A technology for the measurement and analysis of acid rain, applied in the direction of anti-corrosion coatings, coatings, etc., can solve the problem of unsatisfactory surface finish, and achieve the effect of excellent anti-oxidation and high surface finish
Inactive Publication Date: 2018-02-09
CHANGSHU YUHUA METROLOGY TESTING CONSULTING SERVICE CO LTD
View PDF2 Cites 4 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] Existing acid rain sampling and measuring analyzers, the oxidation resistance, abrasion resistance, corrosion resistance, rust resistance,
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Example Embodiment
[0024] Example 1
[0025] An acid rain sampling and measuring analyzer includes a metal shell, and the metal shell is coated with a film. The film coating includes the following steps:
[0026] 1) Put 1 to 2 parts by weight of lauryltrimethylammonium bromide, 2.5 parts by weight of alumina, 1.6 parts by weight of dibutyl phthalate, and 0.9 parts by weight of alum into 50 parts by weight of deionized water in sequence, and stir evenly;
[0027] 2) Then add 15.5 parts by weight of styrene, 9.9 parts by weight of hydroxypropyl methylcellulose, 1.8 parts by weight of alkylphenol polyoxyethylene ether, and 0.9 parts by weight of potassium tetraborate in sequence, and continue to stir until fully mixed and uniformly prepared. Coating treatment liquid;
[0028] 3) Immerse the metal shell in the coating treatment liquid, take it out and dry it.
Example Embodiment
[0029] Example 2
[0030] An acid rain sampling and measuring analyzer includes a metal shell, and the metal shell is coated with a film. The film coating includes the following steps:
[0031] 1) Put 1 part by weight of lauryltrimethylammonium bromide, 2.5 parts by weight of alumina, 1.6 parts by weight of dibutyl phthalate, and 0.9 parts by weight of alum into 50 parts by weight of deionized water in sequence, and stir evenly;
[0032] 2) Then add 15.5 parts by weight of styrene, 9.9 parts by weight of hydroxypropyl methylcellulose, 1.8 parts by weight of alkylphenol polyoxyethylene ether, and 0.9 parts by weight of potassium tetraborate in sequence, and continue to stir until fully mixed and uniformly prepared. Coating treatment liquid;
[0033] 3) Immerse the metal shell in the coating treatment liquid, take it out and dry it.
Example Embodiment
[0034] Example 3
[0035] An acid rain sampling and measuring analyzer includes a metal shell, and the metal shell is coated with a film. The film coating includes the following steps:
[0036] 1) Put 2 parts by weight of lauryltrimethylammonium bromide, 2.5 parts by weight of alumina, 1.6 parts by weight of dibutyl phthalate, and 0.9 parts by weight of alum into 50 parts by weight of deionized water in sequence, and stir evenly;
[0037] 2) Then add 15.5 parts by weight of styrene, 9.9 parts by weight of hydroxypropyl methylcellulose, 1.8 parts by weight of alkylphenol polyoxyethylene ether, and 0.9 parts by weight of potassium tetraborate in sequence, and continue to stir until fully mixed and uniformly prepared. Coating treatment liquid;
[0038] 3) Immerse the metal shell in the coating treatment liquid, take it out and dry it.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses an acid rain sampling, measuring and analyzing instrument which comprises metal shells. The metal shells are laminated and treated. A method for laminating and treating the metal shells includes steps of 1), sequentially inputting, by weight, 1-2 parts of dodecyl trimethyl ammonium bromide, 2.5 parts of aluminum oxide, 1.6 parts of dibutyl phthalate and 0.9 part of alum into 50 parts of deionized water and uniformly stirring the dodecyl trimethyl ammonium bromide, the aluminum oxide, the dibutyl phthalate, the alum and the deionized water to obtain first mixtures; 2), sequentially inputting, by weight, 15.5 parts of styrene, 9.9 parts of hydroxy propyl methylcelluloses, 1.8 parts of alkylphenol ethoxylate and 0.9 part of potassium tetraborate into the first mixtures, and continuing to stir the styrene, the hydroxy propyl methylcelluloses, the alkylphenol ethoxylate, the potassium tetraborate and the first mixtures until the styrene, the hydroxy propyl methylcelluloses, the alkylphenol ethoxylate, the potassium tetraborate and the first mixtures are sufficiently uniformly mixed with one another to obtain laminating and treating liquid; 3), placing the metal shells in the laminating and treating liquid, impregnating the metal shells in the laminating and treating liquid, taking the metal shells out of the laminating and treating liquid and then drying themetal shells. The acid rain sampling, measuring and analyzing instrument has the advantages that protective films cover the surfaces of the metal shells of the acid rain sampling, measuring and analyzing instrument, and accordingly the acid rain sampling, measuring and analyzing instrument is good in performance and high in surface smoothness.
Description
technical field [0001] The invention relates to an acid rain sampling and measuring analyzer. Background technique [0002] In the existing acid rain sampling and measuring analyzer, the oxidation resistance, abrasion resistance, corrosion resistance, rust resistance, heat resistance, cold resistance and weather resistance performance of the metal shell need to be improved, and the surface finish is not ideal. Contents of the invention [0003] The object of the present invention is to provide a kind of acid rain sampling and measuring analyzer, the surface of its metal shell is covered with a protective film, which has excellent oxidation resistance, abrasion resistance, corrosion resistance, rust resistance, heat resistance, cold resistance, weather resistance, and the surface High finish. [0004] In order to achieve the above object, the technical solution of the present invention is: a kind of acid rain sampling and measuring analyzer, which comprises a metal casing,...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more
IPC IPC(8): C09D4/06C09D7/61C09D7/63C09D5/08
CPCC09D4/06C09D5/08
Inventor 马美珍
Owner CHANGSHU YUHUA METROLOGY TESTING CONSULTING SERVICE CO LTD
Login to view more 
Login to view more