Nickel base single crystal high-temperature alloy series Nideal2 alloy series and application thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A high-temperature alloy and nickel-based single crystal technology, applied in the field of high-temperature alloys, can solve problems such as difficult deformation of alloys, and achieve the effect of high temperature bearing capacity
Inactive Publication Date: 2018-04-13
DALIAN UNIV OF TECH
View PDF5 Cites 8 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, with the improvement of high temperature performance, the deformation of the alloy becomes difficult
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0014] The following examples will further illustrate the present invention.
[0015] This example describes the evolution process from the second generation CMSX-4 to the third generation CMSX-10K of the nickel-based single crystal alloy.
[0016] ① CMSX-4 is a second-generation single crystal alloy with a durable life of 139 hours at 1100°C / 137MPa (KyokoKawagishi, Superalloys 2012, TMS 2012). The standard composition of its grade is Ni-9.6Co-3.0Re-6.4Cr-0.6Mo-6.4W-5.6Al-6.5Ta-1Ti-0.1Hf in mass percent, and converted into atomic percent.
[0017] ② Classify the main alloying elements and compare them with the Nideal 2 alloy series components. Ni-like element Ni in CMSX-4 alloy 0.86 co 0.12 Re 0.01 , forming γ′ precipitated phase element Al, other forming γ′ precipitated phase element Ti 0.37 Ta 0.63 , and form the γ-matrix element Cr 0.76 Mo 0.04 W 0.20 The total atomic percentages are: 74.0, 12.6, 3.4, 9.9. It can be seen that there is still a certain composition d...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a nickel base single crystal high-temperature alloy series Nideal2 alloy series and application thereof, and belongs to the technical field of high-temperature alloys. The alloy series comprises main alloy components of a similar Ni element, an element forming a gamma' precipitated phase, an element forming a gamma basal body, and an Al element; and the similar Ni element is selected from one or several of Ni, Co, Re, Ru, Ir, Fe, Pt, Pd, Os, Rh and Tc, and is 80+-1.5 at.%. The element forming the gamma' precipitated phase is selected from one or several of Ti, V, Nb, Ta, Zr and Hf, and is 3.3+-0.1 at.%. The element forming the gamma basal body is selected from one or several of Cr, Mo and W, and is 3.3+-0.1 at.%. The atomic percentage sum of the Al element is 13.3+-0.2 at.%; the alloy components need to be met synchronously; and after components of main alloys are determined, Mg, Si, C, B and one or several of La, Ce and Y rare earth are selected within 0.5 at.%. The alloy series constructed by an ideal ratio is called as the Nideal2 alloy series; and the alloy series achieves high temperature bearing capacity and long service life.
Description
technical field [0001] The invention relates to a nickel-based single-crystal high-temperature alloy series Nideal 2 alloy series and an application thereof, belonging to the technical field of high-temperature alloys. Background technique [0002] Nickel-based superalloy mainly refers to a high-temperature structural material based on nickel, which can work for a long time above 600°C and under certain stress conditions. Nickel-based superalloys have high temperature bearing capacity, long lasting life, good oxidation resistance and corrosion resistance, and good fatigue performance and fracture toughness. With the development of industry, nickel-based superalloys have shown good application prospects in many fields, especially in high-temperature components such as turbine blades, guide vanes and turbine disks of aero-engines and gas turbines. [0003] Nickel-based superalloy is a typical alloy in superalloys. According to the preparation process, superalloys can be divi...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.