A graphene, large-area technology, applied in the field of preparation of large-area graphene materials, can solve problems such as high cost, loss of function, small area, etc., and achieve the effects of prolonging life, low cost, and reducing manufacturing cost

Active Publication Date: 2018-05-08
SHAANXI RES DESIGN INST OF PETROLEUM CHEM IND
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Especially in the application of metal heat conduction and anticorrosion, it is necessary to prepare functional graphene with large area, low cost and strong adhesion. However, the graphene prepared by the current research method is difficul

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing large-area graphene material by adopting suturing method
  • Method for preparing large-area graphene material by adopting suturing method
  • Method for preparing large-area graphene material by adopting suturing method

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0020] Example 1:

[0021] The graphene oxide GO was added to a conical flask containing diethylenetriamine at a mass ratio of 1:100. Then use an ultrasonic disperser to disperse at 90% ultrasonic intensity for 40 minutes, and observe the dispersion. The solution showed a black opaque liquid and was evenly dispersed. It was immediately transferred to a three-necked flask equipped with a stirring device and a distillation device. Under stirring, the temperature was raised to control the reaction temperature within 120°C, and the reaction time was 21h. After the reaction, the reaction solution is evenly coated on the 20# steel sheet that has been polished and cleaned beforehand, cleaned and dried with absolute ethanol, and placed in an oven at 120°C for 3 hours to obtain a graphene film that is "stitched" into a continuous structure. .

[0022] The organic amine as a suture agent reacts with graphene oxide, and the organic amine with primary amine at both ends reacts with graphene ...

Example Embodiment

[0030] Example 2:

[0031] The graphene oxide GO was added to a conical flask containing ethylenediamine at a mass ratio of 1:200. Then use an ultrasonic disperser to disperse at 90% ultrasonic intensity for 60 minutes to observe the dispersion. After being uniformly dispersed, immediately transfer it into a three-necked flask equipped with a stirring device and a distillation device. Under stirring, the temperature is raised to control the reaction temperature within 140°C, and the reaction time is 21h. After the reaction, the reaction solution is evenly coated on the 20# steel sheet that has been polished and cleaned beforehand, cleaned and dried with absolute ethanol, and placed in an oven at 120°C for 3 hours to obtain a graphene film that is "stitched" into a continuous structure. .

Example Embodiment

[0032] Example 3:

[0033] The graphene oxide GO was added to a conical flask containing diethylenetriamine at a mass ratio of 1:400. Then use an ultrasonic disperser to disperse for 55 minutes at 90% ultrasonic intensity, and observe the dispersion. After the dispersion is uniform, immediately transfer it into a three-necked flask equipped with a stirring device and a distillation device. Under stirring, the temperature is raised to control the reaction temperature within 100-200°C, and the reaction time is 23h. After the reaction, the reaction solution is evenly coated on the 20# steel sheet that has been polished and cleaned beforehand, cleaned and dried with absolute ethanol, and placed in an oven at 120°C for 3 hours to obtain a graphene film that is "stitched" into a continuous structure. .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for preparing a large-area graphene material by adopting a suturing method. The preparation method comprises the following steps: adding graphene oxide into a conicalflask filled with one of ethylenediamine, diethylenetriamine, triethylenetetramine and paraphenylenediamine according to a mass ratio of 1 to (100 to 600); then performing dispersion for 30 to 60 minutes by using an ultrasonic dispersing machine, uniformly dispersing the solutions and instantly transferring the solutions into a three-neck flask; heating the flask while stirring, controlling a reaction temperature to be between 100 and 200 DEG C, and performing reaction for 20 to 24 hours; taking reaction solutions after the reaction is finished and uniformly coating a steel plate which is ground and smoothed in advance and is cleaned and dried by using absolute ethyl alcohol with the reaction solutions, and putting the steel plate in a baking oven to be dried for 3 hours at 120 DEG C so as to obtain a graphene film with a sutured continuous structure. According to the method disclosed by the invention, the method for suturing the micron-scale graphene oxide into the graphene film withlarge area, high heat conduction and capability of being firmly adhered on the surface of metal by utilizing a suture agent is innovatively provided.

Description

technical field [0001] The invention relates to a preparation method of a large-area graphene material, which is mainly used in the field of corrosion protection of oil and gas field exploitation, petroleum refining process, heat transfer metal equipment and pipelines of chemical enterprises operating in harsh corrosive environments. Background technique [0002] Graphene, as a new type of two-dimensional nanomaterial, its basic structural unit is a new type of two-dimensional atomic crystal composed of a single atomic layer of carbon atoms connected by sp2 hybridization. It is the most stable benzene six-membered ring in organic materials . This special structure makes it exhibit many excellent properties that existing materials do not have in terms of mechanical strength, carrier mobility, thermal conductivity, and quantum Hall effect. Especially its thermal conductivity can reach 5000w m -1 ·K -1 , 3 times that of diamond (the thermal conductivity of ultra-high thermal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01B32/19
Inventor 黄瑾陈晓东陈君侯雯雯杨源波
Owner SHAANXI RES DESIGN INST OF PETROLEUM CHEM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap