Ceramic product capable of improving human malignant tumor and preparation method of ceramic product

A technology for ceramic products and malignant tumors, which is applied in the field of ceramic products to achieve the effect of improving human metabolic function, speeding up metabolism and meeting market demand

Inactive Publication Date: 2018-01-09
GUANGDONG KANGSHITAI NEW MATERIAL TECH CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, ceramic products cannot realize the effect of delivering bioenergy to people for a long time and improving their overall health. Ceramic products that can improve human malignant tumors are in a vacancy in the ceramic industry.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A method for preparing the ceramic product for improving human malignant tumors, comprising the following steps:

[0013] A. Raw material equipment; calculated in parts by weight, the components of ceramic products include: 40 parts of Dongxing sand, 41 parts of pure white sand, 9 parts of Fuming sand, 13 parts of water mill powder, 5 parts of super white ball soil, and 5 parts of Huidong Yuanni 5 parts, 5 parts of quartz powder, 5 parts of calcined talc, 4 parts of bentonite, and 0.4 parts of auxiliary agent are mixed and prepared to obtain a mixture A1; B, ball milling; put the mixture A1 and water (by weight 2:1) into the ball mill Mix and grind inside to form slurry B1; C, spray granulation; spray the slurry B1 in a spray drying tower to dry and granulate to form powder C1; D, stamping; Material C1 is added to a punching machine for cloth and stamping forming to obtain ceramic tile body D1; E, calcining; putting the ceramic tile body D1 into a kiln for calcining to ...

Embodiment 2

[0015] A method for preparing the ceramic product for improving human malignant tumors, comprising the following steps:

[0016] A. Raw materials: 50 parts of Dongxing sand, 50 parts of pure white sand, 16 parts of Fuming sand, 20 parts of water mill powder, 10 parts of super white ball soil, 15 parts of Huidong Yuanni, 15 parts of quartz powder, 10 parts of burnt talc, 8 parts of bentonite and 1 part of auxiliary agent are mixed and prepared to obtain a mixture A1; B, ball milling; the mixture A1 and water (by weight ratio 2:1) are added to a ball mill for mixing and grinding to form a slurry B1; C, Spray granulation; spray the slurry B1 in a spray drying tower to dry it, granulate it to form powder C1; D, stamping molding; add the powder C1 to a punching machine for cloth and stamping molding to obtain Ceramic tile body D1; E, calcining; put the ceramic tile body D1 into a kiln for calcination to obtain ceramic tile E1; F, take 140 parts of Adenophora chinensis, 160 parts of...

Embodiment 3

[0018] A method for preparing the ceramic product for improving human malignant tumors, comprising the following steps:

[0019] A. Raw materials: 45 parts of Dongxing sand, 45 parts of pure white sand, 10 parts of Fuming sand, 15 parts of water mill powder, 9 parts of super white ball soil, 10 parts of Huidong Yuanni, 10 parts of quartz powder, 8 parts of burnt talc, 6 parts of bentonite and 0.5 parts of auxiliary agent are mixed and prepared to obtain a mixture A1; B, ball milling; the mixture A1 and water (by weight ratio 2:1) are added to a ball mill for mixing and grinding to form a slurry B1; C, Spray granulation; spray the slurry B1 in a spray drying tower to dry it, granulate it to form powder C1; D, stamping molding; add the powder C1 to a punching machine for cloth and stamping molding to obtain Ceramic tile body D1; E, calcining; put the ceramic tile body D1 into a kiln for calcination to obtain ceramic tile E1; F, take 120 parts of Adenophora chinensis, 120 parts o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a ceramic product capable of improving human malignant tumor and a preparation method of the ceramic product. The ceramic product is prepared from components in parts by weight as follows: 40-50 parts of Dongxing sand, 41-50 parts of pure white sand, 9-16 parts of Fuming sand, 13-20 parts of grains ground with water, 5-10 parts of ultra-white ball clay, 5-15 parts of Huidong raw mud, 5-15 parts of quartz powder, 0.4-1 part of an auxiliary, 100-140 parts of radix glehniae, 100-160 parts of radix puerariae, 60-120 parts of plumula nelumbinis, 50-150 parts of bulbus lilii, 110-130 parts of radix trichosanthis, 100-150 parts of radix astragali, 100-180 parts of radix salviae miltiorrhizae, 100-160 parts of semen coicis, 60-100 parts of rhizoma dioscoreae, 80-100 partsof fructus lycii, 100-150 parts of herba scutellariae barbatae and 80-160 parts of herba taraxaci. The ceramic product effectively improves human physical functions, has the function of improving human malignant tumor and has broad market prospect.

Description

technical field [0001] The invention relates to the technical field of ceramic products, in particular to a ceramic product for improving human malignant tumors and a preparation method thereof. Background technique [0002] At present, ceramic products cannot meet the needs of transmitting bioenergy to people for a long time and improving their overall health. Ceramic products that can improve human malignant tumors are in a vacancy in the ceramic industry. Contents of the invention [0003] The object of the present invention is to address the deficiencies in the prior art and propose a ceramic product for improving human malignant tumors and a preparation method thereof. The ceramic product has the function of improving human malignant tumors. [0004] For reaching this purpose, the present invention adopts following technical scheme: [0005] A ceramic product for improving human malignant tumors. Calculated by weight, the components of the ceramic product include: 40...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/14C04B35/622C04B41/82
Inventor 程燕文周永富
Owner GUANGDONG KANGSHITAI NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap