreservation plate material comprises raw materials, by weight, 60-80 parts of agriculture straw, 10-15 parts of binder, 3-6 parts of metal oxide, 3-7 parts of water-proof agent, 3-5 parts of fire retardant, 15-20 parts of modified kaolin, 12-18 parts of white cement and 20-26 parts water. The agriculture straw regeneration fire-proof heat preservation plate material has the excellent properties of rapid prototyping, heat insulation and heat preservation, inflaming retarding, mould proof, deliquescence resistance, high strength and the like, the plate material is divided into a pressed inner core and an outer surface coating layer, the problems of being prone to breaking billet, sticking plate and demoulding are solved, continuous production is achieved, and the production efficiency is improved greatly; and meanwhile, the source of the main raw materials of the agriculture straw regeneration fire-proof heat insulation plate material is wide, the cost is low, the technology is simple and clear, and the high practical value and the good application prospect are achieved.

Description

technical field [0001] The invention relates to the technical field of agricultural straw utilization, in particular to a recycled agricultural straw fire-proof and thermal insulation board and a preparation method thereof. Background technique [0002] At present, there are many types of thermal insulation boards for building exterior walls in China, but their quality and performance are uneven. Polyurethane foam, polystyrene foam and their composite boards, which were widely used in the past, are not only flammable but also emit a lot of smoke (containing toxic carcinogens such as hydrogen cyanide and dioxin) if exposed to high temperature or open flames. In recent years, rapid development such as rock wool insulation board, in the process of production and construction, there will be a large number of cotton-like fibers floating into the air, polluting the air environment and irritating human skin; Poor, fragile and other defects affect the construction quality. [0003...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27N3/10B27N1/02B27N3/02B27N1/00B28B1/16C08L97/02C08L93/02C08L5/00C08L31/04C08L63/00C08L93/04C08L91/06C08K3/00C08K3/22C08K3/38C08K3/34C04B28/04C04B111/28C04B111/20
CPCB27N3/10B27N1/00B27N1/0209B27N3/02B28B1/16C04B28/04C04B2111/2092C04B2111/28C04B2201/32C04B2201/50C08K2003/2206C08K2003/2224C08K2003/2227C08K2003/2296C08K2003/387C08K2201/014C08L97/02C08L2201/02C08L2205/02C08L2205/025C08L2205/035C04B14/106C04B14/304C04B14/30C04B14/303C04B22/064C08L93/02C08L5/00C08L31/04C08L63/00C08L93/04C08L91/06C08K3/00C08K3/22C08K3/38C08K3/346C08K3/34
Inventor 胡贤根
Owner 合肥市风达农业有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap